摘要:
A magnetic recording medium having a ferromagnetic layer formed by oblique vapor deposition wherein the residual magnetic flux density in the width direction of the recording medium is larger than the residual magnetic flux density in the longitudinal direction shows the SN ratio in a practical level at recording in the width direction.
摘要:
A thin metallic layer type magnetic recording medium having thin metallic layers in a structure comprises a layer in which a tilt angle of a metallic particle direction to the normal line to said substrate gradually increases depending upon an increase of a distance from said substrate; and a layer in which a tilt angle of a metallic particle direction to the normal line to said substrate gradually decreases depending upon an increase of a distance from said substrate.
摘要:
A magnetic recording medium having multi-layer structure of two or more thin metallic layers on a substrate. The orientations of metallic particles are different for each of said thin metallic layers.
摘要:
In a magnetic recording medium wherein a metal thin film magnetic layer and a topcoat layer of an organic fluorine compound are formed on a nonmagnetic substrate, the surface of the magnetic layer is plasma treated or plasma oxidized, enhancing the bond between the adjoining layers. A protective film of carbon may be disposed between the magnetic layer and the topcoat, with the surface of the protective carbon film plasma treated. Instead, a protective film of plasma-polymerized organometallic compound may be used.
摘要:
In a magnetic recording medium wherein a metal thin film magnetic layer and an overcoat are formed on a nonmagnetic substrate, durability is improved when the overcoat comprises a plasma-polymerized film and a topcoat of an organic fluorine compound; a plasma-polymerized film, a protective carbon film, and a topcoat of an organic fluorine compound; a plasma-polymerized film containing C, F and H; or a plasma-polymerized organometallic film and a fluorine or silicon-containing topcoat. Oxidation of the upper surface of the magnetic layer with a plasma is also effective.
摘要:
A magnetic recording medium having more than 550 Oersted of a coercive force, less than 1.8 of a ratio of a coercive force at -196.degree. C. to a coercive force at 25.degree. C., less than 1.0 wt. % of a content of Fe.sup.2+ is prepared by incorporating a magnetic powder obtained by dispersing acicular .gamma.-Fe.sub.2 O.sub.3 in an aqueous solution of a cobalt salt and reducing it with a reducing agent to deposit a cobalt compound on the acicular .gamma.-Fe.sub.2 O.sub.3.
摘要翻译:具有超过550矫顽力奥斯特的磁记录介质,在-196℃下的矫顽力与矫顽力在25℃下的比值小于1.8,小于1.0重量%。 通过将针状γ-Fe 2 O 3分散在钴盐水溶液中而得到的磁性粉末并用还原剂还原,在针状γ-Fe 2 O 3上析出钴化合物,可以制备Fe2 +含量的%。
摘要:
In a magnetic recording medium wherein a metal thin film magnetic layer and an overcoat are formed on a nonmagnetic substrate, durability is improved when the overcoat comprises a plasma-polymerized film and a topcoat of an organic fluorine compound; a plasma-polymerized film, a protective carbon film, and a topcoat of an organic fluorine compound; a plasma-polymerized film containing C, F and H; or a plasma-polymerized organometallic film and a fluorine or silicon-containing topcoat. Oxidation of the upper surface of the magnetic layer with a plasma is also effective.
摘要:
In a magnetic recording medium wherein a metal thin film magnetic layer, a protective film or carbon, and a topcoat layer are formed on a rigid substrate in this order, the topcoat layer is from an organic fluorine compound by gas phase deposition.
摘要:
In a magnetic recording medium wherein a metal thin film magnetic layer and an overcoat are formed on a nonmagnetic substrate, durability is improved when the overcoat comprises a plasma-polymerized film and a topcoat of an organic fluorine compound; a plasma-polymerized film, a protective carbon film, and a topcoat of an organic fluorine compound; a plasma-polymerized film containing C, F and H; or a plasma-polymerized organometallic film and a fluorine or silicon-containing topcoat. Oxidation of the upper surface of the magnetic layer with a plasma is also effective.
摘要:
A magnetic recording medium comprises a substrate and a magnetic recording layer formed on the substrate and having an easy magnetization axis in the perpendicular direction to the surface of the medium, characterized in that said magnetic recording layer is composed of from 75 to 90% by weight of Co, at most 15% by weight of Mo and the rest being V and unavoidable impurities.