摘要:
A fiber treating composition based on an organopolysiloxane of the average compositional formula:R.sub.x.sup.1 R.sub.y.sup.2 SiO.sub.(4-x-y)/2 (1)wherein R.sup.1 is an organic group having a nitrogen atom, R.sup.2 is a substituted or unsubstituted monovalent hydrocarbon group having 1 to 20 carbon atoms or a group represented by --OR.sup.3 wherein R.sup.3 is a hydrogen atom or a substituted or unsubstituted monovalent hydrocarbon group having 1 to 8 carbon atoms, and letters x and y are 0
摘要:
A radiation curable organopolysiloxane-containing composition is disclosed which is curable by the irradiation with actinic rays in a relatively low dose to give a cured layer having excellent surface-releasability so that the composition is useful, for example, as a coating agent of release paper for temporary protection of adhesive surface. The composition comprises (a) 0.1 to 20 parts by weight of a linear organopolysiloxane having at least one vinylphenyl or isopropenylphenyl group bonded to only one of the terminal silicon atoms in the molecular chain and (b) 99.9 to 80 parts by weight of a (meth)acrylate compound which is a (meth)acrylic acid ester of a polyhydric alcohol or a polyester of a polyhydric alcohol and a dibasic carboxylic acid esterified with (meth)acrylic acid at the residual hydroxy groups.
摘要:
A solventless silicone composition for release paper containing a partially branched organopolysiloxane as a vinyl base polysiloxane to be cured, which may be applied without containing any organic solvents, and which gives a cured film having excellent slip properties and releasability without using any slip-imparting materials.
摘要:
The invention provides a method for improving the stability of the surface-releasing performance of a silicone-coated release paper so as to minimize the changes in the peeling resistance between the release paper and an adhesive surface bonded thereto even after lapse of time from preparation of the release paper to bonding of the adhesive surface or from bonding of the adhesive surface to peeling thereof. The method comprises providing an overcoating layer of an organotin compound such as dibutyl tin diacetate on the surface of a cured coating layer of an organopolysiloxane composition comprising a vinyl-containing organopolysiloxane, an organohydrogenpolysiloxane and a platinum catalyst to promote the addition reaction between the silicon-bonded vinyl groups and the silicon-bonded hydrogen atoms.
摘要:
The inventive silicon-based coating composition provides an antistatic surface-releasing coating layer on a plastic film without the need of any antistatic undercoating. The coating composition comprises, in addition to the conventional ingredients in similar coating compositions including a vinyl-containing organopolysiloxane, an organohydrogenpolysiloxane and a platinum catalyst, a salt, e.g. nitrate and perchlorate, of a metal of the Ist, IInd or VIIIth Group of the Periodic Table and a specific organopolysiloxane having at least one per molecule of alkanolic pendant groups of the formula HO(CH.sub.2 CH.sub.2 O).sub.n CH.sub.2 CH.sub.2 CH.sub.2 --, in which n is 1 to 9.
摘要:
A coating composition comprising (A) a polyorganosiloxane graft copolymer emulsion, (B) a reaction product between an amino functional silane and/or a hydrolyzate thereof and an acid anhydride, (C) colloidal silica, (D) a curing catalyst, and (E) an inorganic filler is useful in coating exterior and interior building materials. The composition is applicable to a substrate to form a coating at room temperature having sufficient extensibility to follow cracks in the underlying substrate as well as low-to-high temperature sensitive performance, moisture permeability, flame retardance, and decorative effect.
摘要:
A releasing silicone composition, which in cured form has from medium to high bond release strength, comprising 0.1 to 10 parts by weight of an organopolysiloxane of the formula ##STR1## wherein R.sup.1 is alkyl of 1-3 carbon atoms, or a phenyl group; each R.sup.2 is R.sup.1 or R.sup.3 ; R.sup.3 is C.sub.l H.sub.2l+1 COOCH.sub.2 CH.sub.2 CH.sub.2 -- in which l is an integer from 14-20; m is an integer from 50-200; and n is an integer from 0-20, in a silicone composition comprising 100 parts by weight of an organopolysiloxane which contains at least two vinyl groups bonded directly to silicon atoms, from 0.1 to 30 parts by weight of an organohydrogenpolysiloxane which contains at least two hydrogen atoms bonded directly to silicon atoms, and a platinum catalyst.
摘要:
Disclosed herein is an ultraviolet-curable organopolysiloxane composition which provides a cured film having improved brittleness, hardness, scratch resistance, and durability. The composition is composed of an acrylic-functional organopolysiloxane containing phenylsiloxane units and siloxane units having a specific acrylic functional group, a specific acrylate or methacrylate, and a photoinitiator.
摘要:
A solvent-free releasing silicone composition for rendering surfaces non-adherent which gives a cured film having desirable slip factor, toughness, and high-speed peel characteristics without sacrificing its inherenty merits such as curability, uniformity in peel resistance, and the residual adhesive strength employs a diorganovinylpolysiloxane having trivinylsilyloxy as one end group and either a vinyldimethylsilyl or trimethylsilyl group as the other end group.
摘要:
A releasing silicone composition comprising three ingredients including an organopolysiloxane having at least two specific organosiloxy units having an alkenyl group, a methylhydrogenpolysiloxane material, and a platinum catalyst.