公开(公告)号：US4057525A

公开(公告)日：1977-11-08

申请号：US667141

申请日：1976-03-15

申请人： Kiyoshi Kikuchi ,  Takeo Okano ,  Yukio Terakawa ,  Akira Nishihara

发明人： Kiyoshi Kikuchi ,  Takeo Okano ,  Yukio Terakawa ,  Akira Nishihara

IPC分类号： C01B33/145 ,  C04B28/24 ,  C09D5/18 ,  C08L61/28

CPC分类号： C04B28/24 ,  C01B33/145 ,  C09D5/18 ,  C04B2111/00482 ,  Y10T428/31862 ,  Y10T428/31942 ,  Y10T428/31957

摘要： A novel stable silica sol which does not gel even at low temperatures is prepared by adding a di -or polyhydric alcohol having three or more carbon atoms and a water-soluble melamine resin to a silica sol. A novel water-based coating composition which requires only an applying step, not a baking step nor a drying step, in the use is prepared by adding an aggregate or filler and usual additives for coating material to the aforesaid stable silica sol as binder. By adding further a small amount of a synthetic resin emulsion to said binder, an inorganic coating composition containing a smaller amount of organic materials than that in prior products can be obtained. The coating therefrom is excellent in strength and its fire resistance is not lowered.

摘要翻译： 通过向硅溶胶中加入碳原子数为3以上的二元多元醇和水溶性三聚氰胺树脂，制备即使在低温下也不凝胶化的新型稳定的硅溶胶。 通过向上述稳定的二氧化硅溶胶中添加聚集体或填料和常用的涂料添加剂作为粘合剂，制备了仅需要施加步骤，而不是烘烤步骤和干燥步骤的新型水性涂料组合物。 通过进一步向所述粘合剂中加入少量合成树脂乳液，可以获得含有比现有产品少的有机材料的无机涂料组合物。 其涂层强度优异，耐火性不降低。

公开(公告)号：US4189414A

公开(公告)日：1980-02-19

申请号：US951033

申请日：1978-10-13

申请人： Kiyoshi Kikuchi ,  Takeo Okano ,  Yukio Terakawa ,  Akira Nishihara ,  Koji Kono

发明人： Kiyoshi Kikuchi ,  Takeo Okano ,  Yukio Terakawa ,  Akira Nishihara ,  Koji Kono

IPC分类号： E04F13/02 ,  C09D1/00 ,  C09D1/04 ,  C09D5/00 ,  C09D163/00 ,  B05D3/02 ,  C08L61/20

CPC分类号： C09D163/00 ,  C08K3/34 ,  Y10T428/31511 ,  Y10T428/31525 ,  Y10T428/31942

摘要： Novel coating compositions for architectural use are provided, which include a quaternary ammonium silicate having a silica content of 10 to 60% by weight and a liquid epoxide resin, besides the conventional ingredients, such as pigments, fillers, aggregates and water, and which are particularly capable of producing films having excellent adherency to mortar or concrete surfaces. If a stabilized silica sol is added to the compositions, films produced therefrom have much improved resistance to water at low temperatures as well as freeze-thaw stability.

摘要翻译： 提供了用于建筑用途的新型涂料组合物，其包括二氧化硅含量为10至60重量％的季铵硅酸盐和液体环氧树脂，以及常规成分如颜料，填料，聚集体和水，并且它们是 特别是能够生产与砂浆或混凝土表面具有优异粘合性的膜。 如果将稳定的二氧化硅溶胶加入到组合物中，则由其制备的膜在低温下具有大大提高的耐水性以及冻融稳定性。

公开(公告)号：US4134956A

公开(公告)日：1979-01-16

申请号：US539442

申请日：1975-01-08

申请人： Yoshinori Suzuki ,  Akihiko Asayama ,  Fumio Dohi ,  Takaharu Takahashi ,  Isao Toyomoto

发明人： Yoshinori Suzuki ,  Akihiko Asayama ,  Fumio Dohi ,  Takaharu Takahashi ,  Isao Toyomoto

IPC分类号： B32B13/04 ,  C04B28/04 ,  C04B41/50 ,  C04B41/52 ,  C04B41/65 ,  C04B41/70 ,  C09D1/06 ,  B28B1/16

CPC分类号： C04B41/009 ,  C04B28/04 ,  C04B41/5079 ,  C04B41/52 ,  C04B41/65 ,  C04B41/70 ,  C04B2111/00482 ,  Y10S264/57

摘要： A decorative coating layer, unified with the succulent and fragile surface of a concrete board, is formed by a method comprising laminating an inorganic and hydraulic coating material on the surface of an unhardened concrete board placed in a mold, and immediately thereafter heat-curing the thus coated concrete board. According to this method, beautifully dressed precast concrete boards can be mass-produced by a shortened process with improved efficiency of operation.

摘要翻译： 通过以下方法形成与混凝土板的多汁且脆弱的表面一体的装饰涂层，该方法包括将无机和液压涂料层压在放置在模具中的未硬化混凝土板的表面上，然后立即热固化 从而涂层混凝土板。 根据该方法，通过缩短工艺可以大幅度地生产精美的预制混凝土板，提高了操作效率。