公开(公告)号：US09051458B2

公开(公告)日：2015-06-09

申请号：US11990651

申请日：2006-08-17

申请人： Joachim Berthold ,  Hansjörg Nitz ,  Werner Rothhöft ,  Heinz Vogt

发明人： Joachim Berthold ,  Hansjörg Nitz ,  Werner Rothhöft ,  Heinz Vogt

IPC分类号： C08L23/06 ,  C08F10/00 ,  C08F10/02 ,  C08F110/02 ,  C08F210/16 ,  C08L23/08

CPC分类号： C08L23/06 ,  C08F10/00 ,  C08F10/02 ,  C08F110/02 ,  C08F210/16 ,  C08L23/08 ,  C08L23/0807 ,  C08L2205/03 ,  Y02P20/52 ,  C08F2/001 ,  C08F2/18 ,  C08L2666/06 ,  C08F2500/01 ,  C08F2500/07 ,  C08F2500/17 ,  C08F2500/12 ,  C08F210/08 ,  C08F2500/05

摘要： A polyethylene molding composition having a multimodal molecular mass distribution and comprising from 45 to 55% by weight of a low molecular weight ethylene homopolymer A, from 20 to 40% by weight of a high molecular weight copolymer B comprising ethylene and another olefin having from 4 to 8 carbon atoms and from 15 to 30% by weight of an ultrahigh molecular weight ethylene copolymer C can be prepared in the presence of a Ziegler catalyst in a three-stage process and is highly suitable for producing pipes having excellent mechanical properties.

公开(公告)号：US08962763B2

公开(公告)日：2015-02-24

申请号：US13517040

申请日：2010-12-14

申请人： Claudio Cavalieri ,  Monica Galvan ,  Roberto Pantaleoni ,  Enrico Beccarini ,  Francesca Tisi ,  Werner Rothhöft

发明人： Claudio Cavalieri ,  Monica Galvan ,  Roberto Pantaleoni ,  Enrico Beccarini ,  Francesca Tisi ,  Werner Rothhöft

IPC分类号： C08L23/08 ,  C08L23/12 ,  C08L23/14 ,  C08L23/20 ,  C08L23/10 ,  C08L23/16

CPC分类号： C08L23/10 ,  C08L23/0815 ,  C08L23/14 ,  C08L23/16 ,  C08L2203/18 ,  C08L2205/03 ,  C08L2666/02 ,  C08L2666/06 ,  C08F210/06 ,  C08F2/001 ,  C08F4/651 ,  C08F4/6492

摘要： A polypropylene composition for injection-molded drainage systems comprising 78-84 wt % of a crystalline propylene polymer, 8 to less than 13 wt % of an elastomeric copolymer and 8 to less than 13 wt % of polyethylene. The said composition exhibits a flexural modulus value higher than 1400 MPa, a melt flow rate (MFR), determined according to ISO method 1133 (230° C. and 2.16 kg), of from 1.5 to 5.0 g/10 min, and a value of Izod impact resistance at 0° C. of more than 6 kJ/m2 according to ISO method 180/1A.

摘要翻译： 一种用于注射成型的排水系统的聚丙烯组合物，其包含78-84重量％的结晶丙烯聚合物，8至小于13重量％的弹性体共聚物和8至小于13重量％的聚乙烯。 所述组合物显示高于1400MPa的挠曲模量值，根据ISO方法1133（230℃和2.16kg）测定的熔体流动速率（MFR）为1.5至5.0g / 10min，值为 根据ISO方法180 / 1A，0℃下的Izod抗冲击强度大于6kJ / m 2。

公开(公告)号：US20120296039A1

公开(公告)日：2012-11-22

申请号：US13517040

申请日：2010-12-14

申请人： Claudio Cavalieri ,  Moníca Galvan ,  Roberto Pantaleoni ,  Enrico Beccarini ,  Francesca Tisi ,  Werner Rothhöft

发明人： Claudio Cavalieri ,  Moníca Galvan ,  Roberto Pantaleoni ,  Enrico Beccarini ,  Francesca Tisi ,  Werner Rothhöft

IPC分类号： C08L23/12 ,  B29C45/00 ,  C08J3/00

CPC分类号： C08L23/10 ,  C08L23/0815 ,  C08L23/14 ,  C08L23/16 ,  C08L2203/18 ,  C08L2205/03 ,  C08L2666/02 ,  C08L2666/06 ,  C08F210/06 ,  C08F2/001 ,  C08F4/651 ,  C08F4/6492

摘要： A polypropylene composition for injection-moulded drainage systems comprising 78-84 wt % of a crystalline propylene polymer, 8 to less than 13 wt % of an elastomeric copolymer and 8 to less than 13 wt % of polyethylene. The said composition exhibits a flexural modulus value higher than 1400 MPa, a melt flow rate (MFR), determined according to ISO method 1133 (230° C. and 2.16 kg), of from 1.5 to 5.0 g/10 min, and a value of Izod impact resistance at 0° C. of more than 6 kJ/m2 according to ISO method 180/1 A.

摘要翻译： 一种用于注射成型的排水系统的聚丙烯组合物，其包含78-84重量％的结晶丙烯聚合物，8至小于13重量％的弹性体共聚物和8至小于13重量％的聚乙烯。 所述组合物显示高于1400MPa的挠曲模量值，根据ISO方法1133（230℃和2.16kg）测定的熔体流动速率（MFR）为1.5至5.0g / 10min，值为 根据ISO方法180/1 A，0℃下的Izod抗冲击强度大于6kJ / m 2。