摘要:
In one embodiment, a magnetic recording medium comprises an underlying film, a magnetic film and a protective film formed in this order on a substrate. The magnetic film is a cobalt-base alloy film containing chromium and has a plurality of magnetic layers stacked without interposition of any non-magnetic layer. The plural magnetic layers comprise first, second and third magnetic layers. The first magnetic layer is disposed between the underlying film and the second magnetic layer. The second magnetic layer is disposed between the first magnetic layer and the third magnetic layer. The third magnetic layer is disposed between the second magnetic layer and the protective film. The concentration of chromium contained in the first magnetic layer is lower than that of chromium contained in the second magnetic layer. The thickness of the first magnetic layer is smaller than that of the second magnetic layer. The magnetic layers which overlie the first magnetic layer further contain platinum and boron. The concentration of chromium contained in the third magnetic layer is lower than that of chromium contained in the second magnetic layer.
摘要:
A magnetic-recording-disk test-head. The magnetic-recording-disk test-head includes a slider, a test pad and a slider-surface-shape control mechanism. The slider includes a leading edge and a trailing edge. The test pad is disposed at a trailing-edge side of the slider and is configured to remove and to detect asperities on a magnetic-recording disk. The slider-surface-shape control mechanism is configured to change a shape of an air-bearing surface of the slider and is disposed at a leading-edge side of the slider.
摘要:
To avoid the occurrence of a recording error by suppressing the influence that a magneto-static interaction acting between the pattern dots exerts on a recording process and expand a margin for recording synchronization timing lag or tracking misregistration on the pattern dot. Each pattern dot has a structure in which a plurality of parts having different magnetization reversal fields are bonded with exchange interaction in the in-plane direction of a medium, substrate. The positional relationship between the parts having different magnetization reversal fields is substantially coincident between the adjacent pattern dots, which are arranged to have a gradient of magnetization reversal field in a track direction or track transverse direction. Further, the recording is performed by adapting a gradient of recording magnetic field to the gradient of magnetization reversal field. Other methods and systems are described as well.