    Rubber composition containing carbon black
    22.
    发明授权
    Rubber composition containing carbon black 失效
    含有炭黑的橡胶组合物

    公开(公告)号：US5962575A

    公开(公告)日：1999-10-05

    申请号：US973240

    申请日：1997-12-03

    申请人： Fumito Yatsuyanagi ,  Hiroyuki Kaido ,  Tetsuji Kawazura

    发明人： Fumito Yatsuyanagi ,  Hiroyuki Kaido ,  Tetsuji Kawazura

    IPC分类号： B60C1/00 ,  C08K3/04 ,  C08K3/00

    CPC分类号： C08K3/04 ,  B60C1/00 ,  B60C1/0016

    摘要： A carbon-containing rubber composition containing a rubber composition containing carbon black, obtained by coagulating, dehydrating, and drying a rubber latex mixture containing a latex of at least one starting rubber A having an average glass transition temperature TgA of -120.degree. C. to -15.degree. C., carbon black, and part of a softening agent, mixed in an internal mixer with a starting rubber B and part of the softening agent, with a ratio F.sub.A /F.sub.B of the concentration F.sub.A of carbon black in the copolymer in the rubber latex mixture with the concentration F.sub.B of carbon black in the copolymer after kneading by the hermetic mixture being 1.2 to 3.0 and a rubber composition containing carbon black comprising a starting rubber A' comprising a polymer having functional groups represented by formula (I)--C.dbd.N'-- (I)bonded with a polymer chain directly or through another atomic group or a terminal modified diene-based polymer first brought into contact with carbon black, then blended with a starting rubber B' comprising a diene based stock rubber.

    摘要翻译： PCT No.PCT / JP97 / 01051 Sec。 371日期1997年12月3日第 102（e）日期1997年12月3日PCT 1997年3月27日PCT公布。 第WO97 / 38047号公报 日期1997年10月16日含有含有炭黑的橡胶组合物的含碳橡胶组合物，其通过凝固，脱水和干燥含有平均玻璃化转变温度TgA为至少一种起始橡胶A的胶乳的橡胶胶乳混合物而获得， 120℃〜-15℃，炭黑和部分软化剂，在内部混合器中与起始橡胶B和部分软化剂混合，比例FA / FB为碳浓度FA 通过密封混合物捏合后共聚物中的炭黑的浓度FB在橡胶胶乳混合物中的黑色黑色，并且含有炭黑的橡胶组合物包含含有由 式（I）-C = N' - （I）直接或通过另一原子团或末端改性二烯基聚合物与聚合物链键合，首先与炭黑接触，然后混合 用包含二烯基原料橡胶的起始橡胶B'。

    Rubber composition and process for producing thereof
    23.
    发明授权
    Rubber composition and process for producing thereof 失效
    橡胶组合物及其制造方法

    公开(公告)号：US5834552A

    公开(公告)日：1998-11-10

    申请号：US932302

    申请日：1997-09-17

    申请人： Tetsuji Kawazura ,  Hiroyuki Kaido

    发明人： Tetsuji Kawazura ,  Hiroyuki Kaido

    IPC分类号： B06B1/06 ,  B60C1/00 ,  C08J3/22 ,  C08L21/00 ,  G01V1/18 ,  C08J31/04

    CPC分类号： C08J3/226 ,  B60C1/0016 ,  C08L21/00 ,  C08J2321/00 ,  C08J2421/00

    摘要： A process for producing a rubber composition comprising (i) a total amount of 100 parts by weight of starting rubbers (A) and (B), including 30 to 90 parts by weight of the starting rubber (A) having a glass transition temperature (Tg) of -40.degree. to 10.degree. C. and 10 to 40 parts by weight of the starting rubber (B) which is viscoelastically incompatible with the starting rubber (A) and has a Tg of at least 20.degree. C. lower than the Tg of the starting rubber (A) and (ii) 60 to 100 parts by weight of a reinforcing agent, wherein the starting rubber (A) and at least 80% by weight of the total weight of the reinforcing agent are mixed in a hermetic type mixer at 130.degree. C. to 200.degree. C. for at least 10 seconds, then the starting rubber (B) and the remaining reinforcing agent are added and mixed.

    摘要翻译： 一种橡胶组合物的制造方法，其特征在于，含有（i）100重量份的起始橡胶（A）和（B）的总量，包括30〜90重量份的具有玻璃化转变温度的起始橡胶（A） Tg）为-40〜10℃，和10〜40重量份与起始橡胶（A）粘弹性不相容的起始橡胶（B），并且Tg比所述起始橡胶（A）低至少20℃ 起始橡胶（A）的Tg和（ii）60〜100重量份的增强剂，其中起始橡胶（A）和至少80重量％的增强剂的总重量混合在密封 在130℃至200℃下搅拌至少10秒钟，然后加入起始橡胶（B）和剩余的增强剂并混合。