The invention belongs to the technical field of steel refining, and in particular, relates to a method for eliminating edge warp defects of hot-continuous-rolled strip steel and the strip steel produced by the method. Continuous-cast blanks are put in a stepper heating furnace for heating, and are insulated by 50-80 min at 1220-1270 DEG C; the cast blanks are discharged from the furnace for descaling by adopting a descaling box, and are rolled in a rough rolling machine at a rolling temperature of 1100-1150 DEG C by 5-7 gates; rough rolling descaling water is not fed in the previous two gates,so that higher temperatures of intermediate blanks are reached, and the temperatures of the intermediate blanks in the whole rough rolling phase are located in a plastifying area; after the second gate of rough rolling, the rough rolling descaling water is totally fed in to eliminate scales on the surfaces of the intermediate blanks; then, the intermediate blanks are fed in a fine rolling unit for rolling, and the final rolling temperature is 850-930 DEG C; the winding is performed after lamellar cooling at a winding temperature of 500-750 DEG C; and the hot-continuous-rolled strip steel withno or fewer warp defects is finally produced.