公开(公告)号：US20130274091A1

公开(公告)日：2013-10-17

申请号：US13861643

申请日：2013-04-12

Applicant: TATA CONSULTANCY SERVICES LIMITED

Inventor： Auhin Kumar MAPARU ,  Beena RAI ,  Vivek GANVIR

IPC: B01J31/38 ,  B01J27/25 ,  B01J27/232

CPC classification number: B01J31/38 ,  B01J21/063 ,  B01J23/50 ,  B01J27/232 ,  B01J27/24 ,  B01J27/25 ,  B01J35/0013 ,  B01J35/002 ,  B01J35/004 ,  B01J35/023 ,  B01J37/0036 ,  B01J37/009 ,  B01J37/32 ,  B82Y30/00 ,  C01P2002/72 ,  C01P2002/84 ,  C01P2004/03 ,  C01P2004/52 ,  C01P2004/64 ,  C01P2006/90 ,  C09C1/3623 ,  C09C1/3653 ,  C09C1/3669 ,  C25B1/003

Abstract: Present disclosure provides a process for the synthesis of doped titania nanoparticle having photocatalytic activity greater than 90% at 2 hours under sunlight irradiation. The process involves step a) milling a mixture containing anatase titania and a precursor compound, the compound selected from the group consisting of metal and non-metal salts, in the presence of water and oxide milling media, at a temperature in the range of 20 to 50° C. for a period of 60-120 minutes, to form a slurry, wherein the amount of water is in the range of 15 to 25% by weight of the total mixture; and b) filtering the slurry to separate the oxide milling media and obtain a filtrate containing doped titania nanoparticles.

Abstract translation: 本公开提供了一种在阳光照射下在2小时合成具有大于90％的光催化活性的掺杂二氧化钛纳米颗粒的方法。 该方法包括步骤a）在水和氧化物研磨介质的存在下，在20℃的温度下研磨含有锐钛矿二氧化钛和前体化合物的混合物，选自金属和非金属盐的化合物 至50℃，时间为60-120分钟，以形成浆料，其中水的量在总混合物的15至25重量％的范围内; 和b）过滤浆料以分离氧化物研磨介质并获得含有掺杂二氧化钛纳米颗粒的滤液。