摘要:
Polyester fibers having both a high strength and a high modulus prepared from ethylene terephthalate polyester, and having an intrinsic viscosity of not less than 1.0 and an initial tensile modulus is not less than 130 g/d, said intrinsic viscosity being determined in a mixed solvent of p-chlorophenol and tetrachloro ethane (3:1) at 30.degree. C. Processes for producing the fibers are also disclosed.
摘要:
Process for producing polyester fibers of high tenacity and high modulus, by melt-spinning a polyester having an intrinsic viscosity of not lower than 0.3, to obtain extruded filaments of low orientation having a birefringence not higher than 10.0.times.10.sup.-3, post-polymerizing the filaments in a heating medium, and subjecting the filaments to multi-stage drawing in at least two stages.
摘要:
A novel ultra-high-molecular-weight polyester prepared from aromatic dicarboxylic acid or alkyl ester thereof and alkylene glycol, and having intrinsic viscosity of not less than 1.5 and insoluble polymer content of not more than 10% by weight.
摘要:
A process for production of polyester which comprises steps of:subjecting aromatic dicarboxylic acid or alkyl ester thereof, and glycol to ester exchange reaction or esterification, andsubjecting the resulting mixture to polycondensation in a specific heating medium.The process can be carried out by using of small energy and a simple apparatus, and provides polyester having high quality.