摘要:
A polyurethane article with shape memory, comprising a mixture of thermoplastic polyurethane and reactive monomer cross-linker which is formed into a shaped article, irradiated, expanded and applied to a medical device, specifically a biomedical electrical lead.
摘要:
A polymerizable solid aliphatic polyurethane containing olefinically unsaturated double bonds, having a very narrow melting range within the temperature range from 40 to 200° C., which is preparable from A) at least one linear aliphatic diisocyanate, B) at least one aliphatic compound containing at least two isocyanate-reactive functional groups and/or water, and C) at least one olefinically unsaturated compound containing an isocyanate-reactive functional group, and its use as a powder coating material or for preparing powder coating materials.
摘要:
This invention provides a polymer polyol composition (I) comprising a polyol (A) and polymer particles (B) dispersed in (A), the polymer particles (B) being formed by polymerizing an ethylenically unsaturated compound (b) in a polyol, wherein the content of (B) in (I) is from 35 to 75 mass %, based on the mass of (I), and the amount of soluble polymers (P) dissolved in (A) is not more than 5 mass %, based on the mass of (A), and provides methods for producing the polymer polyol composition (I). Further, this invention provides a method for producing a foamed or non-foamed polyurethane resin, which method comprises reacting a polyol component with a polyisocyanate component in the presence or absence of a blowing agent, wherein the above polymer polyol composition is used at least as a portion of the polyol component. A polymer polyol having a low viscosity and excellent dispersion is stability is provided even when having a high concentration of polymer particles, and is used advantageously to produce polyurethane resins having excellent 25% ILD (hardness) and compression set, or foams thereof, with good operation efficiency.
摘要:
A curable composition comprises a prepolymer which comprises, in copolymerized form: (a) an on-average at least bifunctional isocyanate based on a compound of the formula I where R1 and R2 are independently C1-C12-alkylene, (b) an ethylenically unsaturated compound containing isocyanate-reactive groups and (c) if desired, a saturated compound containing isocyanate-reactive groups.
摘要:
The invention relates to a binder composition containing A) 50-90 parts by wt. of OH-functional graft copolymer resins prepared from a) 0.1 to 10 parts by wt. of polybutadiene, b) 5 to 60 parts by wt. of an unsaturated aromatic monomer, c) 10 to 50 parts by wt. of a hydroxyalkyl ester of (meth)acrylic acid, d) 5 to 70 parts by wt. of a cycloaliphatic ester of (meth)acrylic acid, e) 5 to 50 parts by wt. of an aliphatic ester of (meth)acrylic acid, f) 0.1 to 5 parts by wt. of a mono-olifinically unsaturated mono- or dicarboxylic acid and/or maleic or fumaric acid half esters, B) 0.1 to 5 parts by wt. of a polyfunctional crosslinking agent.