公开(公告)号：US4678720A

公开(公告)日：1987-07-07

申请号：US895525

申请日：1986-08-11

申请人： Shih C. Hsu ,  Ramas V. Raman

发明人： Shih C. Hsu ,  Ramas V. Raman

IPC分类号： B23K35/02 ,  B23K35/30 ,  B23K35/34 ,  B23K35/362 ,  C22C1/02 ,  C22C5/08

CPC分类号： B23K35/3006 ,  B23K35/0233 ,  Y10T428/12431 ,  Y10T428/12438

摘要： A silver-copper-titanium brazing alloy foil was produced by a rapid solidification processing method(s). The composition ranged from 10 to 50 weight percent copper, 0.1 to 9.5 weight percent titanium and the balance silver. Since the method provides high cooling rates, at least 10000.degree. C. per second, unique alloy structures and properties were obtained. This resulting foil can be used in the as cast form, it can be rolled down to a thinner dimension having also a more uniform surface finish, or it can be punched into preforms.