公开(公告)号：US20050000601A1

公开(公告)日：2005-01-06

申请号：US10848119

申请日：2004-05-19

申请人： Yuji Arai ,  Kunio Kondo

发明人： Yuji Arai ,  Kunio Kondo

IPC分类号： B60R21/26 ,  C21D8/10 ,  C21D9/08 ,  C22C38/00

CPC分类号： C21D9/08 ,  B60R21/26 ,  C21D8/10 ,  C21D8/105 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/20 ,  C22C38/22 ,  C22C38/24 ,  C22C38/26 ,  C22C38/32 ,  C22C38/54

摘要： A high strength steel pipe for an airbag system has a steel composition comprising C: 0.05-0.20%, Si: 0.1-1.0%, P; at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10% at least one of Ti and Mn satisfying (1) Ti≦0.02% and (2) 0.4%≦Mn+40Ti≦1.2%, and a remainder of Fe. The composition may further include one or more of (i) at least one of Mo: 0.05-0.50%, Ni: 0.05-1.5%, V: 0.01-0.2%, and B: 0.0003-0.005%, (ii) at least one of Cu: 0.05-0.5% and Nb: 0.003-0.1%, and (iii) at least one of Ca: 0.0003-0.01%, Mg: 0.0003-0.01%, and REM: 0.0003-0.01%. The steel pipe can be manufactured by forming a pipe from the above-described steel composition to obtain prescribed dimensions, heating to at least the Ac1 transformation point and quenching, and then tempering at the Ac1 transformation point or below.

摘要翻译： 用于气囊系统的高强度钢管具有C：0.05-0.20％，Si：0.1-1.0％，P; 至少0.025％，S：0.010％以下，Cr：0.05〜1.0％，Al：0.10％以下，满足（1）Ti <0.02％的Ti和Mn中的至少一种，（2）0.4％ + 40Ti <= 1.2％，余量为Fe。 所述组合物还可包括以下中的至少一种：（i）Mo：0.05-0.50％，Ni：0.05-1.5％，V：0.01-0.2％和B：0.0003-0.005％中的至少一种，（ii）至少 Cu：0.05〜0.5％，Nb：0.003〜0.1％，（iii）Ca：0.0003〜0.01％，Mg：0.0003〜0.01％，REM：0.0003〜0.01％中的至少一种。 钢管可以通过从上述钢组合物形成管而获得规定尺寸，至少加热至Ac1相变点并淬火，然后在Ac1相变点或更低温度下回火来制造。

公开(公告)号：US07316143B2

公开(公告)日：2008-01-08

申请号：US11592782

申请日：2006-11-03

申请人： Kunio Kondo ,  Yuji Arai

发明人： Kunio Kondo ,  Yuji Arai

IPC分类号： B21B19/04

CPC分类号： C22C38/38 ,  C21D8/105 ,  C21D9/08 ,  Y10S72/70

摘要： A seamless steel tube comprising, in mass %, C: 0.30 to 0.50%, Si: 0.5% or less, Mn: 0.3 to 2.0%, P: 0.025% or less, S: 0.005% or less, Cr: 0.15 to 1.0%, Al: 0.001 to 0.05%, Ti: 0.005 to 0.05%, N: 0.02% or less, B: 0.0005 to 0.01% and O (oxygen): 0.0050% or less, wherein Beff defined in following equation (a) or (b) takes a value of 0.0001 or more, where Beff=B−10.8×(N−14×Ti/47.9)/14—(a) when Neff=N−14×Ti/47.9≧0, and Beff=B—(b) when Neff=N−14×Ti/47.9

摘要翻译： 1.一种无缝钢管，以质量％计含有C：0.30〜0.50％，Si：0.5％以下，Mn：0.3〜2.0％，P：0.025％以下，S：0.005％以下，Cr：0.15〜1.0 ％，Al：0.001〜0.05％，Ti：0.005〜0.05％，N：0.02％以下，B：0.0005〜0.01％，O（氧）：0.0050％以下， （b）取值为0.0001以上，当Neff = N-14xTi / 47.9> = 0时，Beff = B-10.8x（N-14xTi / 47.9）/ 14-（a），Beff = B- ）当Neff = N-14xTi / 47.9 <0时，能够提供具有优异的冷加工性，淬透性，韧性和扭转疲劳强度的无缝钢管，并且最适合用于制造一体式中空驱动轴 以及。

公开(公告)号：US08845830B2

公开(公告)日：2014-09-30

申请号：US13354609

申请日：2012-01-20

申请人： Kunio Kondo ,  Yuji Arai

发明人： Kunio Kondo ,  Yuji Arai

IPC分类号： C21D8/10 ,  C21D9/14 ,  C22C38/02 ,  C22C38/26 ,  C22C38/04 ,  C22C38/24 ,  C22C38/46 ,  C22C38/48 ,  C22C38/22 ,  C22C38/06 ,  C22C38/42 ,  C22C38/44 ,  C21D1/42

CPC分类号： C21D9/14 ,  C21D1/42 ,  C21D8/105 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/24 ,  C22C38/26 ,  C22C38/42 ,  C22C38/44 ,  C22C38/46 ,  C22C38/48 ,  Y02P10/253

摘要： A steel pipe with a wall thickness over 30 mm is subjected to heat treatment of quenching and tempering using a temperature range of at least not less than 750° C. during the heating stage, makes it possible to obtain a heavy-wall seamless steel pipe having excellent toughness by resulting grain refinement. Quenching is by performing water cooling after heating the steel pipe to a temperature in the range of not less than 900° C. to not more than 1000° C. by using, as a heating means, induction heating at a frequency of not more than 200 Hz. Tempering is performed at a temperature in the range of not less than 500° C. to not more than 750° C. Preferably, after the heating by induction heating, a soaking treatment is performed in the temperature range of not less than 900° C. to not more than 1000° C. for 10 minutes or less followed by water cooling.

摘要翻译： 在加热阶段期间，使用壁厚30mm以上的钢管进行淬火回火热处理，至少不低于750℃的温度范围，可以获得厚壁无缝钢管 由于晶粒细化而具有优异的韧性。 淬火是在将钢管加热至不低于900℃至不超过1000℃的温度下进行水冷，通过以加热方式使用频率不大于 200 Hz。 回火在不低于500℃至不超过750℃的温度下进行。优选地，在通过感应加热加热之后，在不低于900℃的温度范围内进行均热处理 在1000℃以上10分钟以下，然后水冷却。

公开(公告)号：US20100065166A1

公开(公告)日：2010-03-18

申请号：US12575028

申请日：2009-10-07

申请人： Kunio Kondo ,  Yuji Arai

发明人： Kunio Kondo ,  Yuji Arai

IPC分类号： C21D9/08 ,  C22C38/04 ,  C22C38/02 ,  C22C38/18 ,  C22C38/16 ,  C22C38/08 ,  C22C38/00

摘要： A steel pipe with excellent expandability, comprises, by mass %, C: 0.1 to 0.45%, Si: 0.3 to 3.5%, Mn: 0.5 to 5%, P: less than or equal to 0.03%, S: less than or equal to 0.01%, soluble Al: 0.01 to 0.8% (more than or equal to 0.1% in case Si content is less than 1.5%), N: less than or equal to 0.05%, O: less than or equal to 0.01%, and balance being Fe and impurities, having a mixed microstructure comprising ferrite and one or more selected from fine pearlite, bainite and martensite, and has a tensile strength of more than or equal to 600 MPa and a uniform elongation satisfying the following formula u-el≧28−0.0075 TS, wherein u-el is uniform elongation (%) and TS is tensile strength (MPa).

摘要翻译： 具有优异的膨胀性的钢管以C：0.1〜0.45％，Si：0.3〜3.5％，Mn：0.5〜5％，P：小于或等于0.03％，S：小于或等于 至0.01％，可溶性Al：0.01〜0.8％（Si含量小于1.5％时大于等于0.1％），N：小于等于0.05％，O：0.01以下， 余量为Fe和杂质，具有包含铁素体和选自细珠光体，贝氏体和马氏体中的一种或多种的混合显微组织，并且具有大于或等于600MPa的拉伸强度和满足下式u-el的均匀伸长率 ≧28-0.0075 TS，其中u-el为均匀伸长率（％），TS为拉伸强度（MPa）。

公开(公告)号：US09175360B2

公开(公告)日：2015-11-03

申请号：US13540016

申请日：2012-07-02

申请人： Keisuke Hitoshio ,  Kunio Kondo ,  Yuji Arai

发明人： Keisuke Hitoshio ,  Kunio Kondo ,  Yuji Arai

IPC分类号： C21D9/08 ,  C22C38/00 ,  C22C38/08 ,  C21D8/10 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/26 ,  C22C38/28 ,  C22C38/42 ,  C22C38/44 ,  C22C38/46 ,  C22C38/50 ,  C21D1/18 ,  F16L9/02

CPC分类号： C21D8/105 ,  C21D1/18 ,  C21D9/08 ,  C21D9/085 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/26 ,  C22C38/28 ,  C22C38/42 ,  C22C38/44 ,  C22C38/46 ,  C22C38/50 ,  F16L9/02

摘要： There is provided a method for manufacturing a seamless steel pipe for line pipe, capable of improving the toughness of the seamless steel pipe for line pipe. A round billet having a chemical composition, by mass percent, of C: 0.02 to 0.15%, Si: at most 0.5%, and Mn: 0.5 to 2.5%, the balance being Fe and impurities, is heated. The heated round billet is piercing-rolled to produce a hollow shell. The hollow shell is elongated and rolled and sized to produce a seamless steel pipe. The seamless steel pipe is water cooled, and the water cooling is stopped when the temperature of the seamless steel pipe reaches at most 450° C. The water-cooled seamless steel pipe is quenched, and the quenched seamless steel pipe is tempered.

摘要翻译： 提供一种能够提高线管用无缝钢管的韧性的管线管用无缝钢管的制造方法。 将化学组成按C：0.02〜0.15％，Si：0.5％以下，Mn：0.5〜2.5％的化学组成的圆坯加热，其余为Fe和杂质。 加热的圆形坯料被穿孔轧制以制造中空壳体。 中空的外壳是细长的并且被轧制和大小以产生无缝钢管。 无缝钢管水冷却，当无缝钢管的温度达到450℃以上时，水冷停止。水冷无缝钢管淬火，淬火无缝钢管回火。

公开(公告)号：US08852366B2

公开(公告)日：2014-10-07

申请号：US13017087

申请日：2011-01-31

申请人： Kunio Kondo ,  Yuji Arai

发明人： Kunio Kondo ,  Yuji Arai

IPC分类号： C21D9/08 ,  C22C38/04 ,  C21D1/56 ,  C22C38/02 ,  C21D11/00 ,  C22C38/06 ,  C21D8/10

CPC分类号： C22C38/02 ,  C21D1/56 ,  C21D8/10 ,  C21D9/08 ,  C21D11/005 ,  C21D2211/002 ,  C21D2211/005 ,  C21D2211/008 ,  C21D2211/009 ,  C22C38/04 ,  C22C38/06

摘要： A steel pipe with excellent expandability, comprising, by mass %, C: 0.1 to 0.45%, Si: 0.3 to 3.5%, Mn: 0.5 to 5%, P: less than or equal to 0.03%, S: less than or equal to 0.01%, soluble Al: 0.01 to 0.8% (more than or equal to 0.1% in case Si content is less than 1.5%), N: less than or equal to 0.05%, O: less than or equal to 0.01%, and balance being Fe and impurities, having a mixed microstructure comprising ferrite and one or more selected from fine pearlite, bainite and martensite, and having a tensile strength of more than or equal to 600 MPa and a uniform elongation satisfying following formula (1).This steel pipe, having the above described chemical composition, can be obtained, for example, by being heated at temperatures from 700 to 790° C., then being forced-cooled down to a temperature of lower than or equal to 100° C. with the cooling rate of greater than or equal to 100° C./min at the temperature from 700 to 500° C. u-el≧28−0.0075TS  (1), wherein u-el means uniform elongation (%), and TS means tensile strength (MPa).

摘要翻译： 具有优异膨胀性的钢管，以质量％计含有C：0.1〜0.45％，Si：0.3〜3.5％，Mn：0.5〜5％，P：小于或等于0.03％，S：小于或等于 至0.01％，可溶性Al：0.01〜0.8％（Si含量小于1.5％时大于等于0.1％），N：小于等于0.05％，O：0.01以下， 余量为Fe和杂质，具有包含铁素体和选自细珠光体，贝氏体和马氏体中的一种或多种的混合显微组织，并且具有大于或等于600MPa的拉伸强度和满足下式（1）的均匀伸长率。 具有上述化学组成的钢管可以例如通过在700〜790℃的温度下加热而被强制冷却至低于或等于100℃的温度。 在700至500℃的温度下，冷却​​速率大于或等于100℃/ min。u-el≥28-0.0075TS（1），其中u-el表示均匀伸长率（％），以及 TS表示拉伸强度（MPa）。

公开(公告)号：US08696834B2

公开(公告)日：2014-04-15

申请号：US13236702

申请日：2011-09-20

申请人： Keiichi Kondo ,  Toshiharu Abe ,  Kunio Kondo ,  Yuichi Yano ,  Yuji Arai

发明人： Keiichi Kondo ,  Toshiharu Abe ,  Kunio Kondo ,  Yuichi Yano ,  Yuji Arai

IPC分类号： C21D9/08 ,  C22C38/22 ,  C21D11/00

CPC分类号： C21D8/105 ,  C21D9/085 ,  C22C1/002 ,  C22C38/00 ,  C22C38/001 ,  C22C38/002 ,  C22C38/005 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/24 ,  C22C38/26 ,  C22C38/28 ,  C22C38/32

摘要： A method for suppressing shock and storage cracking when manufacturing seamless steel pipes comprises hot piercing and hot rolling a billet consisting of, by mass percent controlled amounts of C, Si, Mn, Cr, Mo, Ti, and Al, with the balance being Fe and impurities of Ni, P, S, N, and O also in controlled amounts. Further heat treatment is performed, wherein a hot rolled steel pipe is direct quenched from a temperature of not lower than the Ar3 transformation point and the pipe is then subjected to heat treatment at a temperature of not lower than 450° C. and not higher than the Ac1 transformation point in heat treatment equipment for performing direct quenching. The steel pipe subjected to the heat treatment is reheated, quenched from a temperature of not lower than the Ac3 transformation point, and tempered at a temperature of not higher than the Ac1 transformation point.

摘要翻译： 制造无缝钢管时的冲击和储存裂纹的抑制方法，其特征在于，以C，Si，Mn，Cr，Mo，Ti，Al的质量百分比计，由热刺穿和热轧制成的坯料，余量为Fe 和Ni，P，S，N和O的杂质也是受控量的。 进行进一步的热处理，其中热轧钢管从不低于Ar 3相变点的温度直接淬火，然后在不低于450℃的温度下对管进行热处理， 用于直接淬火的热处理设备的Ac1转换点。 进行热处理的钢管从不低于Ac 3相变点的温度再加热淬火，并在不高于Ac1相变点的温度下回火。

公开(公告)号：US07727463B2

公开(公告)日：2010-06-01

申请号：US11266265

申请日：2005-11-04

申请人： Yuji Arai ,  Kunio Kondo

发明人： Yuji Arai ,  Kunio Kondo

IPC分类号： C22C38/18 ,  C22C38/00 ,  C21D1/00

CPC分类号： C21D9/08 ,  B60R21/26 ,  C21D8/10 ,  C21D8/105 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/20 ,  C22C38/22 ,  C22C38/24 ,  C22C38/26 ,  C22C38/32 ,  C22C38/54

摘要： A high strength steel pipe for an airbag system has a steel composition comprising C: 0.05-0.20%, Si: 0.1-1.0%, P: at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10%, at least one of Ti and Mn satisfying (1) Ti≦0.02% and (2) 0.4%≦Mn+40Ti≦1.2%, and a remainder of Fe. The composition may further include one or more of (i) at least one of Mo: 0.05-0.50%, Ni: 0.05-1.5%, V: 0.01-0.2%, and B: 0.0003-0.005%, (ii) at least one of Cu: 0.05-0.5% and Nb: 0.003-0.1%, and (iii) at least one of Ca: 0.0003-0.01%, Mg: 0.0003-0.01%, and REM: 0.0003-0.01%. The steel pipe can be manufactured by forming a pipe from the above-described steel composition to obtain prescribed dimensions, heating to at least the Ac1 transformation point and quenching, and then tempering at the Ac1 transformation point or below.

摘要翻译： 用于气囊系统的高强度钢管具有C：0.05-0.20％，Si：0.1-1.0％，P：0.025％以下，S：0.010％以下，Cr：0.05〜1.0％，Al ：至多0.10％，Ti和Mn中的至少一种满足（1）Ti＆nlE; 0.02％和（2）0.4％＆amp; Mn; + 40Ti＆nlE; 1.2％，余量为Fe。 所述组合物还可包括以下中的至少一种：（i）Mo：0.05-0.50％，Ni：0.05-1.5％，V：0.01-0.2％和B：0.0003-0.005％中的至少一种，（ii）至少 Cu：0.05〜0.5％，Nb：0.003〜0.1％，（iii）Ca：0.0003〜0.01％，Mg：0.0003〜0.01％，REM：0.0003〜0.01％中的至少一种。 钢管可以通过从上述钢组合物形成管而获得规定尺寸，至少加热至Ac1相变点并淬火，然后在Ac1相变点或更低温度下回火来制造。

公开(公告)号：US20070101789A1

公开(公告)日：2007-05-10

申请号：US11592782

申请日：2006-11-03

申请人： Kunio Kondo ,  Yuji Arai

发明人： Kunio Kondo ,  Yuji Arai

IPC分类号： C22C38/32 ,  B21B19/04

CPC分类号： C22C38/38 ,  C21D8/105 ,  C21D9/08 ,  Y10S72/70

摘要： A seamless steel tube comprising, in mass %, C: 0.30 to 0.50%, Si: 0.5% or less, Mn: 0.3 to 2.0%, P: 0.025% or less, S: 0.005% or less, Cr: 0.15 to 1.0%, Al: 0.001 to 0.05%, Ti: 0.005 to 0.05%, N: 0.02% or less, B: 0.0005 to 0.01% and O (oxygen): 0.0050% or less, wherein Beff defined in following equation (a) or (b) takes a value of 0.0001 or more, where Beff=B−10.8×(N−14×Ti/47.9)/14 - - - (a) when Neff=N−14×Ti/47.9≧0, and Beff=B - - - (b) when Neff=N−14×Ti/47.9

摘要翻译： 1.一种无缝钢管，以质量％计含有C：0.30〜0.50％，Si：0.5％以下，Mn：0.3〜2.0％，P：0.025％以下，S：0.005％以下，Cr：0.15〜1.0 ％，Al：0.001〜0.05％，Ti：0.005〜0.05％，N：0.02％以下，B：0.0005〜0.01％，O（氧）：0.0050％以下， （b）当Neff = N-14xTi / 47.9> = 0时，Beff = B-10.8x（N-14xTi / 47.9）/ 14 - - （a）的值为0.0001以上，Beff = B- - - （b）当Neff = N-14xTi / 47.9 <0时，能够提供具有优异的冷加工性，淬透性，韧性和扭转疲劳强度的无缝钢管，并且最适用于制造一件式的中空轴坯 型中空驱动轴。

公开(公告)号：US20060130945A1

公开(公告)日：2006-06-22

申请号：US11266265

申请日：2005-11-04

申请人： Yuji Arai ,  Kunio Kondo

发明人： Yuji Arai ,  Kunio Kondo

IPC分类号： C21D9/08

CPC分类号： C21D9/08 ,  B60R21/26 ,  C21D8/10 ,  C21D8/105 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/20 ,  C22C38/22 ,  C22C38/24 ,  C22C38/26 ,  C22C38/32 ,  C22C38/54

摘要： A high strength steel pipe for an airbag system has a steel composition comprising C: 0.05-0.20%, Si: 0.1-1.0%, P: at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10%, at least one of Ti and Mn satisfying (1) Ti≦0.02% and (2) 0.4%≦Mn+40Ti≦1.2%, and a remainder of Fe. The composition may further include one or more of (i) at least one of Mo: 0.05-0.50%, Ni: 0.05-1.5%, V: 0.01-0.2%, and B: 0.0003-0.005%, (ii) at least one of Cu: 0.05-0.5% and Nb: 0.003-0.1%, and (iii) at least one of Ca: 0.0003-0.01%, Mg: 0.0003-0.01%, and REM: 0.0003-0.01%. The steel pipe can be manufactured by forming a pipe from the above-described steel composition to obtain prescribed dimensions, heating to at least the Ac1 transformation point and quenching, and then tempering at the Ac1 transformation point or below.

摘要翻译： 用于气囊系统的高强度钢管具有C：0.05-0.20％，Si：0.1-1.0％，P：0.025％以下，S：0.010％以下，Cr：0.05〜1.0％，Al ：至多0.10％，Ti和Mn中的至少一种满足（1）Ti <= 0.02％和（2）0.4％<= Mn + 40Ti <= 1.2％，余量为Fe。 所述组合物还可包括以下中的至少一种：（i）Mo：0.05-0.50％，Ni：0.05-1.5％，V：0.01-0.2％和B：0.0003-0.005％中的至少一种，（ii）至少 Cu：0.05〜0.5％，Nb：0.003〜0.1％，（iii）Ca：0.0003〜0.01％，Mg：0.0003〜0.01％，REM：0.0003〜0.01％中的至少一种。 钢管可以通过从上述钢组合物形成管而获得规定的尺寸，加热到至少相变点和淬火，然后在Ac＆lt; 1 转换点或以下。