公开(公告)号：US4353951A

公开(公告)日：1982-10-12

申请号：US269291

申请日：1981-06-01

申请人： Teruo Yukitoshi ,  Takao Hino ,  Yoshinobu Ohya

发明人： Teruo Yukitoshi ,  Takao Hino ,  Yoshinobu Ohya

IPC分类号： B32B15/088 ,  B23K11/11 ,  B23K11/16 ,  B32B15/01 ,  B32B15/08 ,  B32B15/092 ,  B32B15/095 ,  B32B27/14

CPC分类号： B32B15/08 ,  Y10S428/901 ,  Y10T428/24826 ,  Y10T428/24893 ,  Y10T428/24917 ,  Y10T428/2495 ,  Y10T428/24967 ,  Y10T428/252 ,  Y10T428/256 ,  Y10T428/2982 ,  Y10T428/2991 ,  Y10T428/2996 ,  Y10T428/31678

摘要： There is provided a spot-weldable bonded clad metal plate wherein the metal sheets are 0.05-1.0 mm thick and at least 0.4 mm thick, respectively, the adhesive layer has a thickness of 15-60 microns and the adhesive layer contains 10-100 g/m.sup.2 of metallic powder having a particle diameter corresponding to 0.5-1.5 times the thickness of the adhesive layer. The metallic powder is not necessarily entirely metallic and, for example, glass beads having surfaces coated with a metal can also be used. As the adhesive, a polyamide resin adhesive, particularly, a hot melt type polyamide resin adhesive is preferred.The bonded clad metal plate shows excellent adhesion strength, and in spite of such thin metal sheets, does not blister when spot-welded.

摘要翻译： 提供了可点焊接合复合金属板，其中金属片分别为0.05-1.0mm厚且至少为0.4mm厚，粘合剂层的厚度分别为15-60微米，粘合剂层含有10-100g / m 2的金属粉末，其粒径对应于粘合剂层的厚度的0.5-1.5倍。 金属粉末不一定完全是金属的，例如也可以使用具有金属表面的玻璃珠。 作为粘合剂，优选聚酰胺树脂粘合剂，特别是热熔型聚酰胺树脂粘合剂。 接合复合金属板显示出优异的粘合强度，并且尽管这种薄金属片，当点焊时不起泡。

公开(公告)号：US4222771A

公开(公告)日：1980-09-16

申请号：US5762

申请日：1979-01-23

申请人： Teishiro Oda ,  Takashi Daikoku ,  Teruo Yukitoshi ,  Kazuhiko Nishida

发明人： Teishiro Oda ,  Takashi Daikoku ,  Teruo Yukitoshi ,  Kazuhiko Nishida

IPC分类号： C22C38/00 ,  C22C38/22 ,  C22C39/02

CPC分类号： C22C38/22

摘要： High chromium steel, for use at high temperature, of a mixed structure containing ferrite and 0.02-0.09% C, less than 1.0% Si, 0.1-2.0% Mn, 7.0-13.0% chromium, 1.2-3.0% Mo, and the rest being iron and the usual impurities, or further adding aluminum in an amount less than 0.1% to said composition, or further adding 0.001-0.1% boron and less than 0.1% Ti necessary to cause the boron to act effectively, said steel being heated at temperatures lower than about 1050.degree. C. to prevent the oxidation of the steel.

摘要翻译： 含有铁素体和0.02-0.09％C，小于1.0％Si，0.1-2.0％Mn，7.0-13.0％铬，1.2-3.0％Mo的混合结构的高铬钢，其余为高铬钢 或者进一步向所述组合物中加入小于0.1％的铝，或者进一步加入0.001-0.1％的硼和小于0.1％的Ti以使硼有效地起作用，所述钢被加热到 温度低于约1050℃，以防止钢的氧化。