摘要:
The present invention aims to provide a toner having excellent developability and excellent low-temperature fixability without causing adhesion of ejected sheets even in a high-speed oilless fixing system and capable of preventing a frameless printing from causing a twisted offseting phenomenon. Specifically, provided is a toner having toner particles including at least a binder resin and a colorant, in which, when the toner is dissolved in a tetrahydrofuran (THF) solvent at 25° C. for 24 hours, the ratio of a THF-soluble matter having an intrinsic viscosity of 5.0×10−2 dl/g or less with respect to the total amount of the THF-soluble matter in a GPC-RALLS-viscometer analysis is 15.0 mass % to 60.0 mass %, and the ratio of a THF-soluble matter having an intrinsic viscosity of 1.5×10−1 dl/g or more with respect to the total amount of the THF-soluble matter in a GPC-RALLS-viscometer analysis is 20.0 mass % to 40.0 mass %.
摘要:
The present invention aims to provide a toner having excellent developability and excellent low-temperature fixability without causing adhesion of ejected sheets even in a high-speed oilless fixing system and capable of preventing a frameless printing from causing a twisted offseting phenomenon. Specifically, provided is a toner having toner particles including at least a binder resin and a colorant, in which, when the toner is dissolved in a tetrahydrofuran (THF) solvent at 25° C. for 24 hours, the ratio of a THF-soluble matter having an intrinsic viscosity of 5.0×10−2 dl/g or less with respect to the total amount of the THF-soluble matter in a GPC-RALLS-viscometer analysis is 15.0 mass % to 60.0 mass %, and the ratio of a THF-soluble matter having an intrinsic viscosity of 1.5×10−1 dl/g or more with respect to the total amount of the THF-soluble matter in a GPC-RALLS-viscometer analysis is 20.0 mass % to 40.0 mass %.
摘要:
A toner is provided which can stably provide a favorable density stability, line reproducibility and dot reproducibility even in high-speed copying machines, printers and the like which form high resolution latent images over a long period regardless of environmental conditions, and can provide the image quality adaptable to embedded pattern printing, QR code printing and the like. The present invention is characterized in that the toner which includes toner particles including at least a binder resin and a colorant, and a fine silica powder, has a volume median diameter (D50) of not less than 0.70 μm and not more than 3.00 μm, and a total pore volume of not more than 0.200 cm3/g, measured in the range of the pore diameter from not less than 1.7 nm and not more than 300.0 nm.
摘要:
A toner is provided which can stably provide a favorable density stability, line reproducibility and dot reproducibility even in high-speed copying machines, printers and the like which form high resolution latent images over a long period regardless of environmental conditions, and can provide the image quality adaptable to embedded pattern printing, QR code printing and the like. The present invention is characterized in that the toner which includes toner particles including at least a binder resin and a colorant, and a fine silica powder, has a volume median diameter (D50) of not less than 0.70 μm and not more than 3.00 μm, and a total pore volume of not more than 0.200 cm3/g, measured in the range of the pore diameter from not less than 1.7 nm and not more than 300.0 nm.
摘要:
Provided is a magnetic toner comprising magnetic toner particles each comprising at least a binder resin and a magnetic iron oxide, the magnetic toner being excellent in developability and environmental stability, and being capable of reducing a toner consumption. A saturation magnetization σs and a remanent magnetization σr of the magnetic toner in a measured magnetic field of 795.8 kA/m are arranged in the range of 5 to 60 Am2/kg and in the range of 0.1 to 10.0 Am2/kg, respectively, and the binder resin having a polyester component polymerized by using a Ti chelate compound as a catalyst is used.
摘要:
A toner of the present invention comprises at least a binder resin comprising as a main component a polyester resin, a wax, and a colorant, in which in case of measuring a wettability of the toner with respect to a mixed solvent of methanol and water in terms of an optical transimittance at an optical wavelength of 780 nm, a methanol concentration of the mixed solvent is in a range of 45 to 65% by volume when an optical transmittance is 80% and 10%, respectively; a melt index (MI) is of 0.1 to 10 g/lO min at a temperature of 125° C. and a load of 5 kg; the toner comparises a resin component insoluble to tetrahydrofuran (THF insoluble component) in an amount of 5 to 40% by mass based on a mass of the binder resin; and the toner comprises a THF soluble component having a main peak in a molecular weight region of 3,000 to 20,000, and has a proportion of a component having a molecular weight of 10,000 or less in the THF soluble component is 50% by mass or more, according to a chromatogram of the THF soluble component measured by gel permeation chromatography. According to the toner of the present invention, it is possible to control lowering of an image density after leaving under a high temperature and high humidity environment, and a decline in the image density due to a charge-rise phenomenon upon low rate printing. Further, the toner has excellent fixing property and high temperature offset characteristic, and occurring of the end-offset is controlled.
摘要:
A toner of the present invention comprises at least a binder resin comprising as a main component a polyester resin, a wax, and a colorant, in which in case of measuring a wettability of the toner with respect to a mixed solvent of methanol and water in terms of an optical transimittance at an optical wavelength of 780 nm, a methanol concentration of the mixed solvent is in a range of 45 to 65% by volume when an optical transmittance is 80% and 10%, respectively; a melt index (MI) is of 0.1 to 10 g/10 min at a temperature of 125° C. and a load of 5 kg; the toner comparises a resin component insoluble to tetrahydrofuran (THF insoluble component) in an amount of 5 to 40% by mass based on a mass of the binder resin; and the toner comprises a THF soluble component having a main peak in a molecular weight region of 3,000 to 20,000, and has a proportion of a component having a molecular weight of 10,000 or less in the THF soluble component is 50% by mass or more, according to a chromatogram of the THF soluble component measured by gel permeation chromatography. According to the toner of the present invention, it is possible to control lowering of an image density after leaving under a high temperature and high humidity environment, and a decline in the image density due to a charge-rise phenomenon upon low rate printing. Further, the toner has excellent fixing property and high temperature offset characteristic, and occurring of the end-offset is controlled.
摘要:
Provided is a magnetic toner comprising magnetic toner particles each comprising at least a binder resin and a magnetic iron oxide, the magnetic toner being excellent in developability and environmental stability, and being capable of reducing a toner consumption. A saturation magnetization σs and a remanent magnetization σr of the magnetic toner in a measured magnetic field of 795.8 kA/m are arranged in the range of 5 to 60 Am2/kg and in the range of 0.1 to 10.0 Am2/kg, respectively, and the binder resin having a polyester component polymerized by using a Ti chelate compound as a catalyst is used.
摘要:
A toner of the present invention comprises at least a binder resin comprising as a main component a polyester resin, a wax, and a colorant, in which in case of measuring a wettability of the toner with respect to a mixed solvent of methanol and water in terms of an optical transimittance at an optical wavelength of 780 nm, a methanol concentration of the mixed solvent is in a range of 45 to 65% by volume when an optical transmittance is 80% and 10%, respectively; a melt index (MI) is of 0.1 to 10 g/10 min at a temperature of 125° C. and a load of 5 kg; the toner comparises a resin component insoluble to tetrahydrofuran (THF insoluble component) in an amount of 5 to 40% by mass based on a mass of the binder resin; and the toner comprises a THF soluble component having a main peak in a molecular weight region of 3,000 to 20,000, and has a proportion of a component having a molecular weight of 10,000 or less in the THF soluble component is 50% by mass or more, according to a chromatogram of the THF soluble component measured by gel permeation chromatography. According to the toner of the present invention, it is possible to control lowering of an image density after leaving under a high temperature and high humidity environment, and a decline in the image density due to a charge-rise phenomenon upon low rate printing. Further, the toner has excellent fixing property and high temperature offset characteristic, and occurring of the end-offset is controlled.
摘要:
A toner of the present invention comprises at least a binder resin comprising as a main component a polyester resin, a wax, and a colorant, in which in case of measuring a wettability of the toner with respect to a mixed solvent of methanol and water in terms of an optical transimittance at an optical wavelength of 780 nm, a methanol concentration of the mixed solvent is in a range of 45 to 65% by volume when an optical transmittance is 80% and 10%, respectively; a melt index (MI) is of 0.1 to 10 g/10 min at a temperature of 125° C. and a load of 5 kg; the toner comparises a resin component insoluble to tetrahydrofuran (THF insoluble component) in an amount of 5 to 40% by mass based on a mass of the binder resin; and the toner comprises a THF soluble component having a main peak in a molecular weight region of 3,000 to 20,000, and has a proportion of a component having a molecular weight of 10,000 or less in the THF soluble component is 50% by mass or more, according to a chromatogram of the THF soluble component measured by gel permeation chromatography. According to the toner of the present invention, it is possible to control lowering of an image density after leaving under a high temperature and high humidity environment, and a decline in the image density due to a charge-rise phenomenon upon low rate printing. Further, the toner has excellent fixing property and high temperature offset characteristic, and occurring of the end-offset is controlled.