公开(公告)号：US20050152569A1

公开(公告)日：2005-07-14

申请号：US11033269

申请日：2005-01-12

申请人： Toshiyuki Ono ,  Tatsuya Suzuki

发明人： Toshiyuki Ono ,  Tatsuya Suzuki

IPC分类号： H04R9/02 ,  B29C65/52 ,  H04R1/06 ,  H04R9/06 ,  H04R31/00 ,  B32B31/00 ,  H04R1/02

CPC分类号： B29C65/524 ,  B29C66/1222 ,  B29C66/1224 ,  B29C66/5344 ,  B29C66/8322 ,  H04R1/06 ,  H04R9/06 ,  H04R31/006 ,  H04R2201/34 ,  H04R2400/11

摘要： A frame with a pot type yoke incorporated therein is held on a seating base, and an adhesive supplying means is disposed at a position located in close proximity to this seating base. A supply head of this adhesive supplying means has its supply port opposing an end face of an annular portion. The supply of the adhesive is effected while the seating base is rotated, and the adhesive is supplied starting with one groove, and is supplied continuously up to the other groove.

摘要翻译： 其中结合有盆型轭的框架保持在座位基座上，并且粘合剂供应装置设置在靠近该座座的位置处。 这种粘合剂供应装置的供应头具有与环形部分的端面相对的供给口。 在座椅底座旋转的同时实现粘合剂的供应，并且从一个凹槽开始提供粘合剂，并且连续地供应到另一个凹槽。

公开(公告)号：US6099669A

公开(公告)日：2000-08-08

申请号：US812499

申请日：1997-03-07

申请人： Norio Yuki ,  Toshiyuki Ono ,  Tetsuo Kawahara

发明人： Norio Yuki ,  Toshiyuki Ono ,  Tetsuo Kawahara

IPC分类号： C21D8/02 ,  B21J1/02 ,  C21D6/00 ,  C21D9/46 ,  C22C38/00 ,  C22C38/08 ,  C22F1/10

CPC分类号： C21D6/001 ,  C21D1/76 ,  C21D7/13 ,  C21D8/0205 ,  C21D8/021 ,  C21D8/0226 ,  C21D9/46 ,  C22C1/02 ,  C22C38/08 ,  H01J29/07 ,  H01J9/142 ,  C21D8/0236 ,  C21D8/0268

摘要： Composition segregation which results in streaks in an Fe--Ni alloy sheet shadow-mask is prevented by the following conditions. Heat-treatment from 1150.degree. C. to a temperature lower than the melting point for longer than 1 hour and not longer than 30 hours. Subsequent rough-rolling or forging at a reduction of area of 40% or more. A slab is subjected to removal of oxide scale on its surface and then heated in hydrogen atmosphere having dew point of 10.degree. C. or lower at a temperature of not less than 1100.degree. C. and lower than the melting point for time (t - hour) which is defined by:t.gtoreq.[3.8.times.10.sup.-7 exp (23830/T)]/R,where R is reduction area (%) at the slab production.

摘要翻译： 通过以下条件可防止导致Fe-Ni合金薄片荫罩中的条纹的组成偏析。 从1150℃热处理至低于熔点的温度超过1小时，不超过30小时。 随后的粗轧或锻造面积减小40％以上。 在其表面上除去氧化皮，然后在不低于1100℃的温度并低于熔点的时间（t-）下在露点为10℃或更低的氢气氛中加热， 小时），其由以下定义：t> / = [3.8×10 -7 exp（23830 / T）] / R，其中R是板坯生产时的还原面积（％）。