    FASERVERSTÄRKUNG VON TREIBMITTELHALTIGEN SCHAUMSTOFFEN
    7.
    发明公开
    FASERVERSTÄRKUNG VON TREIBMITTELHALTIGEN SCHAUMSTOFFEN 审中-公开
    FASERVERSTÄRKUNGVON TREIBMITTELHALTIGEN SCHAUMSTOFFEN

    公开(公告)号：EP3237509A1

    公开(公告)日：2017-11-01

    申请号：EP15813777.8

    申请日：2015-12-15

    申请人： BASF SE

    发明人： RUCKDAESCHEL, Holger ,  ARBTER, Rene ,  STEIN, Robert ,  LONGO-SCHEDEL, Daniela ,  DIEHLMANN, Tim ,  SAMPATH, Bangaru Dharmapuri Sriramulu ,  GUTMANN, Peter ,  TERRENOIRE, Alexandre ,  HARTENSTEIN, Markus ,  KIRGIS, Andreas ,  MORINO, Alessio ,  DAUN, Gregor ,  MARTIN, Marc Claude ,  MERKEL, Peter ,  KICIAK, Thomas

    IPC分类号： C08J9/36 ,  C08J9/14 ,  B29C44/56 ,  C08J9/00 ,  B32B5/18 ,  B32B5/24 ,  B32B7/08

    摘要： The present invention relates to a method for producing a molded body from a blowing-agent containing foam material, which comprises at least one fiber (F), said at least one fiber (F) being partly introduced into the blowing-agent containing foam material. The two ends of the respective fiber (F) which are not surrounded by the foam material thus protrude on one side of the corresponding molded body. The invention further relates to a molded body as such. The invention also relates to a panel which comprises at least one such molded body produced according to the method of the invention, and at least one additional layer (S1). The invention further relates to the production of the panels according to the invention and to the use thereof, for example as rotor blades in wind turbines.

    摘要翻译： 本发明涉及一种由含发泡剂的泡沫材料生产模制体的方法，所述泡沫材料包含至少一种纤维（F），所述至少一种纤维（F）部分引入到含发泡剂的泡沫材料 。 相应纤维（F）的未被泡沫材料包围的两端因此在相应的模制体的一侧上突出。 本发明进一步涉及这样的模制体。 本发明还涉及一种面板，其包括至少一个根据本发明的方法制造的这种模制体和至少一个附加层（S1）。 本发明还涉及根据本发明的面板的生产及其用途，例如作为风力涡轮机中的转子叶片。

    VERFAHREN ZUR HERSTELLUNG VON EXPANDIERTEM GRANULAT
    8.
    发明公开
    VERFAHREN ZUR HERSTELLUNG VON EXPANDIERTEM GRANULAT 有权

    公开(公告)号：EP3008122A1

    公开(公告)日：2016-04-20

    申请号：EP14729348.4

    申请日：2014-06-11

    申请人： BASF SE

    发明人： DAESCHLEIN, Christian ,  GUTMANN, Peter ,  PRISSOK, Frank ,  KEPPELER, Uwe ,  AHLERS, Juergen

    IPC分类号： C08J9/16 ,  C08J9/34 ,  C08J9/12 ,  B29C44/34 ,  B29B9/06 ,  B29B9/12

    CPC分类号： B29C44/3461 ,  B29B7/88 ,  B29B7/90 ,  B29B9/06 ,  B29B9/065 ,  B29B9/12 ,  B29B9/14 ,  B29C44/04 ,  B29C47/0011 ,  B29C47/0014 ,  B29C47/86 ,  B29K2021/003 ,  B29K2077/00 ,  B29K2105/0085 ,  B29K2105/16 ,  B29K2995/007 ,  B29K2995/0082 ,  C08J9/0066 ,  C08J9/122 ,  C08J9/16 ,  C08J9/34 ,  C08J2201/03 ,  C08J2203/06 ,  C08J2300/22 ,  C08J2300/26 ,  C08J2377/06

    摘要： The invention relates to a method for producing expanded granulate from a thermoplastic elastomer having a breaking elongation of more than 100% measured according to DIN EN ISO 527-2, comprising the steps: (a) pressing a polymer melt comprising a propellant through a perforated plate (18) which is temperature-controlled to a temperature between 150°C and 280 °C into a granulating chamber (26), (b) reducing the polymer melt pressed through the perforated plate (18) by means of a cutting device (20) into individual, expanding granulate grains, (c) removal of the granulate grains from the granulating chamber (26) by means of a fluid flow (36), wherein the propellant contains CO2 or N2 or a combination of CO2 and N2 and the volume of propellant in the polymer melt comprising propellant lies in the range from 0.5 to 2.0 wt% and wherein a liquid which is temperature-controlled to a temperature between 5°C 20 and 90°C, having a pressure of 0.1 bar to 20 bar above the environmental pressure, flows through the granulating chamber (26), wherein the pressure and temperature of the liquid in the granulating chamber (26) and the temperature of the perforated plate (18) are selected such that the granulate grains in the pressurized liquid are expanded by the contained propellant such that expanded granulate grains having a closed skin result.

    摘要翻译： 本发明涉及从根据DIN EN 150 527-2测量的断裂伸长率大于100％的热塑性弹性体生产发泡颗粒的方法，所述方法包括以下步骤：（a）将包含 发泡剂通过控制在150℃和280℃之间的温度的多孔盘（18）进入造粒室（26），（b）使用切割装置（20）粉碎通过 （18）分成单独的膨胀颗粒，（c）使用液体流（36）从造粒室（26）排出颗粒，其中发泡剂包括CO 2或N 2或CO 2和N 2的组合， 在包含发泡剂的聚合物熔体中的发泡剂在0.5至2.5重量％的范围内，并且其中造粒室（26）被流动的液体流动，该液体流被控制在5℃和90℃之间的温度 ，其压力为0.1b 在高于环境压力的情况下，选择造粒室（26）中的液体的压力和温度以及多孔板（18）的温度，使得颗粒在加压液体中由发泡剂膨胀， 包含以产生具有不间断皮肤的发泡颗粒。