摘要:
The random, hydrogenated copolymers according to the present invention of unsubstituted conjugated dienes and substituted conjugated dienes, having a glass transition temperature of ≦−60° C., an enthalpy of fusion of ≦100 J/g and a content of residual double bonds in the range from 0 to 80%, are suitable for the production of rubber moldings of all kinds which have good resistance to ageing and high resilience at low temperatures. In particular, various tire components and industrial rubber articles may be mentioned as rubber moldings. The copolymers are also suitable for the rubber modification of brittle thermoplastics.
摘要:
The random, hydrogenated copolymers according to the present invention of unsubstituted conjugated dienes and substituted conjugated dienes, having a glass transition temperature of ≦−60° C., an enthalpy of fusion of ≦100 J/g and a content of residual double bonds in the range from 0 to 80%, are suitable for the production of rubber moldings of all kinds which have good resistance to ageing and high resilience at low temperatures. In particular, various tire components and industrial rubber articles may be mentioned as rubber moldings. The copolymers are also suitable for the rubber modification of brittle thermoplastics.
摘要:
By use of a process for the production of a fibre-composite material, comprising the following steps: a) one or more fibre bundle(s) is/are drawn by way of one or more spreader device(s) into an impregnation chamber in such a way as to give at least two mutually superposed, spatially separate and spread fibre webs; b) melt is introduced by way of horizontally oriented distributor bars, in each case arranged between two fibre webs; c) the individual fibre webs are caused to converge in such a way that they are mutually superposed and contact one another; d) after the fibre webs have converged they are drawn, at the end of the operating unit, through a take-off die where the first shaping takes place, and also by use of a corresponding device, very good impregnation quality is achieved through a specific wetting method implemented after a high degree of expanding, and also through subsequent relative longitudinal and transverse movements of the individual fibres.
摘要:
Very good impregnation quality is achieved by a process for production of a fiber-composite material, with introducing a fiber layer by a spreader device and thus spreading to a width greater than that of the final product, at least by a factor of 1.2, where the extent of spreading of the fiber layer is such that its average thickness is 1 to 50 times the filament diameter; applying a melt by at least one applicator nozzle to the spread material; by virtue of cross-section-narrowing, the mould brings the width of the wetted fiber layer at least to the cross section with which the product leaves the take-off die; a radius then deflects the wetted fibers by an angle of 5 to 60°; a relaxation zone renders the fiber distribution more uniform to give a uniform height; achieving the first shaping by a take-off die at the end of the mould.