摘要:
Disclosed herein are acicular magnetic metal particles containing iron as the main ingredient the surfaces of which are coated with a polymer formed from at least one of silicone compounds represented by the following formula (I):(R.sup.1 HSiO).sub.a (R.sup.2 R.sup.3 SiO).sub.b (R.sup.4 R.sup.5 R.sup.6 SiO.sub.1/2)c (I)wherein R.sup.1, R.sup.2, R.sup.3, R.sup.4, R.sup.5 and R.sup.6 respectively represent a hydrogen atom or hydrocarbon group having 1 to 10 carbon atoms which hydrocarbon group may be substituted by at least one halogen atom, a and b are respectively 0 or integers of not less than 1, and c is 0 or 2, provided that when c is 0, the sum of a and b is an integer of not less than 3 and which have a coercive force of not less than 1400 Oe, a saturation magnetization of not less than 100 emu/g, a major axial diameter of not more than 0.25 .mu.m and an S.F.D. of not more than 0.38, and a process for producing the acicular magnetic metal particles containing iron as the main ingredient.
摘要:
Disclosed herein are spindle-shaped magnetic iron based alloy particles containing at least one selected from the group consisting of Ni, Al, Si, P, Co, Mg, B and Zn, which have a particle length of 0.05 to 0.40 .mu.m, a crystallite size of 110 to 180 .ANG., a specific surface area of 30 to 60 m.sup.2 /g, a coercive force of 1,300 to 1,700 Oe and a saturation magnetization (.sigma.s) of not less than 100 emu/g and a process for producing the same.
摘要:
Disclosed herein are spindle-shaped magnetic iron based alloy particles containing at least one selected from the group consisting of Ni, Al, Si, P, Co, Mg, B and Zn, which have a particle length of 0.05 to 0.40 .mu.m, a crystallite size of 110 to 180 .ANG., a specific surface area of 30 to 60 m.sup.2 /g, a coercive force of 1,300 to 1,700 Oe and a saturation magnetization (.sigma.s) of not less than 100 emu/g and a process for producing the same.
摘要:
Disclosed herein are acicular magnetic iron based alloy particles for magnetic recording, containing 1.5 to 10 mol % of B based on Fe (calculated as B) and 1.5 to 10 mol % of Co based on Fe (calculated as Co) in the vicinity of the surfaces of said particles and having a saturation magnetization of not less than 125 emu/g and an S.F.D. value of not more than 0.50, and a process for producing the same.
摘要:
Disclosed herein are acicular magnetic iron based alloy particles for magnetic recording, containing 1.5 to 10 mol % of B based on Fe (calculated as B) and 1.5 to 10 mol % of Co based on Fe (calculated as Co) in the vicinity of the surfaces of said particles and having a saturation magnetization of not less than 125 emu/g and an S.F.D. value of not more than 0.50, and a process for producing the same.
摘要:
The disclosure describes spindle-shaped magnetic iron-based alloy particles containing cobalt and iron as the main ingredients in which the Co content is 1.0 to 50.0 atm % (calculated as Co) based on the total Fe in the spindle-shaped magnetic iron-based alloy particles, and which the spindle-shaped magnetic iron-based alloy particles have an average major axis diameter of 0.05 to 0.18 .mu.m, a size distribution (standard deviation/major axis diameter) of not more than 0.25, an average minor axis diameter of 0.010 to 0.020 .mu.m, an aspect ratio (major axis diameter/minor axis diameter) of 4 to 15, an X-ray crystallite size D.sub.110 of 120 to 180 .ANG., a coercive force of 1720 to 2500 Oe, a saturation magnetization of not less than 110 emu/g, and a saturation magnetization decrement percentage of not more than 17%.
摘要:
Disclosed herein are plate-like barium ferrite particles with a solid solution of zinc on the surface thereof, which have an average particle diameter of not less than 0.03 .mu.m and less than 0.1 .mu.m, a BET specific surface are of 55 to 80 m.sup.2 /g, a coercive force of 300 to 1,500 Oe and a magnetization of not less than 57 emu/g, preferably not less than 60 emu/g, in magnetic field of 10 KOe, and which are represented by the following formula (I):BaO.n[(Fe.sub.1-x-y Co.sub.x Ti.sub.y).sub.2 O.sub.3-x+y ] (I)wherein x and y are independently from 0.02 to 0.12 and n is from 4 to 11, the atomic ratio of Co to Fe(III) being from 0.02:1 to 0.13:1 and the molar ratio of Ti to Co being from more than 0 to not more than 0.8, and a process for producing the plate-like barium ferrite particles.
摘要:
Spindle-shaped magnetic alloy particles containing Fe and Co as main components of the present invention have a cobalt content of 20 to 50 atm % (calculated as Co) based on whole Fe; an average major axis diameter (L) of 0.03 to 0.10 &mgr;m; a coercive force value of 159.2 to 238.7 kA/m (2,000 to 3,000 Oe); a crystallite size of 100 to 160 Å; and an activation volume (Vact) of 0.01 to 0.07E-4 &mgr;m3. A high-density magnetic recording medium produced by using such spindle-shaped magnetic alloy particles containing Fe and Co as main components, have an excellent output characteristics in a short wavelength region, a considerably reduced noise and an excellent storage stability.
摘要:
The present invention relates to a spindle-shaped goethite particles containing cobalt of 8.0 to 50.0 atm %, calculated as Co, based on the total Fe in the spindle-shaped goethite particles and a compound of at least one element selected from the group consisting of Al, Si, Nd, Y, La, Ce, Pr, Tb, Ca, Mg, Ba and Sr of not more than 25.0 atm %, calculated as the element, based on the total Fe in the spindle-shaped goethite particles, and having an average major axis diameter of 0.05 to 0.15 .mu.m, a size distribution (standard deviation/major axis diameter) of not more than 0.30, an average minor axis diameter of 0.010 to 0.025 .mu.m, an aspect ratio of 4 to 8 and an X-ray crystallite size ratio (D.sub.020 /D.sub.110) of 2.0 to 3.5. These spindle-shaped goethite particles are useful as raw material of spindle-shaped magnetic iron-based alloy particles containing cobalt and iron as the main ingredients, which have a uniform particle size, no inclusion of dendrites, a high coercive force, an excellent coercive force distribution, a large saturation magnetization, and in addition, an excellent stability against oxidation.
摘要:
Magnetic acicular alloy particles containing iron as a main component according to the present invention, have an average major axial diameter of 0.05 to 0.2 &mgr;m, and pH values of water suspensions of said magnetic acicular alloy particles containing iron as a main component, which satisfies the formula: (pH value of water suspension treated by A method)−(pH value of water suspension treated by B method)