摘要:
Surfactant-templated mesoporous silicates and mesoporous layered silicate clays having certain porosity parameters are used as reinforcing agents for polymers to make composites. The combination of porosity parameters that allows mesoporous silicates to be competitive with organoclays for the reinforcement of engineering polymers include an average mesopore size of at least 2 nm, a surface are of more than about 50 square meters per gram, a total pore volume of more than about 0.33 cubic centimeters per gram, wherein at least 20% of the total pore volume is due to mesopores about 2 to about 50 nm.
摘要:
Hybrid mesoporous molecular sieve silica compositions which have intergrown wormhole domains and lamellar or hexagonal domains and prepared from mixtures of water soluble silicate precursors and amine surfactant templates through a neutralization reaction are described. The silica compositions are stable above 600° C.
摘要:
Porous inorganic silica foam compositions are derived from water soluble silicate precursors and swollen non-ionic polymer templates are described. The compositions are useful as catalyst supports and as catalysts in hydrocarbon cracking and organic reactions, among other applications.
摘要:
Novel lamellar mesoporous silica compositions which can contain functional inorganic elements and organic functional groups as part of the lamellar silica framework structure are described. The compositions are prepared using gemini amine surfactants as templates or structure directing agents. The compositions have novel high temperature and hydrothermal stability and unique fundamental particle structures.
摘要:
Novel lamellar mesoporous silica compositions which can contain functional inorganic elements and organic functional groups as part of the lamellar silica framework structure are described. The compositions are prepared using gemini amine surfactants as templates or structure directing agents. The compositions have novel high temperature and hydrothermal stability and unique fundamental particle structures.
摘要:
Porous inorganic silica foam compositions are derived from water soluble silicate precursors and swollen non-ionic polymer templates are described. The compositions are useful as catalyst supports and as catalysts in hydrocarbon cracking and organic reactions, among other applications.
摘要:
A process for the preparation of mesostructured molecular sieve silicas from inorganic silicon precursors and polyoxyethylene oxide based polymers is described. The silicas are stable upon calcination to 600° to 800° C. The silicas are useful in refining processes.
摘要:
A process is described for the synthesis of metal oxides in a nanometric particle form that cannot be easily obtained by conventional bulk synthesis techniques. The method makes use of Colloid Occluded Carbons (COC) and Colloid Imprinted Carbons (CIC) as reagents and as templating agents for the preparation of metal oxides in nanometric particle form. The nanometric particles are suitable useful in the field of chemical catalysis, particularly for petroleum refining when in porous form, and as sensors, optical wave guides, and coatings.
摘要:
A process for the preparation of mesostructured organofunctional silica and silica-alumina compositions using a hydrolyzable organosilane compound is described. The process uses a water soluble silicate to form the compositions, which have hexagonal, wormhole or foam mesostructures. The compositions are useful for catalytic and sorption applications.
摘要:
Novel lamellar mesoporous silica compositions which can contain functional inorganic elements and organic functional groups as part of the lamellar silica framework structure are described. The compositions are prepared using gemini amine surfactants as templates or structure directing agents. The compositions have novel high temperature and hydrothermal stability and unique fundamental particle structures.