摘要:
Water-continuous emulsion of elastomeric polymers are disclosed having a solids content of greater than 75%, an average particle size less than 5 μm, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water comprising; an elastomeric polymer, surfactant, water, optional plasticizer, optional low molecular weight acid, and is essentially free of organic solvents. The water-continuous emulsions of elastomeric polymers can be prepared by; (I) forming a premix that is essentially free of organic solvents comprising an elastomeric polymer and surfactant, and optionally a plasticizer and low molecular weight acid, and (II) adding water to the premix with mixing to form a water continuous emulsion of the elastomeric polymer having a solids content of greater than 75%, an average particle size less than 5 μm, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water.
摘要:
Water-continuous emulsion of elastomeric polymers are disclosed having a solids content of greater than 75%, an average particle size less than 5 &mgr;m, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water comprising; an elastomeric polymer, surfactant, water, optional plasticizer, optional low molecular weight acid, and is essentially free of organic solvents. The water-continuous emulsions of elastomeric polymers can be prepared by; (I) forming a premix that is essentially free of organic solvents comprising an elastomeric polymer and surfactant, and optionally a plasticizer and low molecular weight acid, and (II) adding water to the premix with mixing to form a water continuous emulsion of the elastomeric polymer having a solids content of greater than 75%, an average particle size less than 5 &mgr;m, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water.
摘要:
Water-continuous emulsion of silylated elastomeric polymers are disclosed having a solids content of greater than 75%, an average particle size less than 5 &mgr;m, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water comprising; a silylated elastomeric polymer, surfactant, water, optional plasticizer, and optional low molecular weight acid. The water-continuous emulsions of silylated elastomeric polymers can be prepared by; (I) forming a premix comprising an elastomeric polymer and surfactant, and optionally a plasticizer and low molecular weight acid, and (II) adding water to the premix with mixing to form a water continuous emulsion of the silylated elastomeric polymer having a solids content of greater than 75%, an average particle size less than 5 &mgr;m, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water.
摘要:
Water-continuous emulsion of silylated elastomeric polymers are disclosed having a solids content of greater than 75%, an average particle size less than 5 &mgr;m, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water comprising; a silylated elastomeric polymer, surfactant, water, optional plasticizer, and optional low molecular weight acid. The water-continuous emulsions of silylated elastomeric polymers can be prepared by; (I) forming a premix comprising an elastomeric polymer and surfactant, and optionally a plasticizer and low molecular weight acid, and (II) adding water to the premix with mixing to form a water continuous emulsion of the silylated elastomeric polymer having a solids content of greater than 75%, an average particle size less than 5 &mgr;m, and having sufficient stability to produce a stable lower solids emulsion upon dilution with water.
摘要:
The discoloration of a non-acidic room temperature vulcanizable silicone sealant containing a ultraviolet radiation degradable fungicide is delayed by adding zinc oxide.
摘要:
The longevity of a surface driving oil layer on a room temperature vulcanizable silicone sealant is increased by adding zinc oxide to a non-acidic composition and exposing the composition to atmospheric moisture which forms the surface drying oil layer on an air exposed surface.