摘要:
The present invention provides a two-stage process for the production of polyester carbonates with aliphatic dicarboxylic acids, the polyester carbonates obtained thereby, a process for the production of extrudates and molded articles from the polyester carbonates, and the extrudates and molded articles obtained thereby.
摘要:
This invention relates to the use of polycarbonate for the production of an optical recording medium in which secure high speed operation, a transcriptability of the pit/groove structure of >85% and sufficient disc flatness can be achieved and the polycarbonate is based on bisphenol A and the polycarbonate contains a release agent in an amount less than 2000 ppm.
摘要:
This invention relates to the use of polycarbonate for the production of an optical recording medium in which secure high speed operation, a transcriptability of the pit/groove structure of >85% and sufficient disc flatness can be achieved.
摘要:
A copolycarbonate having glass transition temperature not higher than 160° C. and a rheooptic constant not higher than 4 is disclosed. Containing structural units conforming to wherein the radicals R1 each independently denotes a C1-12-alkyl radical or a halogen atom and n is 0 to 3, the copolycarbonate is suitable for the preparation of lenses and optical mass storage means.
摘要:
This invention relates to DVDs made from polycarbonate and a special UV curable bonder material consisting of A) an urethane acrylate oligomer as binder, which is the reaction product of i) one or more polyisocyanates and ii) one or more hydroxyfunctional lactone ester (meth)acrylates having a number average molecular weight of from 200 g/mol to 2000 g/mol and having the formula: CH2═C(R1)—C(O)—O—R2—[O—C(O)—R3]n—OH wherein, n is an integer from 1 to 5, R1 is hydrogen or methyl, R2 represents an alkylene group or substituted alkylene group having from 2 to 10 carbon atoms and R3 represents a straight or branched chain alkylene group of from 3 to 8 carbon atoms, and which may be substituted with one or more alkyl groups having from 1 to 12 carbon atoms, B) a reactive thinner, comprising of mono functional acrylates and/or (meth)acrylates C) a photo initiator and D) optional additives which offers improved performance at high data transfer rates.
摘要:
A polycarbonate resin comprising fluorescing particles that feature a particular size distribution is disclosed. The size distribution of these particles that fluoresce upon excitation at wavelengths of 400-440 nm, 50× magnification and illumination time of 40 msec per scan was found to be critical in determining the suitability of the resin for optical, particularly optical storage, applications.
摘要:
A polymeric material suitable for making a substrate for optical data storage disks is disclosed. The material, preferably aromatic polycarbonate is characterized in that the potential on 95 to 100% of the total surface of a disk molded therefrom is from −1.5 to +1.5 kV, and in that the potential on 0 to 5% of the total surface of said disk is between −1.5 and −2.5, and +1.5 to +2.5, and in that the potential on no more than 1% of the total surface of said disk is less than −2.5 kV and more than +2.5 kV. The potential measurements are carried out by means of a Monroe probe at a distance of 3.5 mm from the surface of the disk, the scanning region is in each case 12 cm in the X- and Y-direction, and in each case in steps of 2 mm in the X- and in the Y-directions.
摘要:
Optical data carrier comprising a preferably transparent substrate which may, if desired, have previously been coated with one or more reflection layers and to whose surface a light-writeable information layer, if desired one or more reflection layers and if desired a protective layer or a further substrate or a covering layer have been applied, which can be written on and read by means of infrared light, preferably laser light, particularly preferably light having a wavelength in the range 750-800 nm, in particular 770-790 nm, where the information layer comprises a light-absorbent compound and, if desired, a binder, characterized in that at least one cobalt(III) phthalocyanine in which the Co metal centre bears two axial substituents R1 and R2 which represent, independently of one another, CN, SCN, alkoxy or alkylthio is used as light-absorbent compound.
摘要:
This invention relates to an optical recording medium in which at least a recording layer and a light transmitting layer are sequentially formed on a substrate and in which the light is illuminated from the light transmitting layer side for recording and/or reproducing information signals, said substrate comprising an injection molded part, and said substrate having a Young's modulus E of at least 2.15 GPa and a Q factor of lower than 160 measured at 25° C. at 2000 Hz in accordance to ASTM E 756-05 05 and a transcriptability of the pit/groove structure of >85%.
摘要翻译:本发明涉及一种光记录介质,其中至少记录层和透光层依次形成在基板上,并且其中光从光透射层侧照射以用于记录和/或再现信息信号,所述基板 包括注塑部件,并且所述基材根据ASTM E 756-05 05在2000Hz下在25℃下测量的杨氏模量E为至少2.15GPa和低于160的Q因子,并且其转录率 坑/槽结构> 85%。
摘要:
Optical recording mediums comprising a substrate and a recording layer and a light transmitting layer sequentially disposed on the substrate; wherein the substrate comprises one or more parts selected from the group consisting of injection molded parts, injection molded sandwich structures having a molded surface layer and a molded core layer or two injection molded parts which are UV-bonded, and combinations thereof; and wherein the substrate has a Young's modulus E of at least 2.15 GPa and a Q factor of lower than 160 measured at 25° C. at 2000 Hz in accordance to ASTM E 756-05.
摘要翻译:包括基板和记录层的光记录介质和顺序地设置在基板上的透光层; 其特征在于,所述基板包括选自注射成型部件,具有模制表面层的注射成型夹层结构和模制芯层或两个UV结合的注射成型部件的一个或多个部件及其组合; 并且其中所述基材的杨氏模量E至少为2.15GPa,Q值低于160,根据ASTM E 756-05在25℃下以2000Hz测量。