公开(公告)号：US07563431B2

公开(公告)日：2009-07-21

申请号：US10488441

申请日：2002-06-24

申请人： Armin Olbrich ,  Juliane Meese-Marktscheffel ,  Viktor Stoller ,  Michael Erb ,  Sven Albrecht ,  Gerhard Gille ,  Gerd Maikowske ,  Frank Schrumpf ,  Josef Schmoll ,  Matthias Jahn

发明人： Armin Olbrich ,  Juliane Meese-Marktscheffel ,  Viktor Stoller ,  Michael Erb ,  Sven Albrecht ,  Gerhard Gille ,  Gerd Maikowske ,  Frank Schrumpf ,  Josef Schmoll ,  Matthias Jahn

IPC分类号： C01B13/00

CPC分类号： H01M4/366 ,  C01G53/04 ,  C01P2002/60 ,  C01P2004/61 ,  C01P2006/20 ,  C01P2006/40 ,  C01P2006/60 ,  H01M4/32 ,  H01M4/52 ,  H01M10/345

摘要： A process for preparing nickel hydroxide by alkaline precipitation from nickel salt solutions in the presence of complexing agents, in which the precipitation is carried out at at least two different locations in the same mother liquor with different precipitation kinetics at the different locations and the mother liquor is mixed prior to agglomeration of the precipitated primary crystals, is described.

摘要翻译： 一种在络合剂存在下，由镍盐溶液碱沉淀制备氢氧化镍的方法，其中沉淀是在不同位置的不同沉淀动力学的同一母液中的至少两个不同位置进行的，母液 在沉淀的一次晶体凝聚之前进行混合。

公开(公告)号：US06875416B1

公开(公告)日：2005-04-05

申请号：US09601946

申请日：1998-08-13

申请人： Mathias Benz ,  Wolfgang Kummer ,  Evelyn Pross ,  Josef Schmoll ,  Wolfgang Schweda ,  Daniel Duff ,  Ricarda Leiberich ,  Christoph Schild ,  Ulrich Krynitz ,  Juliane Meese-Marktscheffel ,  Viktor Stoller

发明人： Mathias Benz ,  Wolfgang Kummer ,  Evelyn Pross ,  Josef Schmoll ,  Wolfgang Schweda ,  Daniel Duff ,  Ricarda Leiberich ,  Christoph Schild ,  Ulrich Krynitz ,  Juliane Meese-Marktscheffel ,  Viktor Stoller

IPC分类号： C01G53/00 ,  H01M4/48 ,  H01M4/485 ,  H01M4/50 ,  H01M4/505 ,  H01M4/52 ,  H01M4/525 ,  H01M10/0525 ,  H01M10/36 ,  C01D1/02 ,  C01F7/04 ,  C01G37/02 ,  C01G45/02

CPC分类号： C01G45/1228 ,  C01G51/42 ,  C01G51/44 ,  C01G53/42 ,  C01G53/44 ,  C01G53/50 ,  C01P2002/52 ,  C01P2002/74 ,  C01P2004/50 ,  C01P2004/61 ,  C01P2006/12 ,  H01M4/485 ,  H01M4/505 ,  H01M4/525 ,  H01M10/0525

摘要： The invention relates to a method for producing lithium-transition metal mixtures of general formula Lix(M1yM21-y)nOnz, wherein M1 represents nickel, cobalt or manganese, M2 represents chromium, cobalt, iron, manganese, molybdenum or aluminium, and is different from M1, n is 2 if M1 represents manganese and is 1 otherwise, x is comprised between 0.9 and 1.2, y is comprised between 0.5 and 1.0 and z is comprised between 1.9 and 2.1. According to the inventive method, an intimate mixture composed of transition metal compounds containing oxygen and of a lithium compound containing oxygen is calcinated, said mixture being obtained by processing a solid powder transition metal compound with a solution of said lithium compound, and then drying. At least the M1 compound is used in powder form having a specific surface of at least 20 m2/g (BET) and calcination is carried out in a fluidised bed.

摘要翻译： 本发明涉及一种制备通式为Lix（M 1 yM 2-y）n O n z的锂 - 过渡金属混合物的方法，其中M 1表示镍，钴或锰，M 2表示铬 ，钴，铁，锰，钼或铝，并且不同于M 1，如果M 1表示锰，则n为2，否则为1，x为0.9至1.2，y为0.5至1.0 z在1.9和2.1之间。 根据本发明的方法，煅烧由含有氧的过渡金属化合物和含氧化合物的锂化合物组成的紧密混合物，所述混合物通过用所述锂化合物的溶液处理固体粉末过渡金属化合物，然后干燥而获得。 至少M 1化合物以比表面积至少为20m 2 / g（BET）的粉末形式使用，并且在流化床中进行煅烧。

公开(公告)号：US5665127A

公开(公告)日：1997-09-09

申请号：US590629

申请日：1996-01-24

申请人： Paul Moltgen ,  Pirmin Wilhelm ,  Josef Schmoll

发明人： Paul Moltgen ,  Pirmin Wilhelm ,  Josef Schmoll

IPC分类号： B23B27/14 ,  B24D3/00 ,  C04B35/10 ,  C04B35/111 ,  C04B35/64 ,  C09K3/14

CPC分类号： C04B35/64 ,  C04B35/1115 ,  C09K3/1418

摘要： Microcrystalline bodies based on .alpha.-Al.sub.2 O.sub.3 are made by drying sub-micron powders, press compacting and shock sintering at an intermediate sinter temperature range of 1,300.degree. to 1,550.degree. C., i.e. bringing the compact up to such range in under 60 seconds, preferably under 10.

摘要翻译： 基于α-Al2O3的微晶体通过在1300℃至1550℃的中间烧结温度范围内干燥亚微米粉末，压制和冲击烧结来制备，即将压块在60秒以下，优选为 10岁以下。