摘要:
An environmental barrier is formed on a substrate (10) of ceramic matrix composite material and comprises an outer anticorrosion protection layer (12) containing a compound of the type comprising an aluminosilicate of an alkali, or an alkaline-earth, or a rare-earth element. A bond sub-layer (14) is formed between the substrate (10) and the protection layer (12), the composition of the bond sub-layer varying from substantially pure silicon to substantially pure mullite between an inner face beside the substrate and an outer face, with the silicon content decreasing and the mullite content increasing.
摘要:
A fiber reinforcing texture woven as a single part for fabricating a composite material part having an inner portion, or core, made by three-dimensional weaving with yarns made up from discontinuous fibers, and a portion adjacent to an outside surface, or skin, made by weaving with yarns made up from continuous filaments.
摘要:
An environmental barrier for a substrate of ceramic matrix composite material containing silicon, in particular containing SiC, is formed by an anticorrosion protection layer containing an aluminosilicate type compound of an alkali or alkaline-earth or rare earth element, e.g. BSAS, with a chemical barrier forming layer of aluminum nitride being interposed between the substrate and the anticorrosion protection layer.
摘要:
In order to protect a substrate having at least a portion adjacent to a surface that is made of a refractory material containing silicon, while the substrate is in use at high temperature in a medium that is oxidizing and wet, there is formed on the surface of the substrate an environmental barrier that contains no boron and that has at least one layer that is essentially constituted by a system of oxides formed by at least one rare earth oxide, silica, and alumina, and that is capable of self-healing by maintaining the presence of at least one solid phase in a temperature range extending up to at least 1400° C. approximately.
摘要:
A fiber reinforcing texture (10) woven as a single part for fabricating a composite material part having an inner portion (12), or core, made by three-dimensional weaving with yarns made up from discontinuous fibers, and a portion (14, 16) adjacent to an outside surface, or skin, made by weaving with yarns made up from continuous filaments.
摘要:
In order to protect a substrate having at least a portion adjacent to a surface that is made of a refractory material containing silicon, while the substrate is in use at high temperature in a medium that is oxidizing and wet, there is formed on the surface of the substrate an environmental barrier that contains no boron and that has at least one layer that is essentially constituted by a system of oxides formed by at least one rare earth oxide, silica, and alumina, and that is capable of self-healing by maintaining the presence of at least one solid phase in a temperature range extending up to at least 1400° C. approximately.
摘要:
A fiber reinforcing texture woven as a single part for fabricating a composite material part having an inner portion, or core, made by three-dimensional weaving with yarns made up from discontinuous fibers, and a portion adjacent to an outside surface, or skin, made by weaving with yarns made up from continuous filaments.
摘要:
A fiber reinforcing texture (10) woven as a single part for fabricating a composite material part having an inner portion (12), or core, made by three-dimensional weaving with yarns made up from discontinuous fibers, and a portion (14, 16) adjacent to an outside surface, or skin, made by weaving with yarns made up from continuous filaments.
摘要:
An environmental barrier for a substrate of ceramic matrix composite material containing silicon, in particular containing SiC, is formed by an anticorrosion protection layer containing an aluminosilicate type compound of an alkali or alkaline-earth or rare earth element, e.g. BSAS, with a chemical barrier forming layer of aluminum nitride being interposed between the substrate and the anticorrosion protection layer.
摘要:
An environmental barrier is formed on a substrate (10) of ceramic matrix composite material and comprises an outer anticorrosion protection layer (12) containing a compound of the type comprising an aluminosilicate of an alkali, or an alkaline-earth, or a rare-earth element. A bond sub-layer (14) is formed between the substrate (10) and the protection layer (12), the composition of the bond sub-layer varying from substantially pure silicon to substantially pure mullite between an inner face beside the substrate and an outer face, with the silicon content decreasing and the mullite content increasing.