摘要:
Disclosed is a cold-rolled steel sheet having a specific steel composition and having a composite steel structure including a ferrite structure and a martensite-containing second phase. In a surface region of the steel sheet from the surface to a depth one-tenth the gage, the number density of n-ary groups of inclusions determined by specific n-th determinations is 120 or less per 100 cm2 of a rolling plane, in which the distance in steel sheet rolling direction between outermost surfaces of two outermost particles of the group of inclusions is 80 μm or more. Also disclosed is a cold-rolled steel sheet having a specific steel composition and having a steel structure of a martensite single-phase structure. In the surface region, the number density of groups of inclusions, in which the distance between the outermost surfaces is 100 μm or more, is 120 or less per 100 cm2 of a rolling plane.
摘要:
Disclosed is a cold-rolled steel sheet having a specific steel composition and having a composite steel structure including a ferrite structure and a martensite-containing second phase. In a surface region of the steel sheet from the surface to a depth one-tenth the gage, the number density of n-ary groups of inclusions determined by specific n-th determinations is 120 or less per 100 cm2 of a rolling plane, in which the distance in steel sheet rolling direction between outermost surfaces of two outermost particles of the group of inclusions is 80 μm or more. Also disclosed is a cold-rolled steel sheet having a specific steel composition and having a steel structure of a martensite single-phase structure. In the surface region, the number density of groups of inclusions, in which the distance between the outermost surfaces is 100 μm or more, is 120 or less per 100 cm2 of a rolling plane.
摘要:
A cold-rolled steel sheet has a chemical composition of C: 0.12% to 0.3%, Si: 0.5% or less, Mn: less than 1.5%, Al: 0.15% or less, N: 0.01% or less, P: 0.02% or less, and S: 0.01% or less, with the remainder including iron and inevitable impurities and has a martensite single-phase structure as its steel microstructure. In a surface region of the steel sheet from the surface to a depth one-tenth the gauge, the number density of n-ary groups of inclusions determined by specific n-th determinations is 120 or less per 100 cm2 of a rolling plane, where the distance in steel sheet rolling direction between outermost surfaces of two outermost particles of the group of inclusions is 100 μm or more. The steel sheet is a high-strength cold-rolled steel sheet which has a sufficiently minimized rate of bending fracture starting from inclusions and thereby has excellent bending workability.
摘要:
A cold-rolled steel sheet has a chemical composition of C: 0.12% to 0.3%, Si: 0.5% or less, Mn: less than 1.5%, Al: 0.15% or less, N: 0.01% or less, P: 0.02% or less, and S: 0.01% or less, with the remainder including iron and inevitable impurities and has a martensite single-phase structure as its steel microstructure. In a surface region of the steel sheet from the surface to a depth one-tenth the gauge, the number density of n-ary groups of inclusions determined by specific n-th determinations is 120 or less per 100 cm2 of a rolling plane, where the distance in steel sheet rolling direction between outermost surfaces of two outermost particles of the group of inclusions is 100 μm or more. The steel sheet is a high-strength cold-rolled steel sheet which has a sufficiently minimized rate of bending fracture starting from inclusions and thereby has excellent bending workability.
摘要:
The invention relates to a steel sheet having a tensile strength of 1180 MPa or more, which excels in workability and cold brittleness resistance. The high-strength steel sheet contains 0.10% to 0.30% of C, 1.40% to 3.0% of Si, 0.5% to 3.0% of Mn, 0.1% or less of P, 0.05% or less of S, 0.005% to 0.20% of Al, 0.01% or less of N, 0.01% or less of O, as well as Fe and inevitable impurities. The steel sheet has: (i) a ferrite volume fraction of 5% to 35% and a bainitic ferrite and/or tempered martensite volume fraction of 60% or more; (ii) a MA constituent volume fraction of 6% or less (excluding 0%); and (iii) a retained austenite volume fraction of 5% or more.
摘要:
The invention relates to a steel sheet having a tensile strength of 1180 MPa or more, which excels in workability and cold brittleness resistance. The high-strength steel sheet contains 0.10% to 0.30% of C, 1.40% to 3.0% of Si, 0.5% to 3.0% of Mn, 0.1% or less of P, 0.05% or less of S, 0.005% to 0.20% of Al, 0.01% or less of N, 0.01% or less of O, as well as Fe and inevitable impurities. The steel sheet has: (i) a ferrite volume fraction of 5% to 35% and a bainitic ferrite and/or tempered martensite volume fraction of 60% or more; (ii) a MA constituent volume fraction of 6% or less (excluding 0%); and (iii) a retained austenite volume fraction of 5% or more.
摘要:
Disclosed is an ultra high strength steel plate with at least 1100 MPa of tensile strength that has both an excellent strength-stretch balance and excellent bending workability, and a method for producing the same. The metal structure of the steel plate has martensite, and the soft phases of bainitic ferrite and polygonal ferrite. The area of the aforementioned martensite constitutes 50% or more, the area of the aforementioned bainitic ferrite constitutes 15% or more, and the area of the aforementioned polygonal ferrite constitutes 5% or less (including 0%). When the circle-equivalent diameter of the aforementioned soft phases is measured, the coefficient of variation (standard deviation/mean value) is less or equal to 1.0. The ultra high strength steel plate has at least 1100 MPa of tensile strength.
摘要:
Disclosed is an ultra high strength steel plate with at least 1100 MPa of tensile strength that has both an excellent strength-stretch balance and excellent bending workability, and a method for producing the same. The metal structure of the steel plate has martensite, and the soft phases of bainitic ferrite and polygonal ferrite. The area of the aforementioned martensite constitutes 50% or more, the area of the aforementioned bainitic ferrite constitutes 15% or more, and the area of the aforementioned polygonal ferrite constitutes 5% or less (including 0%). When the circle-equivalent diameter of the aforementioned soft phases is measured, the coefficient of variation (standard deviation/mean value) is less or equal to 1.0. The ultra high strength steel plate has at least 1100 MPa of tensile strength.
摘要:
Disclosed is a hot-dip galvanized steel sheet, in which a steel sheet of the hot-dip galvanized steel sheet before galvanization contains, on the percent by mass basis, 0.06% to 0.15% carbon (C); 1% to 3% manganese (Mn); 0.01% to 0.05% phosphorus (P); 0.03% to 1% chromium (Cr); 0.03% to 1% molybdenum (Mo); and 0.02% to 0.15% aluminum (Al). The steel sheet before galvanization has a silicon (Si) content of 0.2% or less (inclusive of 0%) and a sulfur (S) content of 0.03% or less (inclusive of 0%) and has a K value of −2.0 or more, in which the K value is calculated according to following Equation (1): K value=3×[Mo]−5×[Cr] (1) wherein “[Element]” represents the content (percent by mass) of the element.
摘要:
A high-strength hot-dip galvanized steel sheet is provided which comprises a composite structure consisting essentially of ferrite and martensite. The steel comprises, by mass %, C: 0.05 to 0.12%, Si: not more than 0.05%, Mn: 2.7 to 3.5%, Cr: 0.2 to 0.5%, Mo: 0.2 to 0.5%, Al: not more than 0.10%, P: not more than 0.03%, and S: not more than 0.03%. The high-strength hot-dip galvanized steel sheet has not only excellent spot weldability, but also excellent “stability of material properties”, including tensile strength, total elongation, and yield strength, in a high range of strengths from 780 to 1180 MPa, even if the manufacturing condition (especially, the condition of the cooling process after annealing the steel sheet) is changed.