摘要:
The present invention provides a polyester resin component having crystallization improved and including a cyclic compound shown by a below-described formula and polyester capable of having a crystal structure. (In the formula, a ring A and a ring B respectively represent benzene rings, and hydrogen bonded to the benzene rings may optionally be substituted with other groups. Y represents —CONH— or —NHCO—. X represents a heterocyclic group or a condensed heterocyclic group including one or more NH or CO respectively.)
摘要:
A resin composition for molding, added with a nucleating agent suitable for promoting crystallization of a polyester capable of having a crystal structure, and in particular of a biodegradable polyester, and a molded product containing the resin composition for molding thus improved in the crystallinity has either a cyclic compound expressed by general formula (I): (where each of A1, A2, A4 and A5 commonly or independently expresses —CO— or —NH—, each of A3 and A6 commonly or independently expresses hydrogen, halogen, optionally-substituted aliphatic group or optionally-substituted aromatic group) and having both of —CO— and —NH— in the molecule, or a mixture of (i) a cyclic compound having —CO— but no NH in the molecule and (ii) a cyclic compound having no —CO— but NH in the molecule, together with the polyester capable of having a crystal structure.
摘要:
The present invention relates to a polyester resin whose crystallization is improved and comprises a cyclic compound represented by a following formula A1-B-A2 (in the formula, A1 and A2 are the same or different and show groups represented by a below-described formula, P shows a benzene ring which may be replaced by a material, and B shows a bivalent hydrocarbon group which may be replaced by a material) and polyester capable of having a crystal structure.
摘要:
In order to provide a resin composition containing a lactic acid resin, and a molded article obtained from this resin composition which impart flame retardance to the resin composition and suppress a reduction in the molecular weight, use is made of a flame-retardant resin composition which contains a resin composition of which the major component is a lactic acid resin, and a surface-treated metallic hydroxide, wherein the surface-treated metallic hydroxide is added by 50-150 parts by mass per 100 parts by mass of the lactic acid resin.
摘要:
A resin composition comprising 100 parts by mass of lactic acid resin (A), 50 to 100 parts by mass of metal hydroxide (B) and 0.1 to 30 parts by mass of fiber (C), wherein the fiber (C) is a natural fiber or/and a fiber derived from natural material. Moldings thereof satisfy the V-0 standard or VTM-0 standard according to UL94 vertical flame test (UL94V, UL94VTM).
摘要:
To provide a flame retardant injection molded article that not only has flame-retardant properties but also combines impact resistance and heat resistance, either a flame retardant injection molded article is formed from a resin composition comprising a lactic acid resin (A), a metal hydroxide (B) whose surface has been treated with a silane coupling agent, and a copolymer (C) of lactic acid resin and diol/dicarboxylic acid, respectively at prescribed proportions, or a flame retardant injection molded article is formed from a resin composition comprising, in addition to the component (A) and component (B), either or both of an aliphatic polyester other than lactic acid resin and an aromatic aliphatic polyester (D), and an ester compound (E) of molecular weight in the range of 200 to 2,000, respectively at prescribed proportions.
摘要:
To obtain injection molded objects having biodegradability and excellent flame retardance and mechanical strength, the injection molded object includes a lactic acid based resin; and a metal hydroxide in a ratio of 5 to 40 mass parts per 100 mass parts of the lactic acid based resin. The metal hydroxide is surface-treated, and Na2O (w-Na2O) present on a surface of grains of the metal hydroxide is 0.1 mass % or less based on the total mass of the metal hydroxide. Preferably, the injection molded object contains an aliphatic polyester other than the lactic acid based resin or an aromatic-aliphatic polyester in a ratio of 20 to 80 mass parts per 100 mass parts of the lactic acid based resin.
摘要:
To provide a flame retardant injection molded article that not only has flame-retardant properties but also combines impact resistance and heat resistance, either a flame retardant injection molded article is formed from a resin composition comprising a lactic acid resin (A), a metal hydroxide (B) whose surface has been treated with a silane coupling agent, and a copolymer (C) of lactic acid resin and diol/dicarboxylic acid, respectively at prescribed proportions, or a flame retardant injection molded article is formed from a resin composition comprising, in addition to the component (A) and component (B), either or both of an aliphatic polyester other than lactic acid resin and an aromatic aliphatic polyester (D), and an ester compound (E) of molecular weight in the range of 200 to 2,000, respectively at prescribed proportions.
摘要:
A charging circuit includes a generator, a step-down circuit for reducing an output voltage of the generator to a predetermined voltage, a current controller for controlling a charging current that is supplied from the step-down circuit to a secondary battery, based on an amount of power generated by the generator, a mode selector for selecting charging modes, and a monitor for monitoring an amount of stored electricity. The step-down circuit receives an output of the generator, in charging, at a high voltage and a small current and is used to charge the battery at a low voltage and a large current.
摘要:
A resin composition that has high mechanical strength properties, has superior chemical characteristics such as chemical resistance and heat resistance, has high degree of freedom of product design, and has a structure considering the impact on environment is provided at low cost. The resin composition composed of a polyamide resin contains a cotton fiber as a natural fiber. The additive amount of the cotton fiber is preferably 1 wt % to 25 wt % both inclusive. The polyamide resin is polyamide 11 using castor oil as a raw material of plant origin. The average fiber diameter of the cotton fiber is 100 μm or less. The polyamide resin and the cotton fiber are melted and kneaded, and then hot-formed, and thereby a shaped article containing a plant fiber can be fabricated. In addition to the cotton fiber, a plant fiber such as a hemp fiber, a bamboo fiber, and wood powder and a biofiber such as a silk fiber may be applied.