摘要:
A high performance TMR sensor is fabricated by incorporating a tunnel barrier having a Mg/MgO/Mg configuration. The 4 to 14 Angstroms thick lower Mg layer and 2 to 8 Angstroms thick upper Mg layer are deposited by a DC sputtering method while the MgO layer is formed by a NOX process involving oxygen pressure from 0.1 mTorr to 1 Torr for 15 to 300 seconds. NOX time and pressure may be varied to achieve a MR ratio of at least 34% and a RA value of 2.1 ohm-um2. The NOX process provides a more uniform MgO layer than sputtering methods. The second Mg layer is employed to prevent oxidation of an adjacent ferromagnetic layer. In a bottom spin valve configuration, a Ta/Ru seed layer, IrMn AFM layer, CoFe/Ru/CoFeB pinned layer, Mg/MgO/Mg barrier, CoFe/NiFe free layer, and a cap layer are sequentially formed on a bottom shield in a read head.
摘要:
A high performance TMR sensor is fabricated by employing a free layer with a trilayer configurations represented by FeCo/CoFeB/CoB, FeCo/CoB/CoFeB, FeCo/CoFe/CoB, or FeCo/FeB/CoB may also be employed. Alternatively, CoNiFeB or CoNiFeBM formed by co-sputtering CoB with CoNiFe or CoNiFeM, respectively, where M is V, Ti, Zr, Nb, Hf, Ta, or Mo may be included in a composite free layer or as a single free layer in the case of CoNiFeBM. A 15 to 30% in improvement in TMR ratio over a conventional CoFe/NiFe free layer is achieved while maintaining low Hc and RA
摘要:
An insertion layer is provided between an AFM layer and an AP2 pinned layer in a GMR or TMR element to improve exchange coupling properties by increasing Hex and the Hex/Hc ratio without degrading the MR ratio. The insertion layer may be a 1 to 15 Angstrom thick amorphous magnetic layer comprised of at least one element of Co, Fe, or Ni, and at least one element having an amorphous character selected from B, Zr, Hf, Nb, Ta, Si, or P, or a 1 to 5 Angstrom thick non-magnetic layer comprised of Cu, Ru, Mn, Hf, or Cr. Preferably, the content of the one or more amorphous elements in the amorphous magnetic layer is less than 40 atomic %. Optionally, the insertion layer may be formed within the AP2 pinned layer. Examples of an insertion layer are CoFeB, CoFeZr, CoFeNb, CoFeHf, CoFeNiZr, CoFeNiHf, and CoFeNiNbZr.
摘要:
A high performance TMR sensor is fabricated by incorporating a tunnel barrier having a Mg/MgO/Mg configuration. The 4 to 14 Angstroms thick lower Mg layer and 2 to 8 Angstroms thick upper Mg layer are deposited by a DC sputtering method while the MgO layer is formed by a NOX process involving oxygen pressure from 0.1 mTorr to 1 Torr for 15 to 300 seconds. NOX time and pressure may be varied to achieve a MR ratio of at least 34% and a RA value of 2.1 ohm-um2. The NOX process provides a more uniform MgO layer than sputtering methods. The second Mg layer is employed to prevent oxidation of an adjacent ferromagnetic layer. In a bottom spin valve configuration, a Ta/Ru seed layer, IrMn AFM layer, CoFe/Ru/CoFeB pinned layer, Mg/MgO/Mg barrier, CoFe/NiFe free layer, and a cap layer are sequentially formed on a bottom shield in a read head.
摘要:
A composite free layer having a FL1/insertion/FL2 configuration where a top surface of FL1 is treated with a weak plasma etch is disclosed for achieving enhanced dR/R while maintaining low RA, and low λ in TMR or GMR sensors. The weak plasma etch removes less than about 0.2 Angstroms of FL1 and is believed to modify surface structure and possibly increase surface energy. FL1 may be CoFe, CoFe/CoFeB, or alloys thereof with Ni, Ta, Mn, Ti, W, Zr, Hf, Tb, or Nb having a (+) λ value. FL2 may be CoFe, NiFe, or alloys thereof having a (−) λ value. The thin insertion layer includes at least one magnetic element such as Co, Fe, and Ni, and at least one non-magnetic element selected from Ta, Ti, W, Zr, Hf, Nb, Mo, V, Cr, or B. When CoFeBTa is selected as insertion layer, the CoFeB:Ta ratio is from 1:1 to 4:1.
摘要:
A composite seed layer that reduces the shield to shield distance in a read head while improving Hex (exchange coupling field) and Hex/Hc (Hc=coercivity) is disclosed and has a SM/A/SM/B configuration in which the SM layers are soft magnetic layers, the A (amorphous) layer is made of at least one of Co, Fe, Ni, and includes one or more amorphous elements, and the B layer is a buffer layer that contacts the AFM (anti-ferromagnetic) layer in the spin valve. The SM/A/SM stack together with the S1 (bottom) shield forms an effective shield such that the buffer layer serves as the effective seed layer while maintaining a blocking temperature of 260° C. in the AFM layer. The lower SM layer may be omitted. Examples of the amorphous layer are CoFeB, CoFeZr, CoFeNb, CoFeHf, CoFeNiZr, CoFeNiHf, and CoFeNiNbZr while the buffer layer may be Cu, Ru, Cr, Al, or NiFeCr.
摘要翻译:公开了一种复合种子层,其在改进Hex(交换耦合场)和Hex / Hc(Hc =矫顽力)的同时减小了读头中的屏蔽距离,并具有SM / A / SM / B配置,其中SM层 是软磁性层,A(非晶)层由Co,Fe,Ni中的至少一种构成,并且包括一个或多个非晶元素,并且B层是与AFM(反铁磁)层接触的缓冲层 在自旋阀中。 SM / A / SM堆叠与S1(底部)屏蔽件形成有效屏蔽,使得缓冲层用作有效种子层,同时在AFM层中保持260℃的阻挡温度。 可以省略下层SM层。 非晶层的实例是CoFeB,CoFeZr,CoFeNb,CoFeHf,CoFeNiZr,CoFeNiHf和CoFeNiNbZr,而缓冲层可以是Cu,Ru,Cr,Al或NiFeCr。
摘要:
A composite free layer having a FL1/insertion/FL2 configuration is disclosed for achieving high dR/R, low RA, and low λ in TMR or GMR sensors. Ferromagnetic FL1 and FL2 layers have (+) λ and (−) λ values, respectively. FL1 may be CoFe, CoFeB, or alloys thereof with Ni, Ta, Mn, Ti, W, Zr, Hf, Tb, or Nb. FL2 may be CoFe, NiFe, or alloys thereof with Ni, Ta, Mn, Ti, W, Zr, Hf, Tb, Nb, or B. The thin insertion layer includes at least one magnetic element such as Co, Fe, and Ni, and at least one non-magnetic element selected from Ta, Ti, W, Zr, Hf, Nb, Mo, V, Cr, or B. In a TMR stack with a MgO tunnel barrier, dR/R>60%, λ˜1×10−6, and RA=1.2 ohm-um2 when FL1 is CoFe/CoFeB/CoFe, FL2 is CoFe/NiFe/CoFe, and the insertion layer is CoTa or CoFeBTa.
摘要:
An insertion layer is provided between an AFM layer and an AP2 pinned layer in a GMR or TMR element to improve exchange coupling properties by increasing Hex and the Hex/Hc ratio without degrading the MR ratio. The insertion layer may be a 1 to 15 Angstrom thick amorphous magnetic layer comprised of at least one element of Co, Fe, or Ni, and at least one element having an amorphous character selected from B, Zr, Hf, Nb, Ta, Si, or P, or a 1 to 5 Angstrom thick non-magnetic layer comprised of Cu, Ru, Mn, Hf, or Cr. Preferably, the content of the one or more amorphous elements in the amorphous magnetic layer is less than 40 atomic %. Optionally, the insertion layer may be formed within the AP2 pinned layer. Examples of an insertion layer are CoFeB, CoFeZr, CoFeNb, CoFeHf, CoFeNiZr, CoFeNiHf, and CoFeNiNbZr.
摘要:
A composite free layer having a FL1/insertion/FL2 configuration where a top surface of FL1 is treated with a weak plasma etch is disclosed for achieving enhanced dR/R while maintaining low RA, and low λ in TMR or GMR sensors. The weak plasma etch removes less than about 0.2 Angstroms of FL1 and is believed to modify surface structure and possibly increase surface energy. FL1 may be CoFe, CoFe/CoFeB, or alloys thereof with Ni, Ta, Mn, Ti, W, Zr, Hf, Tb, or Nb having a (+) λ value. FL2 may be CoFe, NiFe, or alloys thereof having a (−) λ value. The thin insertion layer includes at least one magnetic element such as Co, Fe, and Ni, and at least one non-magnetic element selected from Ta, Ti, W, Zr, Hf, Nb, Mo, V, Cr, or B. When CoFeBTa is selected as insertion layer, the CoFeB:Ta ratio is from 1:1 to 4:1.
摘要:
A high performance TMR element is fabricated by inserting an oxygen surfactant layer (OSL) between a pinned layer and AlOx tunnel barrier layer in a bottom spin valve configuration. The pinned layer preferably has a SyAP configuration with an outer pinned layer, a Ru coupling layer, and an inner pinned layer comprised of CoFeXBY/CoFeZ wherein x=0 to 70 atomic %, y=0 to 30 atomic %, and z=0 to 100 atomic %. The OSL is formed by treating the CoFeZ layer with oxygen plasma. The AlOx tunnel barrier has improved uniformity of about 2% across a 6 inch wafer and can be formed from an Al layer as thin as 5 Angstroms. As a result, the Hin value can be decreased by ⅓ to about 32 Oe. A dR/R of 25% and a RA of 3 ohm-cm2 have been achieved for TMR read head applications.