摘要:
An aluminum alloy casting material for heat conduction obtained by adding Si to an aluminum alloy casting material with enhanced castability thereby realize enhancement of thermal conductivity. There is provided an aluminum alloy casting material excelling in heat conduction. characterized in that it comprises 5 to 10.0 mass % of Si, 0.1 to 0.5 mass % of Mg and the balance of Al and unavoidable impurities, the aluminum alloy casting material having undergone an aging treatment. Further, there is provided a cast aluminum alloy casting material that while having castability and mechanical strength equivalent to or higher than those of conventional cast aluminum alloys, is also enhanced in heat conduction; and provided a process for producing the cast aluminum alloy. In particular, there are provided a cast aluminum alloy and process for producing the same, wherein Si is contained in an amount of 6.0 to 8.0 mass %, the elements other than Si and Al each in simple form in an amount of ≦0.6%, and wherein the amount of Si solid-dissolved in aluminum parent phase is regulated to 0.5-1.1 mass % while the area ratio of crystallizate in metal structure is regulated to 5-8%. In this connection, the amount of Si solid-dissolved and the area ratio of crystallizate can be attained by performing of heating retaining treatment of the subject matter of cast aluminum alloy after casting operation at 400° to 510°C. for ≧1 hr.
摘要:
An aluminum alloy casting material for heat conducting is provided, wherein the thermal conductivity is improved of an aluminum alloy casting material whereof the castability is improved by the addition of silicon where said invention is characterized by being an aluminum alloy casting material with excellent thermal conductivity, comprising 5-10.0% by mass of silicon, 0.1-0.5% by mass of magnesium and the remainder comprising aluminum and inevitable impurities, and whereon aging treatment has been performed.
摘要:
Disclosed are: a casting aluminum alloy that is excellent in elongation as alternative properties of a high cycle fatigue strength and a thermal fatigue strength and is suitably usable for a casting for which both of the excellent high cycle fatigue strength and the excellent thermal fatigue strength are required, for example, an internal combustion engine cylinder head; a casting made of the aluminum alloy; a manufacturing method of the casting; and further, an internal combustion engine cylinder head composed of the aluminum alloy casting and manufactured by the manufacturing method of the casting. The casting aluminum alloy contains, in terms of mass ratios, 4.0 to 7.0% of Si, 0.5 to 2.0% of Cu, 0.25 to 0.5% of Mg, no more than 0.5% of Fe, no more than 0.5% of Mn, and at least one component selected from the group consisting of Na, Ca and Sr, each mass ratio of which is 0.002 to 0.02%.
摘要:
An aluminum alloy material for use in thermal conduction to which improved castability has been imparted by silicon addition. It has improved thermal conductivity and improved strength. The material has a composition containing 7.5-12.5 mass % Si and 0.1-2.0 mass % Cu, the remainder being Al and unavoidable impurities, wherein the amount of copper in the state of a solid solution in the matrix phase is regulated to 0.3 mass % or smaller. The composition may further contain at least 0.3 mass % Fe and/or at least 0.1 mass % Mg, provided that the sum of (Fe content) and (content of Mg among the impurities)×2 is 1.0 mass % or smaller and the sum of (Cu content), (content of Mg among the impurities)×2.5, and (content of Zn among the impurities) is 2.0 mass % or smaller.
摘要:
An aluminum alloy material for use in thermal conduction to which improved castability has been imparted by silicon addition. It has improved thermal conductivity and improved strength. The material has a composition containing 7.5-12.5 mass % Si and 0.1-2.0 mass % Cu, the remainder being Al and unavoidable impurities, wherein the amount of copper in the state of a solid solution in the matrix phase is regulated to 0.3 mass % or smaller. The composition may further contain at least 0.3 mass % Fe and/or at least 0.1 mass % Mg, provided that the sum of (Fe content) and (content of Mg among the impurities)×2 is 1.0 mass % or smaller and the sum of (Cu content), (content of Mg among the impurities)×2.5, and (content of Zn among the impurities) is 2.0 mass % or smaller.
摘要:
The present invention provides an aluminum alloy for die castings that has superior castability and corrosion resistance. The amounts of Mn, Fe and Cu contained in the aluminum alloy components for die castings were determined to have a considerable effect on the corrosion resistance of the aluminum alloy. Therefore, the aluminum alloy for die castings of the present invention contains 9.0 to 12.0% by weight of Si, 0.20 to 0.80% by weight of Mg, and 0.7 to 1.1% by weight of Mn+Fe, the Mn/Fe ratio is 1.5 or more, the amount of Cu as impurity is controlled to 0.5% by weight or less, and the remainder is composed of aluminum and unavoidable impurities.
摘要:
A high strength aluminum alloy casting obtained by casting an aluminum alloy comprised of 7.5 to 11.5 wt % of Si, 3.8 to 4.8 wt % of Cu, 0.45 to 0.65 wt % of Mg, 0.4 to 0.7 wt % of Fe, 0.35 to 0.45 wt % of Mn, and the balance of Al and not more than 0.2 wt % of unavoidable impurities, wherein this aluminum alloy has 0.1 to 0.3 wt % of Ag added to it or contains 0.1 to 1.0 wt % of at least one element selected from the group of second additive elements comprised of Rb, K, Ba, Sr, Zr, Nb, Ta, V, and Pd and rare earth elements, and a method of production of a high strength aluminum alloy casting comprising the steps of filling a melt of an aluminum alloy in a mold to obtain a casting, taking out the aluminum alloy casting from the mold, solubilizing the high strength aluminum alloy casting by heating in a temperature range of 495 to 505° C. for 2 to 6 hours, quenching the high strength aluminum alloy casting after the solubilization, and age hardening the high strength aluminum alloy casting by heating in a temperature range of 160 to 220° C. for 2 to 6 hours after quenching.
摘要:
A super-elastic titanium alloy for medical use consisting essentially of: molybdenum (Mo) as a β stabilizer element of titanium (Ti): from 2 to 12 at %; an α stabilizer element of the titanium (Ti): from 0.1 to 14 at %; and the balance being titanium (Ti) and inevitable impurities. The α stabilizer element is at least one element selected from the group consisting of aluminum (Al), gallium (Ga) and germanium (Ge).
摘要:
The present invention provides an aluminum alloy for die castings that has superior castability and corrosion resistance. The amounts of Mn, Fe and Cu contained in the aluminum alloy components for die castings were determined to have a considerable effect on the corrosion resistance of the aluminum alloy. Therefore, the aluminum alloy for die castings of the present invention contains 9.0 to 12.0% by weight of Si, 0.20 to 0.80% by weight of Mg, and 0.7 to 1.1% by weight of Mn+Fe, the Mn/Fe ratio is 1.5 or more, the amount of Cu as impurity is controlled to 0.5% by weight or less, and the remainder is composed of aluminum and unavoidable impurities.
摘要:
A method for removing substituted or unsubstituted allyl group from .beta.-lactam compound having substituted or unsubstituted allyl group-protecting carboxyl group, which comprises treating said .beta.-lactam compound with palladium catalyst in the presence of allyl-scavenger in aqueous organic solvent, by which the substituted or unsubstituted group can be easily and effectively removed under moderate conditions so that the desired compound can be obtained in high yield at low cost.