A charging circuit includes a generator, a step-down circuit for reducing an output voltage of the generator to a predetermined voltage, a current controller for controlling a charging current that is supplied from the step-down circuit to a secondary battery, based on an amount of power generated by the generator, a mode selector for selecting charging modes, and a monitor for monitoring an amount of stored electricity. The step-down circuit receives an output of the generator, in charging, at a high voltage and a small current and is used to charge the battery at a low voltage and a large current.
摘要:
By a process for producing a porous carbon material from a plant-derived material as a raw material, said process including carbonizing the plant-derived material at 800° C. to 1,400° C. and then applying a treatment with an acid or alkali, a porous carbon material having a value of specific surface area of at least 10 m2/g as measured by the nitrogen BET method, a silicon content of at most 1 wt % and a pore volume of at least 0.1 cm3/g is obtainable from a plant-derived material, which has a silicon content of at least 10 wt %, as a raw material. Also provided is a process for producing a porous carbon material equipped with excellent functionality so that the porous carbon material can be used, for example, as an anode material for batteries, an adsorbent, masks, adsorbing sheets, or carriers.
摘要:
By a process for producing a porous carbon material from a plant-derived material as a raw material, said process including carbonizing the plant-derived material at 800° C. to 1,400° C. and then applying a treatment with an acid or alkali, a porous carbon material having a value of specific surface area of at least 10 m2/g as measured by the nitrogen BET method, a silicon content of at most 1 wt % and a pore volume of at least 0.1 cm3/g is obtainable from a plant-derived material, which has a silicon content of at least 10 wt %, as a raw material. Also provided is a process for producing a porous carbon material equipped with excellent functionality so that the porous carbon material can be used, for example, as an anode material for batteries, an adsorbent, masks, adsorbing sheets, or carriers.
摘要:
A material for acoustic apparatus housing, which is advantageous not only in that it prevents the resin from suffering corrosion and is unlikely to impose a burden on the environment, but also in that it has excellent performance as an acoustic apparatus housing. A material for acoustic apparatus housing, characterized in that it comprises a biodegradable polymer compound, an inorganic material, and a hydrolysis inhibitor.
摘要:
By molding a biodegradable plastic material which is treated with a compound reactive to the active hydrogen in the biodegradable plastic material, a biodegradable plastic material and molding having long-term reliability are obtained.
摘要:
By molding a biodegradable plastic material which is treated with a compound reactive to the active hydrogen in the biodegradable plastic material, a biodegradable plastic material and molding having long-term reliability are obtained.
摘要:
By molding a biodegradable plastic material which is treated with a compound reactive to the active hydrogen in the biodegradable plastic material, a biodegradable plastic material and molding having long-term reliability are obtained.
摘要:
A composition that is advantageous not only in that it has biodegradability and flame retardancy, as well as mechanical strength, but also in that when disposed of the composition has few adverse effects on the natural environment. The composition is characterized in that it includes at least one organic polymer compound having biodegradability, a flame retardant additive, and a hydrolysis inhibitor for the organic polymer compound having biodegradability.
摘要:
A composite composition includes at least one organic polymer compound having biodegradability, vegetable fibers, and a hydrolysis inhibitor for the organic polymer compound having biodegradability.
摘要:
A resin composition that has high mechanical strength properties, has superior chemical characteristics such as chemical resistance and heat resistance, has high degree of freedom of product design, and has a structure considering the impact on environment is provided at low cost. The resin composition composed of a polyamide resin contains a cotton fiber as a natural fiber. The additive amount of the cotton fiber is preferably 1 wt % to 25 wt % both inclusive. The polyamide resin is polyamide 11 using castor oil as a raw material of plant origin. The average fiber diameter of the cotton fiber is 100 μm or less. The polyamide resin and the cotton fiber are melted and kneaded, and then hot-formed, and thereby a shaped article containing a plant fiber can be fabricated. In addition to the cotton fiber, a plant fiber such as a hemp fiber, a bamboo fiber, and wood powder and a biofiber such as a silk fiber may be applied.