公开(公告)号：EP3167009A1

公开(公告)日：2017-05-17

申请号：EP15738608.7

申请日：2015-07-10

申请人： S.A. Lhoist Recherche et Développement

发明人： LESUEUR, Didier

IPC分类号： C08L95/00 ,  E01C7/32 ,  C04B26/26 ,  E01C7/18 ,  C08K3/22 ,  C04B111/00

CPC分类号： C04B26/26 ,  C04B22/064 ,  C04B2103/0005 ,  C04B2111/0075 ,  C04B2111/766 ,  C08L95/005 ,  C08L2555/28 ,  C08L2555/52 ,  E01C7/18 ,  E01C7/20 ,  E01C7/32 ,  E01C7/353

摘要： The invention relates to a method for the production of cold-process bituminous coatings, in particular surface dressings, comprising the steps of: producing a bituminous binder in the form of a cationic bitumen emulsion, producing an aggregate containing at least a first lime-coated aggregate fraction, and forming said cold-process bituminous coating with at least one layer of the aggregate incorporated into the bituminous binder. The invention also relates to a cold-process bituminous coating composition comprising such lime-coated aggregates and to the use of lime in order to coat aggregates during the production of the bituminous coating.

摘要翻译： 本发明涉及生产冷加工沥青涂层，特别是表面敷料的方法，其包括以下步骤：生产阳离子沥青乳液形式的沥青粘合剂，产生包含至少第一石灰涂覆的聚集体 聚集分数，并且形成所述冷加工沥青涂层，其中至少一层掺入沥青粘合剂的聚集体。 本发明还涉及一种冷加工沥青涂料组合物，其包含这种石灰涂覆的聚集体并且涉及石灰的用途以便在沥青涂料的生产过程中涂覆聚集体。

公开(公告)号：EP0934991B1

公开(公告)日：2004-01-21

申请号：EP99102417.5

申请日：1999-02-08

申请人： KÖSTER BAUCHEMIE GMBH

发明人： Wirringa, Uwe, Dr., c/o Köster Bauchemie ,  Köster,Johann J.,c/o Köster Bauchemie GmbH

IPC分类号： C09K3/10 ,  C04B24/28 ,  C08L95/00 ,  E04B1/66 ,  C04B41/48

CPC分类号： C04B26/26 ,  C04B28/02 ,  C04B2111/00482 ,  C04B2111/27 ,  C04B2111/50 ,  C04B2111/766 ,  C08L95/005 ,  C09K3/1021 ,  C04B14/06 ,  C04B24/282 ,  C04B24/32 ,  C08L75/04

公开(公告)号：EP2832706B1

公开(公告)日：2017-03-15

申请号：EP13769484.0

申请日：2013-03-25

申请人： Denka Company Limited

发明人： NISHIOKA,Asaaki ,  MORI,Taiichiro ,  NANASAWA,Akira ,  YOSHINO,Ryoetsu ,  IWANAMI,Kazuhide ,  YAMAMOTO,Kenji ,  KAWAUCHI,Toshio ,  SHIRAI,Kentaro ,  MATSUMOTO,Masao

IPC分类号： C04B28/02 ,  B28C7/04 ,  C04B22/08 ,  C04B22/10 ,  C04B22/14 ,  C04B24/06 ,  C04B24/26 ,  C04B40/02 ,  C04B28/14 ,  C04B20/10

CPC分类号： C04B28/14 ,  C04B20/1033 ,  C04B2111/00086 ,  C04B2111/766 ,  C04B7/02 ,  C04B7/32 ,  C04B24/2647 ,  C04B2103/22 ,  C04B24/06

公开(公告)号：EP2900617B1

公开(公告)日：2016-06-08

申请号：EP13766514.7

申请日：2013-09-23

申请人： YARA International ASA

发明人： FRANKE, Wolfram

IPC分类号： C04B22/08 ,  C04B28/00 ,  C04B28/02

CPC分类号： C04B7/26 ,  C04B22/085 ,  C04B24/18 ,  C04B28/00 ,  C04B28/02 ,  C04B28/021 ,  C04B40/0039 ,  C04B2111/766 ,  C04B2103/304 ,  C04B2103/32 ,  C04B2103/001 ,  C04B2103/0021

公开(公告)号：EP2852563A1

公开(公告)日：2015-04-01

申请号：EP13724800.1

申请日：2013-05-21

申请人： Lafarge

发明人： SABIO, Serge ,  GHILARDI, Serge ,  PARDAL, Xiaolin ,  TESTUD, Michel

IPC分类号： C04B28/04 ,  C04B28/14

CPC分类号： C04B7/02 ,  C04B28/04 ,  C04B28/14 ,  C04B2111/766 ,  C04B2201/05 ,  Y02W30/92 ,  Y02W30/94 ,  C04B7/527 ,  C04B14/28 ,  C04B18/08 ,  C04B18/146 ,  C04B22/085 ,  C04B22/143 ,  C04B14/106 ,  C04B18/141 ,  C04B2/04

摘要： A hydraulic binder includes a Portland clinker having a Blaine specific surface of 4000 to 5500 cm2/g, from 2.5 to 8% of sulphate expressed by mass of SO3 relative to the mass of clinker, from 1.5 to 10% of calcium nitrite and/or calcium nitrate expressed as anhydrous mass relative to the mass of clinker and from 15 to 50% of a mineral addition including calcium carbonate by mass relative to the total mass of binder.

摘要翻译： 水硬性粘合剂包括具有4000至5500cm 2 /克的Blaine比表面积的奥特兰熟料，2.5质量％的SO 3相对于熟料质量的2.5至8％的硫酸盐，1.5至10％的亚硝酸钙和/或 硝酸钙以相对于熟料质量为无水质量表示，相对于粘合剂的总质量为15〜50％的包含碳酸钙的矿物质添加量。

公开(公告)号：EP2832706A1

公开(公告)日：2015-02-04

申请号：EP13769484.0

申请日：2013-03-25

申请人： Denki Kagaku Kogyo Kabushiki Kaisha

发明人： NISHIOKA,Asaaki ,  MORI,Taiichiro ,  NANASAWA,Akira ,  YOSHINO,Ryoetsu ,  IWANAMI,Kazuhide ,  YAMAMOTO,Kenji ,  KAWAUCHI,Toshio ,  SHIRAI,Kentaro ,  MATSUMOTO,Masao

IPC分类号： C04B28/02 ,  B28C7/04 ,  C04B22/08 ,  C04B22/10 ,  C04B22/14 ,  C04B24/06 ,  C04B24/26 ,  C04B40/02

CPC分类号： C04B28/14 ,  C04B20/1033 ,  C04B2111/00086 ,  C04B2111/766 ,  C04B7/02 ,  C04B7/32 ,  C04B24/2647 ,  C04B2103/22 ,  C04B24/06

摘要： Provided is a rapid hardening cement in which a long setting and hardening time is secured in a low-temperature environment. The rapid hardening cement comprises: (A) a surface-premodified cement with a polycarboxylic acid-based water-reducing agent as a modifier; (B) a rapid hardening agent comprising calcium aluminate and gypsum; and (C) a setting modifier.

摘要翻译： 提供一种快速硬化水泥，其中在低温环境下确保长的凝固时间和硬化时间。 快速硬化水泥包括：（A）具有多元羧酸类减水剂作为改性剂的表面改性水泥; （B）包含铝酸钙和石膏的快速硬化剂; 和（C）设置修饰符。

公开(公告)号：EP2832706A4

公开(公告)日：2015-12-23

申请号：EP13769484

申请日：2013-03-25

申请人： DENKI KAGAKU KOGYO KK

发明人： NISHIOKA ASAAKI ,  MORI TAIICHIRO ,  NANASAWA AKIRA ,  YOSHINO RYOETSU ,  IWANAMI KAZUHIDE ,  YAMAMOTO KENJI ,  KAWAUCHI TOSHIO ,  SHIRAI KENTARO ,  MATSUMOTO MASAO

IPC分类号： C04B28/02 ,  B28C7/04 ,  C04B20/10 ,  C04B22/08 ,  C04B22/10 ,  C04B22/14 ,  C04B24/06 ,  C04B24/26 ,  C04B28/14 ,  C04B40/02

CPC分类号： C04B28/14 ,  C04B20/1033 ,  C04B2111/00086 ,  C04B2111/766 ,  C04B7/02 ,  C04B7/32 ,  C04B24/2647 ,  C04B2103/22 ,  C04B24/06

摘要： Provided is a rapid hardening cement in which a long setting and hardening time is secured in a low-temperature environment. The rapid hardening cement comprises: (A) a surface-premodified cement with a polycarboxylic acid-based water-reducing agent as a modifier; (B) a rapid hardening agent comprising calcium aluminate and gypsum; and (C) a setting modifier.

摘要翻译： 提供一种快速硬化水泥，其中在低温环境下确保长的凝固时间和硬化时间。 快速硬化水泥包括：（A）具有多元羧酸类减水剂作为改性剂的表面改性水泥; （B）包含铝酸钙和石膏的快速硬化剂; 和（C）设置修饰符。

公开(公告)号：EP2910710A1

公开(公告)日：2015-08-26

申请号：EP15155951.5

申请日：2015-02-20

申请人： rent a scientist GmbH

发明人： Nusko, Robert ,  Parzl, Adolf ,  Maier, Georg ,  Zech, Oliver

IPC分类号： E04G21/20 ,  C04B40/06

CPC分类号： C04B40/0616 ,  C04B2111/766 ,  C04B14/047 ,  C04B28/04 ,  C04B40/0082 ,  C04B22/04 ,  C04B22/064 ,  C04B2103/0091 ,  C04B24/04 ,  C04B24/126

摘要： Beschrieben wird ein Wintermörtel in Form eines trockenen Mörtelauftrages insbesondere in Form eines Mörtelbandes, Mörtelplatte oder lose Mörtelaggregate, dadurch gekennzeichnet dass durch die Aktivierung mit Wasser eine Wärmemenge von mindestens 50 kJ/kg Mörtel, bevorzugt mindestens 100 kJ/kg , besonders bevorzugt mindestens 150 kJ/kg freigesetzt wird.

摘要翻译： 冬季砂浆在特别是干砂浆顺序的形式在乳钵条，砂浆板或松散砂浆聚集体的形式，其特征在于通过激活与水的至少50千焦耳/公斤砂浆的热量所描述的，优选至少100千焦耳/ kg，更优选至少150千焦 / kg的被释放。

公开(公告)号：EP2900617A1

公开(公告)日：2015-08-05

申请号：EP13766514.7

申请日：2013-09-23

申请人： YARA International ASA

发明人： FRANKE, Wolfram

IPC分类号： C04B22/08 ,  C04B28/00 ,  C04B28/02

CPC分类号： C04B7/26 ,  C04B22/085 ,  C04B24/18 ,  C04B28/00 ,  C04B28/02 ,  C04B28/021 ,  C04B40/0039 ,  C04B2111/766 ,  C04B2103/304 ,  C04B2103/32 ,  C04B2103/001 ,  C04B2103/0021

摘要： The present invention relates to an admixture for a cementitious composition and a method using said admixture for manufacturing a durable cementitious composition, in particular a concrete, in cold weather conditions, such as in winter time or in cold geographical areas.

公开(公告)号：EP0934991A1

公开(公告)日：1999-08-11

申请号：EP99102417.5

申请日：1999-02-08

申请人： KÖSTER BAUCHEMIE GMBH

发明人： Wirringa, Uwe, Dr., c/o Köster Bauchemie ,  Köster,Johann J.,c/o Köster Bauchemie GmbH

IPC分类号： C09K3/10 ,  C04B24/28 ,  C08L95/00 ,  E04B1/66 ,  C04B41/48

CPC分类号： C04B26/26 ,  C04B28/02 ,  C04B2111/00482 ,  C04B2111/27 ,  C04B2111/50 ,  C04B2111/766 ,  C08L95/005 ,  C09K3/1021 ,  C04B14/06 ,  C04B24/282 ,  C04B24/32 ,  C08L75/04

摘要： Zusammensetzung zur Abdichtung von Bauwerken oder dergleichen gegen Witterungseinflüsse, insbesondere gegen das Eindringen von Wasser, gekennzeichnet durch die folgenden Bestandteile:

a) ein sich durch Aufnahme oder Abgabe von Wasser verfestigendes Material; und
b) ein NCO-funktionelles, hydrophiles Polyether-Polyurethan-Präpolymer.

摘要翻译： 组合物包括：（a）使水吸收和释放硬化的材料; 和（b）氰酸酯（NCO）官能的亲水性聚醚预聚物。 对于涉及施用组合物的建筑物的防风雨程序也包括独立权利要求，所述组合物包括：（a）硬化吸收和释放水的材料; 和（b）NCO-官能的亲水性聚醚预聚物，直接或在向建筑物中加入水之后。 优选的特征：固化剂（a）是砂浆，优选水泥砂浆或沥青乳液，另外还加入沙子。