公开(公告)号：US20110007410A1

公开(公告)日：2011-01-13

申请号：US12667467

申请日：2008-07-02

申请人： Ken Honma ,  Hiroshi Nakano ,  Tatsuya Watari ,  Osamu Takise ,  Morio Tsunoda

发明人： Ken Honma ,  Hiroshi Nakano ,  Tatsuya Watari ,  Osamu Takise ,  Morio Tsunoda

IPC分类号： G02B5/08 ,  C08K3/34 ,  C08K5/49 ,  C08K3/28

CPC分类号： F21V7/22 ,  C08K3/34 ,  C08K5/25 ,  C08K5/51 ,  C08L67/02 ,  F21S41/37 ,  C08L2666/14

摘要： The present invention provides a polyester resin composition for injection-molding which is excellent in mold releasability, and is capable of providing light reflectors which are excellent in apparent luminance and reflectivity, and suppressed in hazing even used under high temperatures. A polyester resin composition for injection-molding comprising, (A) 100 parts by weight of a polyester resin, (B) 0.1 to 20 parts by weight of zirconium silicate having an average primary particle size of 10 μm or smaller and (C) 0 to 5 parts by weight of a chelating agent capable of forming a chelate with mono- to tetra-valent metal ions.

摘要翻译： 本发明提供一种脱模性优异的注射成型用聚酯树脂组合物，能够提供即使在高温下使用的表观亮度和反射率优异的光反射体，也抑制了雾度的抑制。 一种注射成型用聚酯树脂组合物，其特征在于，含有（A）100重量份聚酯树脂，（B）0.1〜20重量份平均一次粒径为10μm以下的硅酸锆和（C）0 至5重量份能够与一价至四价金属离子形成螯合物的螯合剂。

公开(公告)号：US20110200811A1

公开(公告)日：2011-08-18

申请号：US13055335

申请日：2009-07-15

申请人： Morio Tsunoda ,  Osamu Takise ,  Yasushi Yamanaka

发明人： Morio Tsunoda ,  Osamu Takise ,  Yasushi Yamanaka

IPC分类号： B32B3/00 ,  C08K5/53 ,  C08K5/3492

CPC分类号： C08K5/34928 ,  C08K5/5313 ,  C08L67/02

摘要： Provided is a resin article comprising a non-halogen series flame retardant to which high flame resistance is imparted. A flame-retardant polybutylene terephthalate series resin composition comprising 100 parts by weight of a polybutylene terephthalate series resin (A) having a glass-transition temperature according to the dynamic viscoelastic method of 0° C. to 75° C., and 5 to 70 parts by weight of a metal phosphinate (B).

摘要翻译： 本发明提供一种包含赋予高阻燃性的非卤素系阻燃剂的树脂制品。 一种阻燃聚对苯二甲酸丁二醇酯系树脂组合物，其包含100重量份根据动态粘弹性方法为0℃至75℃的玻璃化转变温度的聚对苯二甲酸丁二醇酯系列树脂（A）和5至70 重量份的金属次膦酸盐（B）。

公开(公告)号：US08796367B2

公开(公告)日：2014-08-05

申请号：US13055407

申请日：2009-07-22

申请人： Morio Tsunoda ,  Osamu Takise ,  Yasushi Yamanaka

发明人： Morio Tsunoda ,  Osamu Takise ,  Yasushi Yamanaka

IPC分类号： C08K5/3492

CPC分类号： C08L67/02 ,  C08G77/18 ,  C08G77/70 ,  C08K3/38 ,  C08K5/34928 ,  C08K5/5313 ,  C08L51/08 ,  C08L83/04 ,  C08L2666/02 ,  C08L83/00

摘要： A thermoplastic polyester resin composition comprising 100 parts by weight of a thermoplastic polyester resin (A), 5 to 40 parts by weight of a phosphinate (B), and an organosiloxane (X); wherein the phosphinate is a calcium salt or aluminum salt of phosphine acid having the anion part having a particular structure; which, as the organosiloxane (X), comprises 1.5 to 10 parts by weight of an organosiloxane compound (X-1) or 0.01 to 5 parts by weight of an organosiloxane polymer (X-2), relative to 100 parts by weight of the thermoplastic polyester resin (A); and wherein the organosiloxane compound (X-1) comprises organic groups bonding to a silicon atom directly or through an oxygen atom, and 40 mole % or more of the organic groups are an aryl group, and the organosiloxane polymer (X-2) is in the form of solid at 25° C.

摘要翻译： 一种热塑性聚酯树脂组合物，其包含100重量份的热塑性聚酯树脂（A），5至40重量份的次膦酸盐（B）和有机硅氧烷（X）; 其中次膦酸盐是具有具有特定结构的阴离子部分的膦酸的钙盐或铝盐; 作为有机硅氧烷（X），相对于100重量份的有机硅氧烷（X-1），作为有机硅氧烷（X），含有1.5〜10重量份的有机硅氧烷化合物（X-1）或0.01〜5重量份的有机硅氧烷聚合物 热塑性聚酯树脂（A）; 其中有机硅氧烷化合物（X-1）包含直接或通过氧原子与硅原子键合的有机基团，有机基团的40摩尔％以上为芳基，有机硅氧烷聚合物（X-2）为 在25℃下为固体形式

公开(公告)号：US20110201730A1

公开(公告)日：2011-08-18

申请号：US13055407

申请日：2009-07-22

申请人： Morio Tsunoda ,  Osamu Takise ,  Yasushi Yamanaka

发明人： Morio Tsunoda ,  Osamu Takise ,  Yasushi Yamanaka

IPC分类号： C08K5/3492 ,  C08K5/52

CPC分类号： C08L67/02 ,  C08G77/18 ,  C08G77/70 ,  C08K3/38 ,  C08K5/34928 ,  C08K5/5313 ,  C08L51/08 ,  C08L83/04 ,  C08L2666/02 ,  C08L83/00

摘要： A thermoplastic polyester resin composition comprising 100 parts by weight of a thermoplastic polyester resin (A), 5 to 40 parts by weight of a phosphinate (B), and an organosiloxane (X); wherein the phosphinate is a calcium salt or aluminium salt of phosphine acid having the anion part having a particular structure; which, as the organosiloxane (X), comprises 1.5 to 10 parts by weight of an organosiloxane compound (X-1) or 0.01 to 5 parts by weight of an organosiloxane polymer (X-2), relative to 100 parts by weight of the thermoplastic polyester resin (A); and wherein the organosiloxane compound (X-1) comprises organic groups bonding to a silicon atom directly or through an oxygen atom, and 40 mole % or more of the organic groups are an aryl group, and the organosiloxane polymer (X-2) is in the form of solid at 25° C.

摘要翻译： 一种热塑性聚酯树脂组合物，其包含100重量份的热塑性聚酯树脂（A），5至40重量份的次膦酸盐（B）和有机硅氧烷（X）; 其中次膦酸盐是具有具有特定结构的阴离子部分的膦酸的钙盐或铝盐; 作为有机硅氧烷（X），相对于100重量份的有机硅氧烷（X-1），作为有机硅氧烷（X），含有1.5〜10重量份的有机硅氧烷化合物（X-1）或0.01〜5重量份的有机硅氧烷聚合物 热塑性聚酯树脂（A）; 其中有机硅氧烷化合物（X-1）包含直接或通过氧原子与硅原子键合的有机基团，有机基团的40摩尔％以上为芳基，有机硅氧烷聚合物（X-2）为 在25℃下为固体形式