摘要:
A heat-dissipating black resin composition having excellent physical properties such as heat-dissipation, workability, corrosion resistance, solvent resistance, coating adherence and gloss, and being free from chromium and used for surface treatment of a zinc coated steel sheet and a zinc coated steel sheet treated thereby. The composition includes, based on 100 parts by weight: 10 to 60 parts by weight of a resin composition which at least one main resin and a melamine-based curing agent are mixed in a weight ratio of 10:2-7, the main resin being selected from the group consisting of polyester, epoxy, polyolefin, polyurethane, fluorine, phenol, acryl and polycarbonate resins; 1 to 10 parts by weight of at least one pigment selected from the group consisting of carbon black and carbon nano tube; 1 to 10 parts by weight of a matting agent; and a solvent.
摘要:
A resin-coated steel sheet having excellent properties such as electroconductivity, electrostatic earth property, fingerprint resistance, corrosion resistance, solvent resistance, workability, press formability, workability at multi-processed part, electromagnetic shielding property, adhesion, and heat release property, a resin composition and a surface treatment composition therefore are provided. The resin-coated steel sheet comprising a base steel sheet; and a resin-coating film formed of a resin composition on the surfaces of the base steel sheet, the resin composition comprising a main resin/a melamine-based curing agent composition, a pigment, a flatting agent and at least one of a fingerprint-resistant additive and an electroconductive additive is provided. The resin composition and the surface treatment composition comprising polyethylene acrylate resin and/or polyurethane resin, a melamine-based curing agent, a silane coupling agent, a metal silicate compound and a titanium compound are also provided.
摘要:
Provided are a heat-dissipating black resin composition having excellent physical properties such as heat-dissipation, workability, corrosion resistance, solvent resistance, coating adherence and gloss, and being free from chromium and used for surface treatment of a zinc coated steel sheet, a method for treating a zinc coated steel sheet, and a zinc coated steel sheet treated thereby. The composition includes, based on 100 parts by weight: 10 to 60 parts by weight of a resin composition which at least one main resin and a melamine-based curing agent are mixed in a weight ratio of 10:2-7, the main resin being selected from the group consisting of polyester, epoxy, polyolefin, polyurethane, fluorine, phenol, acryl and polycarbonate resins; 1 to 10 parts by weight of at least one pigment selected from the group consisting of carbon black and carbon nano tube; 1 to 10 parts by weight of a matting agent; and the balance of a solvent. The method includes: coating a steel sheet with the composition so that a thickness of a dry coating film is in a range of 3 to 30 micrometers; and drying the composition, and the steel sheet is treated according to the method.