公开(公告)号：US4332601A

公开(公告)日：1982-06-01

申请号：US162400

申请日：1980-06-23

申请人： Arno Wegerhoff ,  Hans Zengel ,  Walter Brodowski ,  Heinz Beck ,  Ernst Seeberger ,  Gerhard Steenken ,  Karlheinz Hillermeider

发明人： Arno Wegerhoff ,  Hans Zengel ,  Walter Brodowski ,  Heinz Beck ,  Ernst Seeberger ,  Gerhard Steenken ,  Karlheinz Hillermeider

IPC分类号： B01D39/06 ,  B01D39/20 ,  C03B37/01 ,  C03B37/03 ,  C03C13/00 ,  C04B35/622 ,  C08J5/14 ,  D01F9/08 ,  F16D69/02 ,  C03C25/06 ,  B44C1/22 ,  C03C15/00

CPC分类号： C03B37/03 ,  B01D39/06 ,  B01D39/2017 ,  C03B37/011 ,  C03C13/005 ,  C04B35/6224 ,  D01F9/08 ,  F16D69/026 ,  F16D2200/0065 ,  Y02P40/57 ,  Y10T428/2904 ,  Y10T428/2975 ,  Y10T428/298 ,  Y10T442/696

摘要： Process for the production of water containing water glass fibers of the type in which alkali water glass is dry spun into water containing fibers, the improvement being dry-spinning water glass free from non-alkaline compounds having a molar ratio of alkaline oxide to silicon dioxide of from about 1:3 to 1:1.9 and a viscosity of about 10-700 Pa measured at 30.degree. C., at 10.degree.-50.degree. C. in a drying funnel of a temperature of more than 100.degree. C., at a discharge velocity of minimum 5m/min.

摘要翻译： 生产含水玻璃纤维的含水水玻璃纤维干法纺丝成含水纤维的方法，其改进之处在于，不含碱性氧化物与二氧化硅摩尔比的非碱性化合物的干纺丝水玻璃 为约1:3至1:1.9，粘度为约10-700Pa，在30℃，10°-50℃下，在温度大于100℃的干燥漏斗中，在 排气速度最小为5m / min。

公开(公告)号：US4471019A

公开(公告)日：1984-09-11

申请号：US517730

申请日：1983-07-27

申请人： Arno Wegerhoff ,  Hans Zengel ,  Walter Brodowski ,  Heinz Beck ,  Ernst Seeberger ,  Gerhard Steenken ,  Karlheinz Hillermeider

发明人： Arno Wegerhoff ,  Hans Zengel ,  Walter Brodowski ,  Heinz Beck ,  Ernst Seeberger ,  Gerhard Steenken ,  Karlheinz Hillermeider

IPC分类号： B01D39/06 ,  B01D39/20 ,  C03B37/01 ,  C03B37/03 ,  C03C13/00 ,  C04B35/622 ,  C08J5/14 ,  D01F9/08 ,  F16D69/02 ,  B32B17/02

CPC分类号： C03B37/03 ,  B01D39/06 ,  B01D39/2017 ,  C03B37/011 ,  C03C13/005 ,  C04B35/6224 ,  D01F9/08 ,  F16D69/026 ,  F16D2200/0065 ,  Y02P40/57 ,  Y10T428/2904 ,  Y10T428/2975 ,  Y10T428/298 ,  Y10T442/696

摘要： Water-containing water glass fibers are disclosed, substantially free from non-alkaline compounds and having a water content of from about 15 to 30% by weight, a tear strength of from about 5 to 30 cN/tex, a ratio of alkaline oxide to silicon dioxide of from about 1:3 to 1:1.9, an amorphous structure and a density of from about 2 g/cm.sub.3 to 2.5 g/cm.sup.3. The fibers are preferably cut into lengths of from 1 to 40 mm. They may be used for subsequent production of silica fibers, a technique more advantageous than producing the latter from a melt containing SiO.sub.2 or by acid-leaching of glass fibers. The silica fibers are useful for producing wet webs, filter linings and reinforcing material.

摘要翻译： 公开了含水水玻璃纤维，基本上不含非碱性化合物，水含量为约15至30重量％，撕裂强度为约5至30cN / tex，碱性氧化物与 约1：3至1：1.9的二氧化硅，无定形结构和约2g / cm 3至2.5g / cm 3的密度。 纤维优选切割成1至40mm的长度。 它们可以用于随后生产二氧化硅纤维，这种技术比从含有SiO 2的熔体或通过酸浸玻璃纤维制备后者更有利。 二氧化硅纤维可用于生产湿网，过滤衬垫和增强材料。

公开(公告)号：US4332600A

公开(公告)日：1982-06-01

申请号：US110002

申请日：1980-01-07

申请人： Arno Wegerhoff ,  Hans Zengel ,  Walter Brodowski ,  Heinz Beck ,  Ernst Seeberger ,  Gerhard Steenken ,  Karlheinz Hillermeider

发明人： Arno Wegerhoff ,  Hans Zengel ,  Walter Brodowski ,  Heinz Beck ,  Ernst Seeberger ,  Gerhard Steenken ,  Karlheinz Hillermeider

IPC分类号： B01D39/06 ,  B01D39/20 ,  C03B37/01 ,  C03B37/03 ,  C03C13/00 ,  C04B35/622 ,  C08J5/14 ,  D01F9/08 ,  F16D69/02 ,  C03C25/06 ,  B44C1/22 ,  C03C15/00

CPC分类号： C03B37/03 ,  B01D39/06 ,  B01D39/2017 ,  C03B37/011 ,  C03C13/005 ,  C04B35/6224 ,  D01F9/08 ,  F16D69/026 ,  F16D2200/0065 ,  Y02P40/57 ,  Y10T428/2904 ,  Y10T428/2975 ,  Y10T428/298 ,  Y10T442/696

摘要： Process for the production of silica fibers of the type in which alkali water glass is dry spun into water-containing alkali silicate fibers which are then contacted with solutions containing hydrogen ions for transforming into silica fibers, the improvement being dry-spinning glass free from non-alkaline compounds having a molar ratio of alkaline oxide to silic dry dioxide of from about 1:3 to 1:1.9 and a viscosity of about 10-700 Pa measured at 30.degree. C., at 10.degree.-50.degree. C. in a drying funnel of a temperature of more than 100.degree. C., at a discharge velocity of minimum 5 m/min.