公开(公告)号：US20070066772A1

公开(公告)日：2007-03-22

申请号：US10553229

申请日：2004-04-14

申请人： Klaus Foettinger ,  Martin Schneider

发明人： Klaus Foettinger ,  Martin Schneider

IPC分类号： C08F4/44 ,  B01J31/00

CPC分类号： C08F110/02 ,  B01J21/08 ,  B01J27/135 ,  B01J31/0201 ,  B01J31/0211 ,  B01J31/0228 ,  B01J31/0231 ,  B01J31/0254 ,  B01J31/0272 ,  B01J31/122 ,  B01J31/128 ,  B01J31/143 ,  B01J31/38 ,  C08F10/00 ,  C08F210/16 ,  C08F4/6546 ,  C08F4/651 ,  C08F4/025 ,  C08F210/08 ,  C08F2500/17 ,  C08F2500/18 ,  C08F4/6565

摘要： The present invention relates to catalyst systems of the Ziegler-Natta type, to a process for preparing them, to their use for the polymerization of olefins and to ethylene copolymers which can be prepared using this catalyst system.

摘要翻译： 本发明涉及齐格勒 - 纳塔型催化剂体系，其制备方法，其用于烯烃聚合和乙烯共聚物的用途，该共聚物可使用该催化剂体系制备。

公开(公告)号：US20100144988A1

公开(公告)日：2010-06-10

申请号：US12449082

申请日：2008-01-15

申请人： Klaus Foettinger ,  Manfred Hecker ,  Lothar Berger ,  Rainer Karer ,  Dieter Lilge

发明人： Klaus Foettinger ,  Manfred Hecker ,  Lothar Berger ,  Rainer Karer ,  Dieter Lilge

IPC分类号： C08F210/02 ,  C08F4/22

CPC分类号： C08F210/16 ,  C08F2/34 ,  C08F4/24 ,  C08F10/14 ,  C08F2500/12 ,  C08F2500/04 ,  C08F2500/11

摘要： Monomodal copolymers of ethylene and molding compositions comprising such copolymers, wherein the copolymers have a density determined according to DIN EN ISO 1183-1, variant A in the range from 0.938 to 0.944 g/cm3, a melt index MFR21 determined according to ISO 1133 at 190° C. under a load of 21.6 kg in the range from 12 to 17 g/10 min, a weight average molar mass Mw, in the range from 140 000 g/mol to 330 000 g/mol, a polydispersity Mw/Mn in the range from 9 to 17, and a content of comonomer side chains per 1000 carbon atoms C x equal to or above a value defined via equation (I) Cx=128.7−134.62×d′, wherein d′ is the numerical value of the density of the copolymer in g/cm3, the use of the copolymers for producing injection-molded articles, as well as injection-molded articles comprising the copolymers, and process for the preparation of such monomodal copolymers.

摘要翻译： 乙烯的单共聚物和包含这种共聚物的模塑组合物，其中共聚物具有根据DIN EN ISO 1183-1，变体A在0.938至0.944g / cm 3范围内测定的密度，根据ISO 1133测定的熔体指数MFR 21 190℃，21.6kg，12-17g / 10min范围内的重均摩尔质量Mw，140,000g / mol〜330000g / mol，多分散性Mw / Mn 在9至17的范围内，每1000个碳原子的共聚单体侧链的含量C x等于或高于通过式（I）定义的值Cx = 128.7-134.62×d'，其中d'是 共聚物的密度（g / cm 3），用于制备注射成型制品的共聚物的使用，以及包含共聚物的注模制品以及制备这种单峰共聚物的方法。