摘要:
A producing method of a grain-oriented electrical steel sheet includes forming a preferentially-deformable portion at an end region of a steel sheet so as to be parallel with the rolling direction of the steel sheet; coiling the steel sheet; and performing a final annealing to the steel sheet after disposing the steel sheet in a manner such that the end region becomes the lower side of the steel sheet.
摘要:
A value of a parameter Q represented by “Q=([Ti]/48+[V]/51+[Zr]/91+[Nb]/93)/([C]/12)” is not less than 0.9 nor more than 1.1, when contents of Ti, V, Zr, Nb, and C (mass %) are represented as [Ti], [V], [Zr], [Nb], and [C] respectively. A matrix of a metal structure is a ferrite phase, and the metal structure does not contain a non-recrystallized structure. An average grain size of ferrite grains constituting the ferrite phase is not less than 30 μm nor more than 200 μm. A precipitate containing at least one selected from the group consisting of Ti, V, Zr, and Nb exists with a density of 1 particle/μm3 or more in the ferrite grain. An average grain size of the precipitate is not less than 0.002 μm nor more than 0.2 μm.
摘要:
When contents of Ti, V, Zr, Nb, and C (mass %) are represented as [Ti], [V], [Zr], [Nb], and [C] respectively, a value of a parameter Q represented by “Q=([Ti]/48+[V]/51+[Zr]/91+[Nb]/93)/([C]/12)” is not less than 0.9 nor more than 1.1. A matrix of a metal structure is a ferrite phase, and the metal structure does not include a non-recrystallized structure. An average grain size of ferrite grains constituting the ferrite phase is not less than 10 μm nor more than 200 μm. A precipitate containing at least one selected from the group consisting of Ti, V, Zr, and Nb exists with a density of 10 μm−3 or more in the ferrite grain. An average grain size of the precipitate is not less than 0.002 μm nor more than 0.2 μm.
摘要:
A value of a parameter Q represented by “Q=([Ti]/48+[V]/51+[Zr]/91+[Nb]/93)/([C]/12)” is not less than 0.9 nor more than 1.1, when contents of Ti, V, Zr, Nb, and C (mass %) are represented as [Ti], [V], [Zr], [Nb], and [C] respectively. A matrix of a metal structure is a ferrite phase, and the metal structure does not contain a non-recrystallized structure. An average grain size of ferrite grains constituting the ferrite phase is not less than 30 μm nor more than 200 μm. A precipitate containing at least one selected from the group consisting of Ti, V, Zr, and Nb exists with a density of 1 particle/μm3 or more in the ferrite grain. An average grain size of the precipitate is not less than 0.002 μm nor more than 0.2 μm.
摘要:
When contents of Ti, V, Zr, Nb, and C (mass %) are represented as [Ti], [V], [Zr], [Nb], and [C] respectively, a value of a parameter Q represented by “Q=([Ti]/48+[V]/51+[Zr]/91+[Nb]/93)/([C]/12)” is not less than 0.9 nor more than 1.1. A matrix of a metal structure is a ferrite phase, and the metal structure does not include a non-recrystallized structure. An average grain size of ferrite grains constituting the ferrite phase is not less than 10 μm nor more than 200 μm. A precipitate containing at least one selected from the group consisting of Ti, V, Zr, and Nb exists with a density of 10 μm−3 or more in the ferrite grain. An average grain size of the precipitate is not less than 0.002 μm nor more than 0.2 μm.
摘要:
A continuous annealing facility comprised of a heating zone, soaking zone, and cooling zone is used for continuous annealing of a steel strip having a Curie point (Tc) by an annealing temperature over Tc during which the heat treatment in the heating zone is divided into three regions, in a first heating zone, a radiant heating means using gas heating and/or a radiant heating means using electric heaters is used to heat the steel strip to less than Tc−50° C., in a next second heating zone, the heated steel strip is heated by a solenoid coil type high frequency induction heating means to a region of Tc−30° C. to Tc−5° C., and, in a final third heating zone, the heated steel strip is heated by a radiant heating means using gas heating and/or a radiant heating means using electric heaters to a treatment target temperature over Tc to thereby anneal a steel strip having a Curie point uniformly in the longitudinal direction.