The present invention provides a ceramic material allowing a pellet having higher density and satisfactory Li ion conduction to be obtained. The ceramic material contains Li, La, Zr, Al and O and has a garnet-type or garnet-like crystal structure, the ratio of the number of moles of Li with respect to La being 2.0 or greater to 2.5 or lower.
摘要:
A solid electrolyte structure containing a porous solid electrolyte is prepared. At least the porous solid electrolyte of the solid electrolyte structure is immersed in a first sol solution containing at least a precursor of an electrode active material as a solute. Then, the first sol solution, in which the porous solid electrolyte is immersed, is heated. A solvent of the first sol solution is evaporated by the heating, whereby a pore of the porous solid electrolyte is filled with a high concentration (a large amount) of the electrode active material precursor.
摘要:
Disclosed is an ink composition including: (1) a pigment; (2) a polymerization initiator having a content of 2% by mass or more with respect to a total amount of the composition and having a solubility with respect to pure water at 25° C. of 5 to 8 g/l; (3) a compound A that is at least one selected from the group consisting of dimethylacrylamide, diethylacrylamide, N-isopropylacrylamide, dimethylacetamide, N-ethylpyrrolidone, 1-cyclohexyl-2-pyrrolidone, 1-(2-hydroxyethyl)-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, tetramethylurea and gamma-valerolactone; (4) a polymerizable compound having two or more ethylenically unsaturated double bonds; and (5) water having a content of 50% by mass or more with respect to the total amount of the composition.