摘要:
The present invention provides a fluorine-containing elastomer composition comprising a fluorine-containing elastomer (A) and a fluorine-containing elastomer (B) having a fluorine amount of at least 67% by weigh and a lower molecular weight than the fluorine-containing elastomer (A), wherein the fluorine amount of the fluorine-containing elastomer (B) is larger than a fluorine amount of the fluorine-containing elastomer (A). The present invention also provides a molded article obtained by crosslinking the fluorine-containing elastomer composition.
摘要:
This invention provides a novel compound which can be properly used as a surfactant, a method of producing a fluoropolymer, surfactant and a fluoropolymer aqueous dispersions using the novel compound.This invention is a fluoroalkylcarboxylic acid derivative which is represented by the general formula (i): Rf1(OCH2CF2CF2)n1OCX1X2CF2(Rf2)n2COOM (i) wherein Rf1 represents a straight or branched fluoroalkyl group containing 1 to 20 carbon atoms, which fluoroalkyl group may optionally contain 1 to 5 oxygen atoms in the principal chain thereof, Rf2 represents a straight or branched fluoroalkylene group containing 1 to 25 carbon atoms, said fluoroalkylene group may optionally contain 1 to 5 oxygen atoms in the principal chain thereof, n1 represents an integer of 0 to 3, n2 represents an integer of 0 or 1, X1 and X2 are the same or different and each represents hydrogen atom or fluorine atom, and M represents NH4 or a monovalent metal element.
摘要:
The present invention provides a peroxide-vulcanizable fluorine-containing elastomer composition which is remarkably improved in fluidity and thereby exhibits improved processability, though conventional fluorine-containing elastomer compositions could be molded only by a molding process having a problem in its productivity, for instance, compression molding or transfer molding which has been used so far as a general molding process. The present invention further provides a molded article obtained by vulcanizing the composition. The present invention also provides a fluorine-containing elastomer composition in which a large amount of a filler can be blended. Specifically, the present invention relates to the fluorine-containing elastomer composition comprising a fluorine-containing elastomer (A) composed of a structural unit derived from vinylidene fluoride and/or a structural unit of tetrafluoroethylene and a structural unit derived from at least one other monomer, and having (a) a number average molecular weight (Mn) of 30,000 to 70,000 g/mol, and (b) an iodine content of 0.3 to 1.0% by weight and an organoperoxide vulcanizing agent (B).
摘要:
The present invention has for its object to provide a fluorocopolymer which is available at low cost, has fluidity at room temperature, and is curable, a method of producing the same copolymer and a curable composition having good processability and in situ moldability. The present invention is directed to a fluorocopolymer which is fluid at room temperature and curable, and which is obtainable from a trifluorovinyl group-containing monomer with an ethylenically unsaturated double bond moiety being a trifluorovinyl group.
摘要:
The present invention provides a process for preparing a fluorine-containing elastomer in a high productivity comparable to that of non-iodine transfer polymerization process by carrying out an iodine transfer polymerization at high pressure. The present invention also provides a fluorine-containing elastomer prepared by this process, and fluorine-containing molded articles. The process is a batch copolymerization process conducted under conditions that the reduced temperature of the critical constant is at least 0.95 and the reduced pressure of the critical constant is at least 0.80 wherein the reduced temperature and the reduced pressure are calculated using the Peng-Robinson formula from the critical temperature, the critical pressure and the composition ratio of each of the monomers in the gaseous phase in a reaction vessel, in which ethylenically unsaturated compounds containing at least one fluoroolefine are copolymerized in the presence of a compound having the formula: Rf1·Ix wherein Rf1 is a saturated or unsaturated fluorohydrocarbon or chlorofluorohydrocarbon group having 1 to 16 carbon atoms, and x is the number of bonds of Rf1 and an integer of 1 to 4.
摘要:
A transparent elastomer composition is obtained by co-coagulation of an emulsion of fluorine-containing resin fine particles having an average particle size of from 20 to 150 nm and an emulsion of elastomer particles, in which the fluorine-containing resin fine particles are finely dispersed uniformly in the elastomer. The transparent elastomer composition provides an elastomeric molded article having excellent mechanical strength, abrasion resistance and transparency.
摘要:
To provide a novel and effective cleaning method which can give a cleaned fluorine-containing rubber molded article for semiconductor production apparatuses. The method of cleaning the fluorine-containing rubber molded article for semiconductor production apparatuses, which comprises washing the fluorine-containing rubber molded article at least once with ultra pure water which has a metal content of not more than 1.0 ppm and does not contain fine particles of not less than 0.2 &mgr;m in an amount of more than 300 per 1 ml.
摘要:
A fluorine-containing triallyl isocyanurate of the formula [I]: wherein at least one of X and Y is a fluorine atom, and the other is a hydrogen atom or a fluorine atom, exhibits good curing properties even when it is used as a crosslinking aid for elastomers which are required to have good heat resistance, such as in particular, fluororubbers, and provides cured materials having good mechanical properties and heat resistance.
摘要:
The present invention provides the fluorine-containing elastic copolymer which is excellent in molding processability, particularly molding stability and further vulcanization properties, flowability at molding and compression set of a vulcanized rubber. The copolymer is prepared through emulsion polymerization of vinylidene fluoride and at least one of other monomers in two polymerization stages by using a water-soluble radical polymerization initiator in a very small amount of 0.001 to 0.03% by weight based on the total weight of copolymers prepared in the two stages and an oil-soluble radical polymerization initiator. The present invention also provides a process for preparation thereof and a vulcanizable composition containing the same.
摘要:
The present invention provides a TFE/Pr type elastomer being excellent in not only amine resistance but also heat resistance and chemical resistance and having a small gel content, and a crosslinkable composition comprising the elastomer. The above-mentioned fluorine-containing elastomer is a fluorine-containing elastomer being crosslinkable with the compound (A), comprising 40 to 70% by mole of tetrafluoroethylene unit, 30 to 60% by mole of propylene unit and 0.1 to 2.5% by mole of a carboxyl group-containing vinyl monomer unit and having a Mooney viscosity at 121° C. of 5 to 100.