摘要:
The present invention relates to an aqueous coating material containing polymer (I), colloidal silica (II), and nonionic surfactant (III) with an HLB value of 16 or more. The polymer (I) is obtained by copolymerization of monomer mixture (M) that contains 0.2 to 10% by mass of monomer (a) having two or more radically polymerizable groups. The solid content of the colloidal silica (II) is 0.1 to 20 parts by mass with respect to 100 parts by mass of the polymer (I). The content of the nonionic surfactant (III) is 0.01 to 10 parts by mass with respect to 100 parts by mass of the polymer (I). The present invention also relates to a painted article where the aqueous coating material is applied. Therefore, an aqueous coating material and a painted article capable of expressing stain resistance and weather resistance can be provided by reducing a water contact angle.
摘要:
The present invention relates to an aqueous coating material containing polymer (I), colloidal silica (II), and nonionic surfactant (III) with an HLB value of 16 or more. The polymer (I) is obtained by copolymerization of monomer mixture (M) that contains 0.2 to 10% by mass of monomer (a) having two or more radically polymerizable groups. The solid content of the colloidal silica (II) is 0.1 to 20 parts by mass with respect to 100 parts by mass of the polymer (I). The content of the nonionic surfactant (III) is 0.01 to 10 parts by mass with respect to 100 parts by mass of the polymer (I). The present invention also relates to a painted article where the aqueous coating material is applied. Therefore, an aqueous coating material and a painted article capable of expressing stain resistance and weather resistance can be provided by reducing a water contact angle.
摘要:
A coating comprsing a polymer (I)-containing coating component and colloidal. silica (II) of 60 nm or less average particle diameter, wherein 0.5 to 20 parts by mass, in terms of solid content, of colloidal silica (II) is contained per 100 parts by mass of polymer (I) and wherein the area of colloidal silica exposed from the surface of the coating occupies 35% or more based on the coating surface. This coating exhibits excellent antifouling performance and excels in transparency, weather resistance, water resistance, and elongation degree.
摘要:
A coating comprising a polymer (I)-containing coating component and colloidal silica (II) of 60 nm or less average particle diameter, wherein 0.5 to 20 parts by mass, in terms of solid content, of colloidal silica (II) is contained per 100 parts by mass of polymer (I) and wherein the area of colloidal silica exposed from the surface of the coating occupies 35% or more based on the coating surface. This coating exhibits excellent antifouling performance and excels in transparency, weather resistance, water resistance, and elongation degree.
摘要:
Disclosed is a water-based resin composition containing a copolymer (A) which is obtained by carrying out emulsion polymerization of an unsaturated monomer composed of 0.5 to 50 parts by mass of a specific ethylenically unsaturated monomer (a) having a piperidyl group in a molecule and 50 to 99.5 parts by mass of an ethylenically unsaturated monomer (b), which does not substantially contain an ethylenically unsaturated monomer having a specific functional group in a molecule, with the total of the ethylenically unsaturated monomers (a) and (b) being 100 parts by mass, under the coexistence of 0.1 to 10 parts by mass of an emulsifier. Also disclosed are a weather resistance improver for water-based paints using the foregoing water-based resin composition, a weather resistance improver for thermoplastic resins, and a weather resistance improver for solvent-based paints.
摘要:
Disclosed is a water-based resin composition containing a copolymer (A) which is obtained by carrying out emulsion polymerization of an unsaturated monomer composed of 0.5 to 50 parts by mass of a specific ethylenically unsaturated monomer (a) having a piperidyl group in a molecule and 50 to 99.5 parts by mass of an ethylenically unsaturated monomer (b), which does not substantially contain an ethylenically unsaturated monomer having a specific functional group in a molecule, with the total of the ethylenically unsaturated monomers (a) and (b) being 100 parts by mass, under the coexistence of 0.1 to 10 parts by mass of an emulsifier. Also disclosed are a weather resistance improver for water-based paints using the foregoing water-based resin composition, a weather resistance improver for thermoplastic resins, and a weather resistance improver for solvent-based paints.