摘要:
Disclosed is a polyester film for optical applications, and more specifically to a polyester film having refractive index of 1.6 to 1.7 and a film having refractive index of 1.4 to 1.6 on both surfaces of the polyester film, wherein a thickness of each coating layer is 0.03 to 0.1 μm and total light transmittance of the entire film is 93% or more. The polyester film according to the embodiment has total light transmittance higher than the polyester film without the coating layer and is more suitable to use the polyester film for optical applications due to the excellent adhesive strength between the polyester film and layer for the post-processing working.
摘要:
The present invention relates to a process for forming a porous poly(vinyl alcohol) (PVA) scaffold using a pore-forming agent, comprising: mixing PVA with the pore-forming agent to form micropores in the PVA scaffold and using an easily decomposable pore-forming agent after the formation of the pores to improve convenience and reduce the processing time in manufacturing the porous PVA scaffold as well as to enable a pore size and porosity to be selected. A process for forming a porous PVA scaffold using a pore-forming agent according to the present invention includes heating to melt the PVA, cooling the melted PVA and mixing the PVA with a heat-decomposable pore-forming agent, repeating the freezing/thawing of the mixed PVA to cure the PVA mixture, and stirring the cured PVA mixture with a hydrochloric acid solution at a high temperature of 65° C. or more to produce foam.
摘要:
Disclosed is a polyester film for optical applications, and more specifically to a polyester film having refractive index of 1.6 to 1.7 and a film having refractive index of 1.4 to 1.6 on both surfaces of the polyester film, wherein a thickness of each coating layer is 0.03 to 0.1 μm and total light transmittance of the entire film is 93% or more. The polyester film according to the embodiment has total light transmittance higher than the polyester film without the coating layer and is more suitable to use the polyester film for optical applications due to the excellent adhesive strength between the polyester film and layer for the post-processing working.
摘要:
The present invention relates to a process for forming a porous poly(vinyl alcohol) (PVA) scaffold using a pore-forming agent, and more particularly, to a process for forming a porous PVA scaffold using a pore-forming agent, comprising: mixing PVA with the pore-forming agent to form micropores in the PVA scaffold and using an easily decomposable pore-forming agent after the formation of the pores to improve convenience and reduce the processing time in manufacturing the porous PVA scaffold as well as to enable a pore size and porosity to be selected. A process for forming a porous PVA scaffold using a pore-forming agent according to the present invention includes heating to melt the PVA, cooling the melted PVA and mixing the PVA with a heat-decomposable pore-forming agent, repeating the freezing/thawing of the mixed PVA to cure the PVA mixture, and stirring the cured PVA mixture with a hydrochloric acid solution at a high temperature of 65° C. or more to produce foam.