摘要:
The present invention pertains to a UHMWPE film having a tensile strength of at least 2.0 GPa, a tensile energy to break of at least 30 J/g, an Mw of at least 500 000 gram/mole, and a Mw/Mn ratio of at most 6. The film may be manufactured via a process which comprises subjecting a starting UHMWPE with a weight average molecular weight of at least 500 000 gram/mole, an elastic shear modulus determined directly after melting at 160° C. of at most 0.9 MPa, and a Mw/Mn ratio of at most 6 to a compacting step and a stretching step under such conditions that at no point during the processing of the polymer its temperature is raised to a value above its melting point. The film may be used as starting material in any applications where high tensile strength and high energy to break are important. Suitable applications include ballistic applications, ropes, cables, nets, fabrics, and protective applications.
摘要:
The present invention pertains to a UHMWPE film having a tensile strength of at least 2.0 GPa, a tensile energy to break of at least 30 J/g, an Mw of at least 500 000 gram/mole, and a Mw/Mn ratio of at most 6. The film may be manufactured via a process which comprises subjecting a starting UHMWPE with a weight average molecular weight of at least 500 000 gram/mole, an elastic shear modulus determined directly after melting at 160° C. of at most 0.9 MPa, and a Mw/Mn ratio of at most 6 to a compacting step and a stretching step under such conditions that at no point during the processing of the polymer its temperature is raised to a value above its melting point. The film may be used as starting material in any applications where high tensile strength and high energy to break are important. Suitable applications include ballistic applications, ropes, cables, nets, fabrics, and protective applications.
摘要:
A process for manufacturing high molecular weight polyethylene fibers, including subjecting a polyethylene tape with a weight average molecular weight of at least 500,000 grams/mole, a Mw/Mn ratio of at most 6, and a 200/110 uniplanar orientation parameter of at least 3 to a force in the direction of the thickness of the tape over the entire width of the tape. A polyethylene fiber having a Mw of at least 500 000 gram/mole, a Mw/Mn ratio of at most 6, and a 020 uniplanar orientation value of at most 55°.
摘要:
A process for manufacturing high molecular weight polyethylene fibers, including subjecting a polyethylene tape with a weight average molecular weight of at least 500,000 grams/mole, a Mw/Mn ratio of at most 6, and a 200/110 uniplanar orientation parameter of at least 3 to a force in the direction of the thickness of the tape over the entire width of the tape. A polyethylene fiber having a Mw of at least 500 000 gram/mole, a Mw/Mn ratio of at most 6, and a 020 uniplanar orientation value of at most 55°.
摘要:
A process for rolling and stretching of a sheet into a tape is provided. A sheet may be rolled into a rolled sheet in the nip between two rolls of the calender and the rolled sheet is stretched immediately thereafter into a tape on the surface of one of the two calender rolls. The speed of the rolled sheet on the surface of the calender roll may be higher than the speed of the calender roll. The position of the start of the neck-down of the rolled sheet and the rate of neck-down can be easily controlled by the proposed process.
摘要:
A process for rolling and stretching of a sheet into a tape is provided. A sheet may be rolled into a rolled sheet in the nip between two rolls of the calender and the rolled sheet is stretched immediately thereafter into a tape on the surface of one of the two calender rolls. The speed of the rolled sheet on the surface of the calender roll may be higher than the speed of the calender roll. The position of the start of the neck-down of the rolled sheet and the rate of neck-down can be easily controlled by the proposed process.