摘要:
A toner comprised of pigment, and an addition polymer resin generated from about 55 to about 80 weight percent of styrene, from about 1 to about 25 weight percent of acrylate, from about 1 to about 20 weight percent of acrylonitrile, and from about 0.5 to about 5 weight percent of acrylic acid.
摘要:
A toner comprised of pigment, and an addition polymer resin generated from about 55 to about 80 weight percent of styrene, from about 1 to about 25 weight percent of acrylate, from about 1 to about 20 weight percent of acrylonitrile, and from about 0.5 to about 5 weight percent of acrylic acid.
摘要:
A process for the preparation of toner comprising (i) blending (a) an aqueous pigment dispersion containing a first ionic surfactant and an optional charge control agent with (b) a latex blend comprised of linear polymer and crosslinked polymer particles, optional nonionic surfactant and a second ionic surfactant with a charge polarity opposite to that of said first ionic surfactant in said pigment dispersion; (ii) heating the resulting mixture at about below the glass transition temperature (Tg) of the linear latex polymer to form toner sized aggregates; and (iii) subsequently heating said aggregate suspension about above the Tg of the linear latex polymer to effect fusion or coalescence of said aggregates.
摘要:
An in situ chemical process for the preparation of toner comprised of(i) the provision of a latex, which latex is comprised of polymeric resin particles, an ionic surfactant and a nonionic surfactant;(ii) providing a pigment dispersion, which dispersion is comprised of a pigment solution, a counterionic surfactant with a charge polarity of opposite sign to that of said ionic surfactant, and optionally a charge control agent;(iii) mixing said pigment dispersion with said latex with a stirrer equipped with an impeller, stirring at speeds of from about 100 to about 900 rpm for a period of from about 10 minutes to about 150 minutes;(iv) heating the above resulting blend of latex and pigment mixture to a temperature below about the glass transition temperature (Tg) of the resin to form electrostatically bound toner size aggregates;(v) adding further aqueous ionic surfactant or stabilizer in the range amount of from about 0.1 percent to 5 percent by weight of reactants to stabilize the above electrostatically bound toner size aggregates;(vi) heating said electrostatically bound toner sized aggregates above about the Tg of the resin to form toner size particles containing pigment, resin and optionally a charge control agent;(vii) optionally isolating said toner, optionally washing with water; and optionally(viii) drying said toner.
摘要:
A process for the preparation of toner comprising (i) blending (a) a colorant dispersion containing a first ionic surfactant and an optional charge control agent with (b) a latex blend comprised of linear polymer and crosslinked polymer particles, optional nonionic surfactant and a second ionic surfactant with a charge polarity opposite to that of said first ionic surfactant in said colorant dispersion; (ii) heating the resulting mixture at about below the glass transition temperature (Tg) of the linear latex polymer to form toner sized aggregates; and (iii) subsequently heating said aggregate suspension about above the Tg of the linear latex polymer to effect fusion or coalescence of said aggregates, and wherein said linear polymer is of an M.sub.w of from about 20,000 to about 40,000.
摘要:
A process for the preparation of toner including(i) blending an aqueous colorant dispersion with a latex blend comprised of a linear polymer and a soft crosslinked polymer;(ii) heating the resulting mixture at about below, or about equal to the glass transition temperature (Tg) of the linear latex polymer to form aggregates; and(iii) subsequently heating said aggregate suspension about above, or about equal to the Tg of the linear latex polymer to effect fusion or coalescence of said aggregates.
摘要:
A toner composition includes a styrene/butadiene resin having a weight average molecular weight of less than about 70,000 and a number average molecular weight of from about 8,000 to about 12,000, has a glass transition temperature of from about 50.degree. C. to about 60.degree. C. and provides excellent gloss and high fix properties at a low fusing temperature. The styrene/butadiene resin is produced by an emulsion polymerization process that includes forming an emulsion of a surfactant, styrene monomer, butadiene monomer and a water-soluble monomer in water, and then polymerizing the monomers in the presence of a water-soluble initiator.
摘要:
Embodiments include a toner with a distilled wax having a crystallinity of from about 55 to about 100 percent, wherein the degree of crystallinity is calculated using the following formulas: [Heat of enthalpy (Hm) J/g/294 J/g]×100=degree of crystallinity (Xc); [Heat of recrystallization (Hrc) J/g/294 J/g]×100=degree of crystallinity (Xc); and Sc/(Sc+Sa)]×100%, wherein Sc is a diffraction peak area of a crystalline component of the wax and the Sa is a diffraction peak area of an amorphous component of the wax; and wherein the Mp, Mn and Mw of the wax are all within the range of from about 500 to about 800, and wherein the wax has a polydispersity of from about 1 to about 1.05.
摘要:
Embodiments include a fractionated and/or distilled wax having from about 30 to about 64 carbon units, a degree of crystallinity as calculated by heat of melting and as measured by DSC of from about 55 to about 100, a Mw is from about 500 to about 800, and a polydispersity of from about 1 to about 1.05.
摘要:
Embodiments include a distilled wax having a crystallinity of from about 55 to about 100 percent, wherein the degree of crystallinity is calculated using the following formulas: [Heat of enthalpy (Hm) J/g/294 J/g]×100=degree of crystallinity (Xc); [Heat of recrystallization (Hrc) J/g/294 J/g]×100=degree of crystallinity (Xc); and Sc/(Sc+Sa)]×100%, wherein Sc is a diffraction peak area of a crystalline component of the wax and the Sa is a diffraction peak area of an amorphous component of the wax; and wherein the Mp, Mn and Mw of the wax are all within the range of from about 500 to about 800, and wherein the wax has a polydispersity of from about 1 to about 1.05.