摘要:
A material for producing far-infrared radiation is disclosed. The material comprises a substrate and an Al--Mn alloy-derived oxide surface layer on the substrate, the oxide surface layer being porous with an average pore diameter of 0.01-2.0 micrometers and a porosity of 10.sup.3 -10.sup.12 pores/cm.sup.2, the weight ratio of Mn/Al of the oxide surface layer being 0.001-2.0, and the thickness of the oxide surface layer being 0.1-100 micrometers.
摘要:
A metal foil for a current collector of a secondary battery formed by electrodeposition and has a thickness (T) of 8 to 40 μm, the metal foil satisfying the following formulae: 4.9×108≦T×S×Y≦31×108 4.5≦ε−(0.0005×T2)≦15 where S is a breaking strength (MPa), ε is a tensile elongation (%) and Y is a Young's modulus (MPa). This foil is preferably a nickel foil and is manufactured by softening or annealing the metal foil obtained by electrodeposition. Thereby, a metal foil for a negative electrode of a secondary battery is obtained with an excellent capability of supporting the active material and large electric conductivity.
摘要:
A method and apparatus for molten salt electroplating a steel member are disclosed, in which the surface of the steel member is activated by anodic treatment and the molten salt electroplating is performed on the activated surface of said steel member.
摘要:
A method and apparatus for molten salt electroplating a steel member are disclosed, in which the surface of the steel member is activated by anodic treatment and the molten salt electroplating is performed on the activated surface of said steel member.