摘要:
A rubber composition comprising: a cured rubber; and thermoplastic resin, where the thermoplastic resin is in the form of discrete domains dispersed within a continuous phase of the cured rubber, and where the cured rubber includes silicon-containing crosslinks.
摘要:
A rubber composition comprising: a cured rubber; and thermoplastic resin, where the thermoplastic resin is in the form of discrete domains dispersed within a continuous phase of the cured rubber, and where the cured rubber includes silicon-containing crosslinks.
摘要:
A method for preparing a thermoplastic vulcanizate, the method comprising dynamically vulcanizing a rubber within a blend that includes the rubber and a thermoplastic polymer, where said dynamically vulcanizing is effected with a cure system that includes a hydrosilating agent and a catalyst, where the hydrosilating agent includes a compound including at least 3 silicon hydride groups defined by the formula where each R is independently a monovalent organic group or hydrogen, and where the silicon atoms of the respective silicon hydride groups are spatially separated by at least 6 atoms.
摘要:
A method for preparing a thermoplastic vulcanizate, the method comprising dynamically vulcanizing a rubber within a blend that includes the rubber and a thermoplastic polymer, where said dynamically vulcanizing is effected with a cure system that includes a hydrosilating agent and a catalyst, where the hydrosilating agent includes a compound including at least 3 silicon hydride groups defined by the formula where each R is independently a monovalent organic group or hydrogen, and where the silicon atoms of the respective silicon hydride groups are spatially separated by at least 6 atoms.
摘要:
A dynamically vulcanized alloy contains at least one isobutylene-containing elastomer and at least one thermoplastic resin, wherein the elastomer is present as a dispersed phase of small vulcanized or partially vulcanized particles in a continuous phase of the thermoplastic resin. The dynamically vulcanized alloy also contains an anhydride functionalized oligomer. The alloy maintains a high Shore A hardness value while obtaining improved flowability for processing.
摘要:
A method of preparing a thermoplastic vulcanizate, the method comprising dynamically vulcanizing a rubber within a blend with a thermoplastic resin, where the dynamic vulcanization is effected with a cure system that includes a free-radical cure agent and triallyl isocyanurate.
摘要:
Thermoplastic elastomer compositions having improved processabillity while maintaining good physical properties are prepared from a mixture of olefinic rubber and a polypropylene composition having a melt flow rate in the range of from about 0.5 to about 5 dg/min. and a molecular weight distribution Mw/Mn of greater than 5.5 up to about 20. The rubber component of the mixture may be at least partially cured by dynamic vulcanization.
摘要:
A thermoplastic vulcanizate prepared by a process comprising the steps of dynamically vulcanizing a vulcanizable rubber within a mixture that includes from about 15 to about 90 percent by weight of the rubber and from about 10 to about 85 percent by weight of a long-chain branched thermoplastic resin, where the long-chain branched thermoplastic resin is (i) an &agr;-olefin polymer, (ii) a copolymer of an &agr;-olefin and an &agr;-&ohgr;-olefin diene, or (iii) a mixture thereof, where the long-chain branched thermoplastic resin is characterized by a weight average molecular weight from about 100,000 to about 600,000, a number average molecular weight from about 40,000 to about 200,000, a z-average molecular weight from about 400,000 to about 2,000,000, a vis from about 0.2 to about 0.95, and a melt flow rate from about 0.3 to about 30 dg/min.
摘要:
Random thermoplastic ethylene copolymers can be used to increase the elongation to break and toughness of thermoplastic vulcanizates. Polypropylene is a preferred thermoplastic phase. The rubber can be olefinic rubbers. Random thermoplastic ethylene copolymers are different from Ziegler-Natta ethylene copolymers as the compositional heterogeneity of the copolymer is greater with Ziegler-Natta copolymers. This difference results in substantial differences in properties (elongation to break and toughness) between thermoplastic vulcanizates modified with random thermoplastic ethylene and those modified with Ziegler-Natta ethylene copolymers. An increase in elongation to break results in greater extensibility in the articles made from a thermoplastic vulcanizate.
摘要:
An improved composition for steel cord reinforced tire belts and tire belts as well as other products made from such composition are provided. The composition includes natural or butadiene rubber or mixtures thereof. A sulfur producing curing agent is present. The composition also includes both carbon black and silica as well as up to about 12 phr of zinc dimethacrylate or other metal salt of a low molecular weight organic acid. A silane may also be present.