摘要:
The present invention is intended to provide a process for forming an electrodeposition coating film, wherein generation of gas pinhole is reduced and coating film appearance is excellent without using a specific resin as a binder resin.The present invention relates a process for forming an electrodeposition coating film having reduction of generation of gas pinhole, comprising a step of electrocoating by immersing an article to be coated in a cationic electrodeposition coating composition, wherein, the cationic electrodeposition coating composition comprises 10 to 30 parts by weight of a pigment comprising zinc oxide based on 100 parts by weight of a solid content of the coating composition, and the content of zinc oxide contained in the pigment is 0.25 to 5 parts by weight based on 100 parts by weight of the pigment.
摘要:
An electrodeposition coating composition that is excellent in bath stability and that can give a cured film enhanced in hardness and an electrodeposition coating process is provided. An electrodeposition coating composition to be used in an electrodeposition coating process which comprises the electrodeposition step of immersing a substrate in an electrodeposition coating composition and applying a voltage between the substrate as an anode or cathode and a counter electrode to thereby form a film of said electrodeposition coating composition on the surface of the substrate, and the heating step of heating said film obtained in the above electrodeposition step, and said electrodeposition coating composition comprising having electrodeposition potentiality against the curing reaction of said film.
摘要:
An aliphatic hydrocarbon group-containing resin composition for cationic electrocoating, which comprises a resin having a skeleton of epoxy resin and has a number average molecular weight of 500 to 20,000, and which contains, per 100 grams of the nonvolatile matter in said resin composition, (a) 5 to 400 millimoles of sulfonium group, (b) 80 to 355 millimoles of at least one aliphatic hydrocarbon group containing 8 to 24 carbon atoms and optionally containing unsaturated double bond within its chain, and (c) 10 to 315 millimoles of at least one member selected from among propargyl group and a terminal unsaturated double bond-containing organic group containing 3 to 7 carbon atoms; the total content of said (a), said (b) and said (c) being not more than 500 millimoles per 100 grams of the nonvolatile matter in said resin composition.
摘要:
A method for stably and effectively adding a hydrophobic anti-foaming agent into the electrodeposition paint is achieved by adding an anti-foaming agent into a cationic electrodeposition paint wherein, when adding the anti-foaming agent to a cationic electrodeposition paint, a dispersion obtained by preliminarily dispersing the anti-foaming agent into a pigment dispersing resin for a cation electrodeposition paint in an amount of 5 to 1,000 parts by weight (solid content) based on 100 parts by weight (solid content) of a pigment dispersing resin is added to the cationic electrodeposition paint.
摘要:
The present invention provides an improved two-layer coating system. The present invention relates to a process for forming a cured gradient coating film, comprising the steps of: applying an aqueous electrodeposition coating composition comprising at least two resins and a curing agent, on an electrically conductive substrate, heating a electrodeposition coating film to form a layer separation, and then, curing the electrodeposition coating film to form a cured gradient coating film; wherein the resins include one resin component constituting a resin layer (a) in direct contact with air before applying top coating and other resin component constituting a resin layer (b) in direct contact with the electrically conductive substrate, and, wherein a solubility parameter (δa) of a resin component A and a solubility parameter (δb) of a resin component B have a specific relationship.