公开(公告)号：EP2468699A1

公开(公告)日：2012-06-27

申请号：EP10810039.7

申请日：2010-08-20

申请人： Noritake Co., Limited

发明人： ITO, Yoshihisa ,  YAMADA, Yoshihisa ,  INADA, Hiroshi ,  BAN, Kiyoko

IPC分类号： C04B35/48

CPC分类号： C04B35/486 ,  C04B35/632 ,  C04B35/6455 ,  C04B2235/32 ,  C04B2235/3206 ,  C04B2235/3208 ,  C04B2235/3217 ,  C04B2235/3225 ,  C04B2235/3294 ,  C04B2235/3298 ,  C04B2235/3418 ,  C04B2235/42 ,  C04B2235/447 ,  C04B2235/656 ,  C04B2235/6567 ,  C04B2235/72 ,  C04B2235/727 ,  C04B2235/76 ,  C04B2235/765 ,  C04B2235/96 ,  C04B2235/9684

摘要： Provided is a high-strength zirconia sintered body in which the progression of low-temperature degradation is inhibited. The zirconia sintered body contains partially-stabilized zirconia as a matrix phase and contains at least one element from among phosphorus (P), arsenic (As), antimony (Sb), and bismuth (Bi). The content of the abovementioned element(s) in the zirconia sintered body ranges from 4×10 -4 mol to 4×10 -2 mol with respect to 1 mol of zirconium(IV) oxide. Preferably, the zirconia sintered body further contains 0.03% to 3% by mass of silicon dioxide.

摘要翻译： 本发明提供一种高强度的氧化锆烧结体，其低温劣化的进展被抑制。 氧化锆烧结体含有部分稳定的氧化锆作为基体相和包含磷中的至少一种元素（P），砷（As），锑（Sb）和铋（Bi）。 在氧化锆烧结体的上述元件（一个或多个）的含量为4×10 -4摩尔，以4×10 -2摩尔，相对于1个摩尔锆（IV）氧化物的。 优选地，氧化锆烧结体含有0.03重量％至进一步至3％二氧化硅的质量。