摘要:
A method of improving the oxidation and corrosion resistance of a superalloy article comprises providing a superalloy substrate having a sulphur content which is less than 0.8 ppm by weight, and depositing on the substrate a protective antioxidation coating having a sulphur content also less than 0.8 ppm by weight. A heat barrier layer may also be provided by depositing on the protective anti-oxidation coating a ceramic coating of columnar structure.
摘要:
A low thermal conductivity heat barrier coating deposited on a superalloy substrate is characterised in that it comprises a homogeneous mixture of oxides and has a composition containing a zirconia base, a zirconia-stabilizing oxide, and from 0.5 to 12 weight % of an additional metal element selected from nickel, cobalt, iron and mixtures thereof. The additional metal element may be added in an oxidised form, and the coating may also contain from 0.01 to 1 weight % of carbon.
摘要:
A ceramic heat barrier coating is deposited on a substrate so that the coating has a columnar growth pattern which is interrupted and repeated a number of times throughout its thickness by successive regermination of the ceramic deposit. The regermination is obtained by a vapour phase deposition process wherein a polluting gas is introduced intermittently during the deposition of the ceramic. The resulting ceramic coating has a lower thermal conductivity than conventional columnar ceramic coatings.
摘要:
A method of improving the oxidation and corrosion resistance of a superalloy article comprises providing a superalloy substrate having a sulphur content which is less than 0.8 ppm by weight, and depositing on the substrate a protective antioxidation coating having a sulphur content also less than 0.8 ppm by weight. A heat barrier layer may also be provided by depositing on the protective anti-oxidation coating a ceramic coating of columnar structure.
摘要:
A ceramic heat barrier coating is deposited on a substrate so that the coating has a columnar growth pattern which is interrupted and repeated a number of times throughout its thickness by successive regermination of the ceramic deposit. The regermination is obtained by a vapor phase deposition process wherein a polluting gas is introduced intermittently during the deposition of the ceramic. The resulting ceramic coating has a lower thermal conductivity than conventional columnar ceramic coatings.
摘要:
A thermal barrier coating for a superalloy part used, in particular, in turbomachines comprises a ceramic coating and a sub-layer interposed between the superalloy substrate and the ceramic coating, the sub-layer being composed of a nickel and/or cobalt aluminide containing at least one platinum-like metal and at least one metal for promoting the formation of a layer of oxide constituted by the alpha-allotropic variety of alumina.