    GOLF BALL
    7.
    发明申请
    GOLF BALL 有权
    高尔夫球

    公开(公告)号：US20130090188A1

    公开(公告)日：2013-04-11

    申请号：US13645136

    申请日：2012-10-04

    申请人： DUNLOP SPORTS CO. LTD.,

    发明人： Satoko OKABE

    IPC分类号： A63B37/02

    CPC分类号： A63B37/0075 ,  A63B37/0003 ,  A63B37/0031 ,  A63B37/0036 ,  A63B37/0051 ,  A63B37/0058 ,  A63B37/0059 ,  A63B37/0062 ,  A63B37/0064 ,  A63B37/0065 ,  A63B37/0069 ,  A63B37/0076

    摘要： A center of a golf ball is formed from a composition having a flexural modulus from 150-450 MPa, a maximum loss factor (tan δ) between −20 and 0° C. of 0.08 or less, a rebound resilience of 55% or more, and a slab hardness ranging from 40-60 in Shore D hardness. The center composition includes, as a resin component, 30 to 70 mass % of (A) a modified polyester elastomer having a Shore A hardness of 95 or less; 70-30 mass % of (B) a binary ionomer resin having a Shore D hardness of 65 or more, a flexural modulus of 300 MPa or more, and a melt flow rate (190° C., 2.16 kg) of 1.0 g/10 min or more; and 0-50 mass % of (C) a thermoplastic resin other than (A) and (B) components (provided that a total content of (A), (B), and (C) components is 100 mass %).

    摘要翻译： 高尔夫球的中心由弯曲弹性模量为150-450MPa，-20℃和0℃之间的最大损耗因子（tanδ）为0.08以下，回弹性为55％以上的组合物形成 ，硬度为40-60的肖氏D硬度的板坯硬度。 作为树脂成分，中心组合物含有（A）肖氏A硬度为95以下的改性聚酯弹性体30〜70质量％ 70-30质量％的（B）肖氏D硬度为65以上，弯曲弹性模量为300MPa以上，熔体流动速率（190℃，2.16kg）的二元离聚物树脂为1.0g / 10分钟以上; 和（C）（A）和（B）成分以外的热塑性树脂为0〜50质量％（条件是（A），（B）和（C）成分的总含量为100质量％）。

    GOLF BALL RESIN COMPOSITION AND GOLF BALL
    9.
    发明申请
    GOLF BALL RESIN COMPOSITION AND GOLF BALL 有权
    高尔夫球形树脂组合物和高尔夫球

    公开(公告)号：US20110263352A1

    公开(公告)日：2011-10-27

    申请号：US13085635

    申请日：2011-04-13

    申请人： Takahiro SHIGEMITSU

    发明人： Takahiro SHIGEMITSU

    IPC分类号： A63B37/02 ,  C08L33/06

    CPC分类号： A63B37/0003 ,  A63B37/0031 ,  A63B37/0036 ,  A63B37/0039 ,  A63B37/0045 ,  A63B37/0048 ,  A63B37/0087 ,  A63B37/0092 ,  A63B37/0094 ,  C08L23/0876 ,  C08L23/0869

    摘要： An object of the present invention is to provide a golf ball resin composition containing an ionomer resin with an excellent resilience and fluidity. Another object of the present invention is to provide a golf ball using an ionomer resin for an intermediate layer, with an excellent shot feeling, durability and resilience. The present invention provides a golf ball resin composition comprising (A) an ionomer resin consisting of a metal ion-neutralized product of a ternary copolymer composed of an olefin, an α,β-unsaturated carboxylic acid having 3 to 8 carbon atoms and an α,β-unsaturated carboxylic acid ester; (B) a binary copolymer composed of an olefin and an α,β-unsaturated carboxylic acid having 3 to 8 carbon atoms and/or a ternary copolymer composed of an olefin, an α,β-unsaturated carboxylic acid having 3 to 8 carbon atoms and an α,β-unsaturated carboxylic acid ester, and (C) a zinc compound, wherein a content ratio ((A)/(B)) of (A) component to (B) component ranges from 50/50 to 80/20 in a mass ratio and a content of (C) component ranges from 0.1 part to 20 parts with respect to 100 parts by mass of a sum of (A) component and (B) component, and the golf ball resin composition has a melt flow rate (190° C., 2.16 kg) of 5 g/10 min or more.

    摘要翻译： 本发明的目的是提供一种含有优异的弹性和流动性的离聚物树脂的高尔夫球树脂组合物。 本发明的另一个目的是提供一种使用离聚物树脂作为中间层的高尔夫球，具有优异的拍摄感，耐久性和弹性。 本发明提供一种高尔夫球树脂组合物，其包含（A）由烯烃，具有3-8个碳原子的α，bgr-不饱和羧酸的三元共聚物的金属离子中和产物组成的离聚物树脂和 α，β-不饱和羧酸酯; （B）由烯烃和具有3-8个碳原子的α，β-不饱和羧酸和/或由烯烃，α和bgr-不饱和羧酸组成的三元共聚物组成的二元共聚物，其具有3至8个 碳原子和α，β-不饱和羧酸酯和（C）锌化合物，其中（A）成分与（B）成分的含量比（（A）/（B））为50/50 至80/20，相对于（A）成分和（B）成分的总和为100质量份，（C）成分的含量为0.1〜20份，高尔夫球用树脂组合物 熔体流动速率（190℃，2.16kg）为5g / 10min以上。

    Golf ball
    10.
    发明授权
    Golf ball 有权
    高尔夫球

    公开(公告)号：US07648429B2

    公开(公告)日：2010-01-19

    申请号：US12039513

    申请日：2008-02-28

    申请人： Hiroyuki Nagasawa

    发明人： Hiroyuki Nagasawa

    IPC分类号： A63B37/06

    CPC分类号： A63B37/0004 ,  A63B37/0022 ,  A63B37/0027 ,  A63B37/0031 ,  A63B37/0036 ,  A63B37/0073 ,  A63B37/0074 ,  A63B37/0075 ,  A63B37/0094 ,  A63B37/12 ,  A63B45/02 ,  A63B2209/00

    摘要： In a golf ball composed of a core, a cover of at least one layer that encloses the core, and a plurality of dimples on an outermost layer of the cover, at least one constituent element contains from 0.5 to 30 parts by weight of one or more rare-earth oxide composed of a single rare-earth element, or a rare-earth mixed oxide composed of a plurality of rare-earth elements mixed in a desired ratio, per 100 parts by weight of a base material. Unlike ordinary golf balls, the golf ball of the invention has a visibility which differs under display or indoor light as opposed to outdoors, and is also very fashionable.

    摘要翻译： 在由芯组成的高尔夫球中，包围芯的至少一层的覆盖物和在盖的最外层上的多个凹坑，至少一个构成元素含有0.5至30重量份的一个或多个 相对于每100重量份的基材，由单个稀土元素构成的更多的稀土类氧化物或以所需比例混合的多种稀土元素构成的稀土类混合氧化物。 与普通高尔夫球不同，本发明的高尔夫球具有与室外不同的显示或室内光的可见度，并且也非常时尚。