摘要:
The present invention is a method of cutting an imaging element. An imaging element is moved through a cutting zone formed by a first cutting blade having a first cutting surface and a first engaging surface and a second cutting blade having a second cutting surface and a second engaging surface. In the cutting zone the first engaging surface and the second engaging surface are in contact for a distance greater than or equal to a thickness of the imaging element. The first cutting surface and said second cutting surface are separated by from 1 to 30 percent of the thickness of the imaging element in the cutting zone. The present invention reduces debris and skiving generation.
摘要:
The present invention relates to polyethylene compositions comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, in particular, this invention further relates to polyethylene blends comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, wherein the modifier has: 1) a g′vis value less than 0.75; 2) at least 0.6 ppm ester groups as determined by 1H NMR; 3) a Tm of 100° C. or more; 4) an Mw of 50,000 g/mol or more, as determined by GPC; 5) an average number of carbon atoms between branch points of 70 or more as determined by 1H NMR.
摘要翻译:本发明涉及包含一种或多种乙烯聚合物和一种或多种树枝状烃聚合物改性剂的聚乙烯组合物,特别地,本发明还涉及包含一种或多种乙烯聚合物和一种或多种树枝状烃聚合物改性剂的聚乙烯共混物,其中改性剂 具有:1)g'vis值小于0.75; 2)通过1 H NMR测定的至少0.6ppm的酯基; 3)Tm为100℃以上; 4)通过GPC测定的Mw为50,000g / mol以上的Mw; 5)通过1 H NMR测定的分支点之间的平均碳原子数为70以上。
摘要:
The invention relates to a thermoplastic membrane (e.g. film, fluid barrier, and the like) which is formed from a blend of: a) a first polymer component (FPC), wherein said FPC comprises a propylene-ethylene copolymer containing from 80 to 93 percent by weight of units derived from propylene, and having a melting point derived from stereoregular polypropylene sequences, as determined by differential scanning calorimetry (DSC), in the range of from 25° C. to 70° C., and a heat of fusion of from 2 J/g to 25 J/g; b) an inorganic filler; c) a processing oil, and d) optionally, a second polymer component (SPC), wherein said SPC is a stereoregular polypropylene containing less than 7 percent by weight of units derived from ethylene or alpha-olefin monomer containing from 4 to 8 carbon atoms and having melting point, as determined by DSC, greater than 130° C., and a heat of fusion greater than 80 J/g.
摘要:
A toner fuser belt for use with electrophotographic apparatus including a thermally conductive substrate through which heat is applied; and a toner release layer formed over the substrate; and including an aliphatic cross-linked polyurethane which is stable at fusing temperatures and wherein the aliphatic cross-linked polyurethane is selected to provide good adhesion to the substrate, inorganic material selected to increase toner fuser belt durability and being in an amount 20 to 60 percent by volume of the toner release layer, and a lubricant which reduces surface energy to thereby promote toner release of the toner release layer.
摘要:
The present invention relates to polyethylene compositions comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, in particular, this invention further relates to polyethylene blends comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, wherein the modifier has: 1) a g′ value less than 0.75; 2) a Cayley tree topology with a layer number of 2 or more more; and 3) a average Mw between the branch points of 1,500 g/mol or more.
摘要:
The present invention relates to polyethylene compositions comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, in particular, this invention further relates to polyethylene blends comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, wherein the modifier has: 1) a g′vis value less than 0.75; 2) at least 0.6 ppm ester groups as determined by 1H NMR; 3) a Tm of 100° C. or more; 4) an Mw of 50,000 g/mol or more, as determined by GPC; 5) an average number of carbon atoms between branch points of 70 or more as determined by 1H NMR.
摘要翻译:本发明涉及包含一种或多种乙烯聚合物和一种或多种树枝状烃聚合物改性剂的聚乙烯组合物,特别地,本发明还涉及包含一种或多种乙烯聚合物和一种或多种树枝状烃聚合物改性剂的聚乙烯共混物,其中改性剂 具有:1)g'vis值小于0.75; 2)通过1 H NMR测定的至少0.6ppm的酯基; 3)Tm为100℃以上; 4)通过GPC测定的Mw为50,000g / mol以上的Mw; 5)通过1 H NMR测定的分支点之间的平均碳原子数为70以上。
摘要:
The present invention relates to polyethylene compositions comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, in particular, this invention further relates to polyethylene blends comprising one or more ethylene polymers and one or more dendritic hydrocarbon polymer modifiers, wherein the modifier has: 1) a g′ value less than 0.75; 2) a Cayley tree topology with a layer number of 2 or more more; and 3) a average Mw between the branch points of 1,500 g/mol or more.
摘要:
Compatibilized blends of an isoolefin polymer and an unsaturated diene polymer are prepared by utilizing a compatibilizing agent comprising a block/graft copolymer containing poly- or copoly-isoolefin segments and C4 to C6 alkyl-substituted styrene polymer segments, such as poly(t-butylstyrene) segments.
摘要:
The invention provides a method for increasing the viscosity of C4–C7 isoolefin copolymers including halomethylstyrene derived units by mixing the copolymer with a hindered amine or phosphine of the structure R1 R2 R3 N or R1 R2 R3 P wherein R1, R2 and R3 are preferably lower and higher alkyl groups. The resulting ionically associated, amino or phosphine modified elastomers are used to prepare thermoplastic elastomer blend compositions, including dynamically vulcanized compositions, containing more finely dispersed elastomers which results in compositions having improved mechanical properties.
摘要:
Oriented films are prepared. A thermoplastic vulcanizate, prepared by mixing at least 20 wt % of a thermoset rubber by weight of the total composition into a thermoplastic polymer are disclosed. After the mixture is prepared the thermoset rubber is entrained as discrete particles within the continuous thermoplastic polymer phase. The resulting composite is subjected to a stress either by pulling, blow molding, or any other film-forming process as is known in the art. This stress causes the continuous phase polymer molecules to become aligned or oriented in the direction in which the stress was applied, thus creating the oriented thermoplastic vulcanizate of the invention. This material has improved gas permeability and improved flexibility properties.