摘要:
The present invention is a polyoxyalkylene polyol, its manufacture method, and derivatives, wherein: it is obtained using a phosphazenium compound as a catalyst; the hydroxyl value is 2˜200 mgKOH/g; total degree of unsaturation is 0.0001˜0.07 meq./g; the head-to-tail bond selectivity of the polyoxyalkylene polyol is 95 mole %; and when the maximum height of the peak of GPC elution curve is set to be 100%, W20 is defined as the peak width at the 20% peak height, and W80 is defined as the peak width at 80% peak height, the ratio of W20/W80 is 1.5 or greater, and less than 3.
摘要:
The object is to provide a method for producing a polyoxyalkylene polyol and a method for producing a derivative thereof wherein the remaining catalyst compound is efficiently removed from a crude polyoxyalkylene polyol by a simple manner, and a method for producing a polyoxyalkylene polyol wherein a crude polyoxyalkylene polyol is produced by addition polymerization of an epoxide compound to an active hydrogen compound using as a catalyst a compound having a P═N bond, then, the crude polyoxyalkylene polyol is allowed to contact with a solid acid having a specific surface area of 450 to 1200 m2/g and an average pore diameter of 40 to 100 Å to control the catalyst-remaining amount in the polyoxyalkylene polyol to 150 ppm or less, and a method for producing a derivative of the-above-described polyol are provided.
摘要:
Disclosed are a polyol with a molecular weight distribution Mw/Mn of 4 or more, obtained by reacting a compound comprising an alkylene oxide compound (II) having a hydroxyl group in a base polyol (I) with a molecular weight of 2000 or more; and a polyol composition for a flexible polyurethane foam, comprising a polyol compound and a crosslinker, wherein the crosslinker comprises a polyol (a) with a hydroxyl value of 50 to 1100 mgKOH/g and with a primary hydroxylate ratio of 25% or more and 60% or less, which is obtained by an addition of a compound comprising alkylene oxide compound (ii) having a hydroxyl group to active hydrogen compound (i).
摘要:
Disclosed are a polyol with a molecular weight distribution Mw/Mn of 4 or more, obtained by reacting a compound comprising an alkylene oxide compound (II) having a hydroxyl group in a base polyol (I) with a molecular weight of 2000 or more; and a polyol composition for a flexible polyurethane foam, comprising a polyol compound and a crosslinker, wherein the crosslinker comprises a polyol (a) with a hydroxyl value of 50 to 1100 mgKOH/g and with a primary hydroxylate ratio of 25% or more and 60% or less, which is obtained by an addition of a compound comprising alkylene oxide compound (ii) having a hydroxyl group to active hydrogen compound (i).
摘要:
To provide a two-component curable solventless adhesive which enables a laminated composite film comprising a barrier layer and a plastic film laminated with each other to maintain excellent appearance and adhesive strength for a long period even after a sterilization treatment at high temperature, and to appropriately adjust a reaction between a base resin and a curing agent during a production of the laminated composite film, thereby to ensure excellent workability, the two-component curable solventless adhesive comprises a base resin and a curing agent, wherein the base resin contains a polyol having an acid group and a secondary or tertiary terminal hydroxyl group accounting for 30% or more of the entire terminal hydroxyl groups of the polyol, and the curing agent contains an isocyanate group-terminated urethane prepolymer containing at least an aralkyl polyisocyanate and/or a modified substance thereof as a raw polyisocyanate, and a content of a low molecular weight polyisocyanate having a molecular weight of 190 or less is 3% by weight or less.
摘要:
A two-component curable solventless adhesive which enables a laminated composite film comprising a barrier layer and a plastic film laminated with each other to maintain excellent appearance and adhesive strength for a long period even after a sterilization treatment at high temperature, and to appropriately adjust a reaction between a base resin and a curing agent during a production of the laminated composite film. The two-component curable solventless adhesive comprises a base resin and a curing agent, wherein the base resin contains a polyol having an acid group and a secondary or tertiary terminal hydroxyl group accounting for 30% or more of the entire terminal hydroxyl groups of the polyol, and the curing agent contains an isocyanate group-terminated urethane prepolymer containing at least an aralkyl polyisocyanate and/or a modified substance thereof as a raw polyisocyanate, and a content of a low molecular weight polyisocyanate is defined.