Abstract:
The present invention relates to a surface-modifying sheet including a release sheet and a surface-modifying layer, and the surface-modifying layer containing a component that reacts with a thermosetting resin; a surface-modified member, a coated article, a printed article and a joined body, using the surface-modifying sheet; and a method for producing a surface-modified member.
Abstract:
The present invention provides a double-faced pressure-sensitive adhesive sheet comprising a foam substrate, pressure-sensitive adhesive layers provided on a first face and a second face of the foam substrate, and having an overall thickness t of 400 μm or smaller. At least one of the pressure-sensitive adhesive layers is constituted with a rubber-based pressure-sensitive adhesive comprising, as a base polymer, a block copolymer of a mono-vinyl-substituted aromatic compound and a conjugated diene compound.
Abstract:
This invention provides a PSA sheet comprising a single PSA layer having a thickness of 100 μm or larger. The PSA layer is formed from a solvent-based PSA composition. When a cross-sectional area vertical to the PSA layer is observed, the PSA layer has fewer than 1.0 bubble of 100 μm size or larger per mm2 of cross-sectional area. When the PSA layer is stored at 80° C. for 30 minutes, the mass of toluene released from the PSA layer is 10000 ppm or less of the mass of the PSA layer.
Abstract:
The present invention provides a pressure-sensitive adhesive composition and a pressure-sensitive adhesive sheet comprising a layer formed from the said composition. The pressure-sensitive adhesive composition comprises, as a base polymer, a block copolymer of a mono-vinyl-substituted aromatic compound and a conjugated diene compound. The pressure-sensitive adhesive composition further comprises a tackifier resin (TH) having a hydroxyl value of 80 mgKOH/g or higher.
Abstract:
Provided is a double-faced pressure-sensitive adhesive sheet comprising a non-woven fabric substrate, and a pressure-sensitive adhesive layer provided on each of a first face and a second face thereof. The double-faced pressure-sensitive adhesive sheet has a mass per area of 150 g/m2 or smaller. 85% or more of its mass corresponds to the combined mass of the pressure-sensitive adhesive layers. The non-woven fabric substrate comprises Manila hemp fibers of 6 μm diameter or larger at a proportion of 25% or more by the number of threads of its constituent fibers.
Abstract translation:本发明提供一种双面粘合片,其包含无纺布基材和设置在其第一面和第二面中的每一个上的压敏粘合剂层。 双面粘合片的面积为150g / m 2以下。 其质量的85%以上对应于压敏粘合剂层的组合质量。 非织造织物基材包含直径为6μm或更大的马尼拉麻纤维,其比例为25%或更多,其纤维的丝数。
Abstract:
The present invention provides a pressure-sensitive adhesive composition comprising a base polymer and a tackifier resin. The base polymer is a block copolymer of a mono-vinyl-substituted aromatic compound and a conjugated diene compound. The tackifier resin comprises a low softening point resin having a softening point below 120° C. and a high softening point resin having a softening point of 120° C. or above. The high softening point resin comprises a terpene-phenol resin.