摘要:
A Co--Pt based magnetic alloy which has been doped with a relatively high amount of nitrogen, e.g., at or above 1 at. % is obtained having high coercivity, for example in the range of 1400 Oe or above, and an increased signal-to-noise ratio as compared to the same Co--Pt based alloy which has not been doped with nitrogen. The alloy is vacuum deposited, for example, by sputtering, and the nitrogen may be introduced from the sputtering gas or from the sputtering target. Other low-solubility elements providing the grain uniformity and isolation include: B, P, S, C, Si, As, Se and Te.
摘要:
A Co-Pt based magnetic alloy which has been doped with a relatively high amount of nitrogen, e.g., or above 1 at. % is obtained having high coercivity, for example in the range of 1400 Oe or above, and an increased signal-to-noise ratio as compared to the same Co-Pt based alloy which has not been doped with nitrogen. The alloy is vacuum deposited, for example, by sputtering, and the nitrogen may be introduced from the sputtering gas or from the sputtering target. Other low-solubility elements providing the grain uniformity and isolation include: B, P, S, C, Si, As, Se and Te.
摘要:
Media according to the present invention is comprised of individual magnetic grains as small as 300 .ANG. or smaller in diameter, which are uniformly spaced apart by a distance between 5 and 50 .ANG. by a solid segregant. This media will typically exhibit coercivity and remanent coercivity squareness of at least 0.8 each, a switching field distribution of less than 0.2, and a coercivity of at least 1500 Oe (with a minimum required Pt content), while simultaneously providing the lowest media jitter noise for optimum magnetic performance. The media is deposited at a low partial pressure of water and in the presence of an optimum amount of contributant gas on a doped nucleation layer for grain growth control.
摘要:
A Co-Pt based magnetic alloy which has been doped with a relatively high amount of nitrogen, e.g., or above 1 at. % is obtained having high coercivity, for example in the range of 1400 Oe or above, and an increased signal-to-noise ratio as compared to the same Co-Pt based alloy which has not been doped with nitrogen. The alloy is vacuum deposited, for example, by sputtering, and the nitrogen may be introduced from the sputtering gas or from the sputtering target. Other low-solubility elements providing the grain uniformity and isolation include: B, P, S, C, Si, As, Se and Te
摘要:
A Co--Pt based magnetic alloy which has been doped with a relatively high amount of nitrogen, e.g., at or above 1 at. % is obtained having high coercivity, for example in the range of 1400 Oe or above, and an increased signal-to-noise ratio as compared to the same Co--Pt based alloy which has not been doped with nitrogen. The alloy is vacuum deposited, for example, by sputtering, and the nitrogen may be introduced from the sputtering gas or from the sputtering target. Other low-solubility elements providing the grain uniformity and isolation include: B, P, S, C, Si, As, Se and Te.